Material Notes:
HB600TF is a low melt flow rate polypropylene homopolymer intended for extrusion and thermoforming. Its very good organoleptic properties allows this grade to be used with any master batch without discoloring problems. Applications: HB600TF is recommended for in-line and off line thermoforming, house ware and thin wall packaging, margarine tubs, and mixing with copolymerInformation provided by Borealis AG
Physical Properties Metric English Comments
Density 0.905 g/cc
0.0327 lb/in³
base resin; ISO 1183
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 33.5 MPa
4860 psi
ISO 527-2
Elongation at Yield 10 %
10 %
50mm/min; ISO 527-2
Tensile Modulus 1.40 GPa
203 ksi
1mm/min; ISO 527-2
Flexural Modulus 1.30 GPa
189 ksi
5mm/min; ISO 178
Charpy Impact, Notched 0.400 J/cm²

@Temperature 23.0 °C
1.90 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 162 - 166 °C
324 - 331 °F
DSC; ISO 3146
Deflection Temperature at 0.46 MPa (66 psi) 86.0 °C
187 °F
ISO 75-2