Lanxess Durethan® DP 2037/30 H2.0 LT 904040 Nylon 6, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® DP 2037/30 H2.0 LT 904040 Nylon 6, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, 30% glass fibers, black colored for laser transmission-welding (laser-transparent), good heat-ageing resistance
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| Viscosity Test | 125 cm³/g | 125 cm³/g | Viscosity number; ISO 307, 1157, 1628 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0035 cm/cm | 0.0035 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 120 MPa | 17400 psi | Conditioned; ISO 527-1/-2 |
| 175 MPa | 25400 psi | ISO 527-1/-2 | |
| Tensile Strength, Yield | 125 MPa | 18100 psi | Conditioned; ISO 527-1/-2 |
| 175 MPa | 25400 psi | ISO 527-1/-2 | |
| Elongation at Break | 3.6 % | 3.6 % | ISO 527-1/-2 |
| 5.8 % | 5.8 % | Conditioned; ISO 527-1/-2 | |
| Elongation at Yield | 3.3 % | 3.3 % | ISO 527-1/-2 |
| 4.2 % | 4.2 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 7.25 GPa | 1050 ksi | Conditioned; ISO 527-1/-2 |
| 9.50 GPa | 1380 ksi | ISO 527-1/-2 | |
| Puncture Energy | 2.90 J | 2.14 ft-lb | ISO 6603-2 |
| 4.20 J | 3.10 ft-lb | Conditioned; ISO 6603-2 | |
| 3.10 J @Temperature -30.0 °C |
2.29 ft-lb @Temperature -22.0 °F |
ISO 6603-2 | |
| 3.10 J @Temperature -30.0 °C |
2.29 ft-lb @Temperature -22.0 °F |
Conditioned; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 188 °C | 370 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 76.0 °C | 169 °F | ISO 75-1/-2 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release agent | |
| Features | Heat stabilized or stable to heat | |
| Form | Pellets | |
| ISO Shortname | 1874-1: PA 6,MHR,12,-090,GF30 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycolac® S701SU ABS (Europe-Africa-Middle East)
- Radici Radilon® A HSX88 (cond.) Nylon 66
- 3M Dyneon™ THV 220A Fluorothermoplastic (discontinued **)
- Kraton® G1633 E (SEBS) Linear Triblock Copolymer
- Momentive Performance Materials Addisilâ„¢ 440 E Healthcare Extrusion Grade Heat Cured Rubber
- SABIC Innovative Plastics Valox® V9260CS PET (Europe-Africa-Middle East)
- Shandong Dongyue Polymer DF-11 PTFE Molding Powder (Micronized Particles)
- Von Roll Isola IMI Varnish 74036 Solventless Epoxy Varnish for Electrical Insulation
- Trelleborg Hypalon® H608 Chlorosulphonated Polyethylene
- Ascend Performance Materials Vydyne® 25WSP Nylon 66, Conditioned (2.5% Moisture)
Copyright © lookpolymers.com All Rights Reserved