DuPont Performance Polymers Delrin® 527UV NC010 Acetal (POM)  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced
Manufacturer DuPont Performance Polymers
Trade Name Delrin®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® 527UV NC010 Acetal (POM)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
UV Stabilized Medium Viscosity Acetal HomopolymerDelrin 527UV NC010 is a medium viscosity acetal homopolymer resin with UV stabilizers developed for automotive interior applications. It has improvements in UV aging characteristics and thermal stabilityInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
ISO 1183
Water Absorption 1.2 %

@Thickness 2.00 mm
 1.2 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.170 %

@Thickness 2.00 mm
 0.170 %

@Thickness 0.0787 in
 Sim. to ISO 62
Viscosity 84000 cP

@Shear Rate 5000 1/s,
Temperature 230 °C
 84000 cP

@Shear Rate 5000 1/s,
Temperature 446 °F
 ISO 11403-1 -2
90000 cP

@Shear Rate 5000 1/s,
Temperature 215 °C
 90000 cP

@Shear Rate 5000 1/s,
Temperature 419 °F
 ISO 11403-1 -2
97000 cP

@Shear Rate 5000 1/s,
Temperature 200 °C
 97000 cP

@Shear Rate 5000 1/s,
Temperature 392 °F
 ISO 11403-1 -2
268000 cP

@Shear Rate 500 1/s,
Temperature 230 °C
 268000 cP

@Shear Rate 500 1/s,
Temperature 446 °F
 ISO 11403-1 -2
306000 cP

@Shear Rate 500 1/s,
Temperature 215 °C
 306000 cP

@Shear Rate 500 1/s,
Temperature 419 °F
 ISO 11403-1 -2
351000 cP

@Shear Rate 500 1/s,
Temperature 200 °C
 351000 cP

@Shear Rate 500 1/s,
Temperature 392 °F
 ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.020 cm/cm
0.020 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.019 cm/cm
0.019 in/in
ISO 294-4 2577
Melt Flow 13 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 13 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 cm³/10min; ISO 1133
15 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 15 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 92
92
ISO 2039-2
Hardness, Rockwell R 120
120
ISO 2039-2
Tensile Stress 11.4 MPa

