LATI Latan 9 POM
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | LATI |
| Trade Name | Latan |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Latan 9 POM.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyoxymethylene (POM). Unfilled. Medium viscosity. Very good tribological properties.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.020 - 0.023 cm/cm | 0.020 - 0.023 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0205 - 0.0225 cm/cm | 0.0205 - 0.0225 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | |
| Elongation at Break | 50 % @Temperature 23.0 °C |
50 % @Temperature 73.4 °F |
|
| >= 100 % @Temperature 60.0 °C |
>= 100 % @Temperature 140 °F |
||
| >= 100 % @Temperature 90.0 °C |
>= 100 % @Temperature 194 °F |
||
| Elongation at Yield | 10 % | 10 % | |
| Tensile Modulus | 0.900 GPa @Temperature 90.0 °C |
131 ksi @Temperature 194 °F |
|
| 1.40 GPa @Temperature 60.0 °C |
203 ksi @Temperature 140 °F |
||
| 2.60 GPa @Temperature 23.0 °C |
377 ksi @Temperature 73.4 °F |
||
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
|
| NB @Temperature -20.0 °C |
NB @Temperature -4.00 °F |
||
| Charpy Impact, Notched | 0.500 J/cm² @Temperature -20.0 °C |
2.38 ft-lb/in² @Temperature -4.00 °F |
|
| 0.700 J/cm² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 75.0 °C | 167 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | |
| Vicat Softening Point | 150 °C @Load 5.00 kg |
302 °F @Load 11.0 lb |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V | 600 V | A solution |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 175 - 200 °C | 347 - 392 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Drying Temperature | 80.0 - 90.0 °C @Time 10800 sec |
176 - 194 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 1-8357 Polyamide 66, with carbon fiber and glass fiber, heat stabilized
- Lord Adhesives 7545B Two-Component, Equal-Mix, Non-Sag Urethane Adhesive
- Iran Petrochemical (PCC) PC 0712 Polycarbonate
- Sumitomo Bakelite North America Epiall® 2061B-1 Mineral and Glass Filled Electrical Encapsulation Grade Epoxy
- Sumitomo Chemical ESPOLEX® UT461A Thermoplastic Elastomer
- Wanhua Chemical Wanthane® WHT-8185 Polyether-Based TPU
- ArcelorMittal Save 27-15 Electrical Steel
- DuPont Performance Polymers Hypalon® 30 Chlorosulfonated Polyethylene Rubber, Gum Compound (discontinued **)&
- Dielectric Polymers NT-581 Fume Mask (discontinued **)