Haynes 230® alloy, as cast vacuum investment casting

Category Metal , Nonferrous Metal , Nickel Alloy , Superalloy
Manufacturer Haynes International, Inc.
Trade Name
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Haynes 230® alloy, as cast vacuum investment casting.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applications include combustion cans, transition ducts, flameholders, thermocouple sheaths and other gas turbine components; used for catalyst grid supports in ammonia burners, high-strength thermocouple protection tubes, high-temperature heat exchangers, ducts, high-temperature bellows; furnace retorts, chains and fixtures, burner flame shrouds, recuperator internals, dampers, nitriding furnace internals, heat-treating baskets, grates, trays, sparger tubes, and cyclone internals.Data provided by the manufacturer, Haynes International, Inc.
Physical Properties Metric English Comments
Density 8.97 g/cc
0.324 lb/in³
at RT
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 615 MPa
89200 psi
89.0 MPa
<br>@Temperature 1093 °C
 12900 psi
<br>@Temperature 1999 °F
205 MPa
<br>@Temperature 982 °C
 29700 psi
<br>@Temperature 1800 °F
285 MPa
<br>@Temperature 871 °C
 41300 psi
<br>@Temperature 1600 °F
385 MPa
<br>@Temperature 760 °C
 55800 psi
<br>@Temperature 1400 °F
450 MPa
<br>@Temperature 538 °C
 65300 psi
<br>@Temperature 1000 °F
480 MPa
<br>@Temperature 649 °C
 69600 psi
<br>@Temperature 1200 °F
Tensile Strength, Yield 325 MPa
<br>@Strain 0.200 %
 47100 psi
<br>@Strain 0.200 %
87.0 MPa
<br>@Strain 0.200 %,<br> Temperature 1093 °C
 12600 psi
<br>@Strain 0.200 %,<br> Temperature 1999 °F
170 MPa
<br>@Strain 0.200 %,<br> Temperature 982 °C
 24700 psi
<br>@Strain 0.200 %,<br> Temperature 1800 °F
185 MPa
<br>@Strain 0.200 %,<br> Temperature 871 °C
 26800 psi
<br>@Strain 0.200 %,<br> Temperature 1600 °F
225 MPa
<br>@Strain 0.200 %,<br> Temperature 649 °C
 32600 psi
<br>@Strain 0.200 %,<br> Temperature 1200 °F
225 MPa
<br>@Strain 0.200 %,<br> Temperature 760 °C
 32600 psi
<br>@Strain 0.200 %,<br> Temperature 1400 °F
230 MPa
<br>@Strain 0.200 %,<br> Temperature 538 °C
 33400 psi
<br>@Strain 0.200 %,<br> Temperature 1000 °F
Elongation at Break 37.8 %
37.8 %
in 5D
19 %
<br>@Temperature 871 °C
 19 %
<br>@Temperature 1600 °F
 in 5D
25.5 %
<br>@Temperature 982 °C
 25.5 %
<br>@Temperature 1800 °F
 in 5D
32.3 %
<br>@Temperature 760 °C
 32.3 %
<br>@Temperature 1400 °F
 in 5D
38.2 %
<br>@Temperature 538 °C
 38.2 %
<br>@Temperature 1000 °F
 in 5D
41 %
<br>@Temperature 1093 °C
 41 %
<br>@Temperature 1999 °F
 in 5D
44.2 %
<br>@Temperature 649 °C
 44.2 %
<br>@Temperature 1200 °F
 in 5D
Reduction of Area 37.7 %
37.7 %
29.8 %
<br>@Temperature 871 °C
 29.8 %
<br>@Temperature 1600 °F
34.9 %
<br>@Temperature 649 °C
 34.9 %
<br>@Temperature 1200 °F
35.9 %
<br>@Temperature 538 °C
 35.9 %
<br>@Temperature 1000 °F
36 %
<br>@Temperature 760 °C
 36 %
<br>@Temperature 1400 °F
39.9 %
<br>@Temperature 982 °C
 39.9 %
<br>@Temperature 1800 °F
46.6 %
<br>@Temperature 1093 °C
 46.6 %
<br>@Temperature 1999 °F
Modulus of Elasticity 211 GPa
30600 ksi
RT
150 GPa
<br>@Temperature 1000 °C
 21800 ksi
<br>@Temperature 1830 °F
157 GPa
<br>@Temperature 900 °C
