DuPont Performance Polymers Zytel® 70K20HSL NC010 Nylon 66  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/Nylon 6 Blend, Glass Fiber Filled
Manufacturer DuPont Performance Polymers
Trade Name Zytel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® 70K20HSL NC010 Nylon 66  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Kevlar® Fiber Reinforced Heat Stabilized Polyamide 66 Zytel 70K20HSL NC010 is a heat stabilized PA66 resin modified with Kevlar aramid fiber for excellent wear resistance.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.19 g/cc
0.0430 lb/in³
DAM; ISO 1183
Water Absorption 6.8 %

@Thickness 2.00 mm
 6.8 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Moisture Absorption 2.70 %

@Thickness 2.00 mm
 2.70 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Viscosity Test 135 cm³/g
135 cm³/g
DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.0090 cm/cm
0.0090 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.014 cm/cm
0.014 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 85.0 MPa
12300 psi
50%RH; ISO 527-1/-2
110 MPa
16000 psi
DAM; ISO 527-1/-2
Tensile Stress 8.75 MPa

@Strain 0.880 %,
Temperature 150 °C
 1270 psi

@Strain 0.880 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
9.04 MPa

@Strain 0.820 %,
Temperature 150 °C
 1310 psi

@Strain 0.820 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
12.5 MPa

@Strain 0.830 %,
Temperature 90.0 °C
 1810 psi

@Strain 0.830 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
13.93 MPa

@Strain 0.860 %,
Temperature 90.0 °C
 2020 psi

@Strain 0.860 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
18.52 MPa

@Strain 0.900 %,
Temperature 40.0 °C
 2686 psi

@Strain 0.900 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
25.19 MPa

@Strain 3.50 %,
Temperature 150 °C
 3654 psi

@Strain 3.50 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
25.82 MPa

@Strain 0.870 %,
Temperature 23.0 °C
 3745 psi

@Strain 0.870 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
26.02 MPa

@Strain 0.540 %,
Temperature 23.0 °C
 3774 psi

@Strain 0.540 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
26.2 MPa

@Strain 3.25 %,
Temperature 150 °C
 3800 psi

@Strain 3.25 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
27.21 MPa

@Strain 0.540 %,
Temperature 0.000 °C
 3946 psi

@Strain 0.540 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
28.08 MPa

@Strain 0.660 %,
Temperature 40.0 °C
 4073 psi

@Strain 0.660 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
29.33 MPa

@Strain 0.560 %,
Temperature -20.0 °C
 4254 psi

@Strain 0.560 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
33.12 MPa

@Strain 0.710 %,
Temperature 0.000 °C
 4804 psi

@Strain 0.710 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
33.22 MPa

@Strain 0.610 %,
Temperature -20.0 °C
 4818 psi

@Strain 0.610 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
33.89 MPa

@Strain 3.32 %,
Temperature 90.0 °C
 4915 psi

@Strain 3.32 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
35.54 MPa

@Strain 6.10 %,
Temperature 150 °C
 5155 psi

@Strain 6.10 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
37.55 MPa

@Strain 8.70 %,
Temperature 150 °C
 5446 psi

@Strain 8.70 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
37.59 MPa

@Strain 3.36 %,
Temperature 90.0 °C
 5452 psi

@Strain 3.36 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
37.79 MPa

@Strain 5.68 %,
Temperature 150 °C
 5481 psi

@Strain 5.68 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
41.14 MPa

@Strain 8.11 %,
Temperature 150 °C
 5967 psi

@Strain 8.11 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
46.25 MPa

@Strain 3.57 %,
Temperature 40.0 °C
 6708 psi

@Strain 3.57 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
48.34 MPa

@Strain 5.83 %,
Temperature 90.0 °C
 7011 psi

@Strain 5.83 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