@Strain 1.20 %,
Temperature 90.0 °C
 1650 psi

@Strain 1.20 %,
Temperature 194 °F
 ISO 11403-1 -2
28.0 MPa

@Strain 4.80 %,
Temperature 90.0 °C
 4060 psi

@Strain 4.80 %,
Temperature 194 °F
 ISO 11403-1 -2
28.0 MPa

@Strain 1.30 %,
Temperature 40.0 °C
 4060 psi

@Strain 1.30 %,
Temperature 104 °F
 ISO 11403-1 -2
31.4 MPa

@Strain 1.20 %,
Temperature 23.0 °C
 4550 psi

@Strain 1.20 %,
Temperature 73.4 °F
 ISO 11403-1 -2
32.0 MPa

@Strain 8.50 %,
Temperature 90.0 °C
 4640 psi

@Strain 8.50 %,
Temperature 194 °F
 ISO 11403-1 -2
32.5 MPa

@Strain 12.1 %,
Temperature 90.0 °C
 4710 psi

@Strain 12.1 %,
Temperature 194 °F
 ISO 11403-1 -2
35.1 MPa

@Strain 1.00 %,
Temperature -40.0 °C
 5090 psi

@Strain 1.00 %,
Temperature -40.0 °F
 ISO 11403-1 -2
42.6 MPa

@Strain 1.20 %,
Temperature 0.000 °C
 6180 psi

@Strain 1.20 %,
Temperature 32.0 °F
 ISO 11403-1 -2
48.2 MPa

@Strain 1.30 %,
Temperature -20.0 °C
 6990 psi

@Strain 1.30 %,
Temperature -4.00 °F
 ISO 11403-1 -2
54.0 MPa

@Strain 5.00 %,
Temperature 40.0 °C
 7830 psi

@Strain 5.00 %,
Temperature 104 °F
 ISO 11403-1 -2
57.8 MPa

@Strain 8.80 %,
Temperature 40.0 °C
 8380 psi

@Strain 8.80 %,
Temperature 104 °F
 ISO 11403-1 -2
58.5 MPa

@Strain 11.5 %,
Temperature 40.0 °C
 8480 psi

@Strain 11.5 %,
Temperature 104 °F
 ISO 11403-1 -2
61.1 MPa

@Strain 4.90 %,
Temperature 23.0 °C
 8860 psi

@Strain 4.90 %,
Temperature 73.4 °F
 ISO 11403-1 -2
66.4 MPa

@Strain 8.60 %,
Temperature 23.0 °C
 9630 psi

@Strain 8.60 %,
Temperature 73.4 °F
 ISO 11403-1 -2
67.5 MPa

@Strain 12.3 %,
Temperature 23.0 °C
 9790 psi

@Strain 12.3 %,
Temperature 73.4 °F
 ISO 11403-1 -2
68.8 MPa

@Strain 4.80 %,
Temperature 0.000 °C
 9980 psi

@Strain 4.80 %,
Temperature 32.0 °F
 ISO 11403-1 -2
72.7 MPa

@Strain 8.40 %,
Temperature 0.000 °C
 10500 psi

@Strain 8.40 %,
Temperature 32.0 °F
 ISO 11403-1 -2
73.5 MPa

@Strain 12.0 %,
Temperature 0.000 °C
 10700 psi

@Strain 12.0 %,
Temperature 32.0 °F
 ISO 11403-1 -2
79.5 MPa

@Strain 5.20 %,
Temperature -20.0 °C
 11500 psi

@Strain 5.20 %,
Temperature -4.00 °F
 ISO 11403-1 -2
83.1 MPa

@Strain 9.10 %,
Temperature -20.0 °C
 12100 psi

@Strain 9.10 %,
Temperature -4.00 °F
 ISO 11403-1 -2
84.0 MPa

@Strain 13.0 %,
Temperature -20.0 °C
 12200 psi

@Strain 13.0 %,
Temperature -4.00 °F
 ISO 11403-1 -2
87.3 MPa

@Strain 4.00 %,
Temperature -40.0 °C
 12700 psi

@Strain 4.00 %,
Temperature -40.0 °F
 ISO 11403-1 -2
97.7 MPa

@Strain 7.00 %,
Temperature -40.0 °C
 14200 psi

@Strain 7.00 %,
Temperature -40.0 °F
 ISO 11403-1 -2
99.1 MPa

@Strain 10.0 %,
Temperature -40.0 °C
 14400 psi

@Strain 10.0 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Tensile Strength, Yield 70.0 MPa
10200 psi
ISO 527-1/-2
Elongation at Break 30 %
30 %
Nominal; ISO 527-1/-2
Elongation at Yield 17 %
17 %
ISO 527-1/-2
Tensile Modulus 3.10 GPa
450 ksi
ISO 527-1/-2
Flexural Modulus 3.00 GPa
435 ksi
ISO 178
Shear Modulus 0.2554 GPa

@Temperature 120 °C
 37.04 ksi

@Temperature 248 °F
 Dynamic; ISO 11403-1 -2
0.5689 GPa

@Temperature 70.0 °C
 82.51 ksi

@Temperature 158 °F
 Dynamic; ISO 11403-1 -2
0.9834 GPa

@Temperature 20.0 °C
 142.6 ksi

@Temperature 68.0 °F
 Dynamic; ISO 11403-1 -2
1.2147 GPa

@Temperature -20.0 °C
 176.18 ksi

@Temperature -4.00 °F
 Dynamic; ISO 11403-1 -2
1.3839 GPa

@Temperature -50.0 °C
 200.72 ksi

@Temperature -58.0 °F
 Dynamic; ISO 11403-1 -2
Secant Modulus 0.357 GPa

@Strain 8.40 %,
Temperature 100 °C
 51.8 ksi

@Strain 8.40 %,
Temperature 212 °F
 ISO 11403-1 -2
0.450 GPa

@Strain 8.40 %,
Temperature 80.0 °C
 65.3 ksi

@Strain 8.40 %,
Temperature 176 °F
 ISO 11403-1 -2
0.588 GPa

@Strain 4.20 %,
Temperature 100 °C
 85.3 ksi

@Strain 4.20 %,
Temperature 212 °F
 ISO 11403-1 -2
0.644 GPa

@Strain 9.00 %,
Temperature 40.0 °C
 93.5 ksi

@Strain 9.00 %,
Temperature 104 °F
 ISO 11403-1 -2
0.685 GPa

@Strain 9.80 %,
Temperature 23.0 °C
 99.3 ksi

@Strain 9.80 %,
Temperature 73.4 °F
 ISO 11403-1 -2
0.750 GPa

@Strain 4.20 %,
Temperature 80.0 °C
 109 ksi

@Strain 4.20 %,
Temperature 176 °F
 ISO 11403-1 -2
0.760 GPa

@Strain 9.60 %,
Temperature 0.000 °C
 110 ksi

@Strain 9.60 %,
Temperature 32.0 °F
 ISO 11403-1 -2
0.803 GPa

@Strain 10.4 %,
Temperature -20.0 °C
 116 ksi

@Strain 10.4 %,
Temperature -4.00 °F
 ISO 11403-1 -2
0.980 GPa

@Strain 1.00 %,
Temperature 100 °C
 142 ksi

@Strain 1.00 %,
Temperature 212 °F
 ISO 11403-1 -2
1.08 GPa

@Strain 5.00 %,
Temperature 40.0 °C
 157 ksi

@Strain 5.00 %,
Temperature 104 °F
 ISO 11403-1 -2
1.10 GPa

@Strain 1.10 %,
Temperature 80.0 °C
 160 ksi

@Strain 1.10 %,
Temperature 176 °F
 ISO 11403-1 -2
1.23 GPa

@Strain 8.00 %,
Temperature -40.0 °C
 178 ksi

@Strain 8.00 %,
Temperature -40.0 °F
 ISO 11403-1 -2
1.25 GPa

@Strain 4.90 %,
Temperature 23.0 °C
 181 ksi

@Strain 4.90 %,
Temperature 73.4 °F
 ISO 11403-1 -2
1.43 GPa

@Strain 4.80 %,
Temperature 0.000 °C
 208 ksi

@Strain 4.80 %,
Temperature 32.0 °F
 ISO 11403-1 -2
1.53 GPa

@Strain 5.20 %,
Temperature -20.0 °C
 222 ksi

@Strain 5.20 %,
Temperature -4.00 °F
 ISO 11403-1 -2
2.15 GPa

@Strain 1.30 %,
Temperature 40.0 °C
 312 ksi

@Strain 1.30 %,
Temperature 104 °F
 ISO 11403-1 -2
2.1825 GPa

@Strain 4.00 %,
Temperature -40.0 °C
 316.55 ksi

@Strain 4.00 %,
Temperature -40.0 °F
 ISO 11403-1 -2