 22800 ksi
<br>@Temperature 1650 °F
164 GPa
<br>@Temperature 800 °C
 23800 ksi
<br>@Temperature 1470 °F
171 GPa
<br>@Temperature 700 °C
 24800 ksi
<br>@Temperature 1290 °F
177 GPa
<br>@Temperature 600 °C
 25700 ksi
<br>@Temperature 1110 °F
184 GPa
<br>@Temperature 500 °C
 26700 ksi
<br>@Temperature 932 °F
190 GPa
<br>@Temperature 400 °C
 27600 ksi
<br>@Temperature 752 °F
196 GPa
<br>@Temperature 300 °C
 28400 ksi
<br>@Temperature 572 °F
202 GPa
<br>@Temperature 200 °C
 29300 ksi
<br>@Temperature 392 °F
207 GPa
<br>@Temperature 100 °C
 30000 ksi
<br>@Temperature 212 °F
Thermal Properties Metric English Comments
CTE, linear 12.7 µm/m-°C
<br>@Temperature 25.0 - 100 °C
 7.06 µin/in-°F
<br>@Temperature 77.0 - 212 °F
13.0 µm/m-°C
<br>@Temperature 25.0 - 200 °C
 7.22 µin/in-°F
<br>@Temperature 77.0 - 392 °F
13.3 µm/m-°C
<br>@Temperature 25.0 - 300 °C
 7.39 µin/in-°F
<br>@Temperature 77.0 - 572 °F
13.7 µm/m-°C
<br>@Temperature 25.0 - 400 °C
 7.61 µin/in-°F
<br>@Temperature 77.0 - 752 °F
14.0 µm/m-°C
<br>@Temperature 25.0 - 500 °C
 7.78 µin/in-°F
<br>@Temperature 77.0 - 932 °F
14.4 µm/m-°C
<br>@Temperature 25.0 - 600 °C
 8.00 µin/in-°F
<br>@Temperature 77.0 - 1110 °F
14.8 µm/m-°C
<br>@Temperature 25.0 - 700 °C
 8.22 µin/in-°F
<br>@Temperature 77.0 - 1290 °F
15.2 µm/m-°C
<br>@Temperature 25.0 - 800 °C
 8.44 µin/in-°F
<br>@Temperature 77.0 - 1470 °F
15.7 µm/m-°C
<br>@Temperature 25.0 - 900 °C
 8.72 µin/in-°F
<br>@Temperature 77.0 - 1650 °F
16.1 µm/m-°C
<br>@Temperature 25.0 - 1000 °C
 8.94 µin/in-°F
<br>@Temperature 77.0 - 1830 °F
Specific Heat Capacity 0.397 J/g-°C
0.0949 BTU/lb-°F
RT
0.419 J/g-°C
<br>@Temperature 100 °C
 0.100 BTU/lb-°F
<br>@Temperature 212 °F
0.435 J/g-°C
<br>@Temperature 200 °C
 0.104 BTU/lb-°F
<br>@Temperature 392 °F
0.448 J/g-°C
<br>@Temperature 300 °C
 0.107 BTU/lb-°F
<br>@Temperature 572 °F
0.465 J/g-°C
<br>@Temperature 400 °C
 0.111 BTU/lb-°F
<br>@Temperature 752 °F
0.473 J/g-°C
<br>@Temperature 500 °C
 0.113 BTU/lb-°F
<br>@Temperature 932 °F
0.486 J/g-°C
<br>@Temperature 600 °C
 0.116 BTU/lb-°F
<br>@Temperature 1110 °F
0.574 J/g-°C
<br>@Temperature 700 °C
 0.137 BTU/lb-°F
<br>@Temperature 1290 °F
0.595 J/g-°C
<br>@Temperature 800 °C
 0.142 BTU/lb-°F
<br>@Temperature 1470 °F
Electrical Properties Metric English Comments
Electrical Resistivity 0.000125 ohm-cm
0.000125 ohm-cm
RT
0.000125 ohm-cm
<br>@Temperature 1000 °C
 0.000125 ohm-cm
<br>@Temperature 1830 °F
0.0001258 ohm-cm
<br>@Temperature 100 °C
 0.0001258 ohm-cm
<br>@Temperature 212 °F
0.0001265 ohm-cm
<br>@Temperature 200 °C
 0.0001265 ohm-cm
<br>@Temperature 392 °F
0.0001271 ohm-cm
<br>@Temperature 900 °C
 0.0001271 ohm-cm
<br>@Temperature 1650 °F
0.0001273 ohm-cm
<br>@Temperature 300 °C
 0.0001273 ohm-cm
<br>@Temperature 572 °F
0.0001284 ohm-cm
<br>@Temperature 400 °C
 0.0001284 ohm-cm
<br>@Temperature 752 °F
0.0001291 ohm-cm
<br>@Temperature 800 °C
 0.0001291 ohm-cm
<br>@Temperature 1470 °F
0.0001302 ohm-cm
<br>@Temperature 500 °C
 0.0001302 ohm-cm
<br>@Temperature 932 °F
0.0001307 ohm-cm
<br>@Temperature 700 °C
 0.0001307 ohm-cm
<br>@Temperature 1290 °F
0.0001312 ohm-cm
<br>@Temperature 600 °C
 0.0001312 ohm-cm
<br>@Temperature 1110 °F