52.2 MPa

@Strain 8.30 %,
Temperature 90.0 °C
 7570 psi

@Strain 8.30 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
53.89 MPa

@Strain 5.86 %,
Temperature 90.0 °C
 7816 psi

@Strain 5.86 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
58.0 MPa

@Strain 3.38 %,
Temperature 23.0 °C
 8410 psi

@Strain 3.38 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
59.5 MPa

@Strain 9.30 %,
Temperature 90.0 °C
 8630 psi

@Strain 9.30 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
64.42 MPa

@Strain 6.25 %,
Temperature 40.0 °C
 9343 psi

@Strain 6.25 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
69.0 MPa

@Strain 8.90 %,
Temperature 40.0 °C
 10000 psi

@Strain 8.90 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
75.18 MPa

@Strain 2.60 %,
Temperature 40.0 °C
 10900 psi

@Strain 2.60 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
75.85 MPa

@Strain 5.90 %,
Temperature 23.0 °C
 11000 psi

@Strain 5.90 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
81.52 MPa

@Strain 2.17 %,
Temperature 23.0 °C
 11820 psi

@Strain 2.17 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
81.65 MPa

@Strain 2.85 %,
Temperature 0.000 °C
 11840 psi

@Strain 2.85 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
81.8 MPa

@Strain 8.40 %,
Temperature 23.0 °C
 11900 psi

@Strain 8.40 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
87.33 MPa

@Strain 4.57 %,
Temperature 40.0 °C
 12670 psi

@Strain 4.57 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
88.63 MPa

@Strain 2.12 %,
Temperature -20.0 °C
 12850 psi

@Strain 2.12 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
89.2 MPa

@Strain 2.21 %,
Temperature 0.000 °C
 12900 psi

@Strain 2.21 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
93.68 MPa

@Strain 2.45 %,
Temperature -20.0 °C
 13590 psi

@Strain 2.45 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
94.4 MPa

@Strain 6.50 %,
Temperature 40.0 °C
 13700 psi

@Strain 6.50 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
96.83 MPa

@Strain 4.97 %,
Temperature 0.000 °C
 14040 psi

@Strain 4.97 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
98.62 MPa

@Strain 3.79 %,
Temperature 23.0 °C
 14300 psi

@Strain 3.79 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
104.7 MPa

@Strain 7.10 %,
Temperature 0.000 °C
 15190 psi

@Strain 7.10 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
105.34 MPa

@Strain 5.40 %,
Temperature 23.0 °C
 15278 psi

@Strain 5.40 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
112.16 MPa

@Strain 4.27 %,
Temperature -20.0 °C
 16267 psi

@Strain 4.27 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
115.95 MPa

@Strain 3.71 %,
Temperature -20.0 °C
 16817 psi

@Strain 3.71 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
122.32 MPa

@Strain 6.11 %,
Temperature -20.0 °C
 17741 psi

@Strain 6.11 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
127.35 MPa

@Strain 5.30 %,
Temperature -20.0 °C
 18471 psi

@Strain 5.30 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
Elongation at Break 5.2 %
5.2 %
DAM; ISO 527-1/-2
7.2 %
7.2 %
50%RH; ISO 527-1/-2
Tensile Modulus 3.50 GPa
508 ksi
50%RH; ISO 527-1/-2
5.30 GPa
769 ksi
DAM; ISO 527-1/-2
0.910 GPa

@Temperature 230 °C
 132 ksi

@Temperature 446 °F
 DAM; Dynamic; ISO 11403-1 -2
1.449 GPa

@Temperature 150 °C
 210.2 ksi

@Temperature 302 °F
 DAM; Dynamic; ISO 11403-1 -2
2.039 GPa

@Temperature 100 °C
 295.7 ksi

@Temperature 212 °F
 DAM; Dynamic; ISO 11403-1 -2
4.223 GPa

@Temperature 50.0 °C
 612.5 ksi

@Temperature 122 °F
 DAM; Dynamic; ISO 11403-1 -2
4.50 GPa

@Temperature 23.0 °C
 653 ksi

@Temperature 73.4 °F
 DAM; Dynamic; ISO 11403-1 -2
Flexural Modulus 3.30 GPa
479 ksi
50%RH; ISO 178
4.90 GPa
711 ksi
DAM; ISO 178
Secant Modulus 0.949 GPa

@Strain 7.13 %,
Temperature 40.0 °C
 138 ksi

@Strain 7.13 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2