Lotte Chemical Titan TITANLENE® LDF264YZ Low density polyethylene
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Extrusion Grade |
| Manufacturer | Lotte Chemical Titan Holding Sdn. Bhd. (Former Titan Chemicals) |
| Trade Name | TITANLENE® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lotte Chemical Titan TITANLENE® LDF264YZ Low density polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LDF264YZ is a low density polyethylene resin for film extrusion. LDF264YZ has no slip and anti-block additives. LDF264YZ meets the U.S. Food and Drug Administration (FDA) criteria for food contact use as specified in 21 CFR 177.1520 (c) 2.1 & (c) 2.2.Applications: Low haze and heavy duty film Shrink film Construction filmAdditives: BarefootAdvantages: Excellent mechanical properties Good process abilityInformation provided by Titan Chemicals
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Base Resin Density | 0.922 g/cc | 0.0333 lb/in³ | ASTM D1505 |
| Thickness | 150 microns | 5.91 mil | extruded at 1.5:1 BUR |
| Base Resin Melt Index | 0.40 g/10 min | 0.40 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 490 % | 490 % | ASTM D882 |
| Film Elongation at Break, TD | 620 % | 620 % | ASTM D882 |
| Dart Drop | 3.00 g/micron | 76.2 g/mil | ASTM D1709 |
| Film Tensile Strength at Break, MD | 21.6 MPa | 3130 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 19.6 MPa | 2840 psi | ASTM D882 |
| 1% Secant Modulus, MD | 176.52 MPa | 25602 psi | ASTM D882 |
| 1% Secant Modulus, TD | 196.14 MPa | 28447 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 97.0 °C | 207 °F | resin; ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 17 % | 17 % | ASTM D1003 |
| Gloss | 60 % | 60 % | 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 160 - 190 °C | 320 - 374 °F | |
| Blow-up Ratio (BUR) | 1.5 | 1.5 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Trouser tear, MD g/micron | 9 | ASTM D1938 |
| Trouser tear, TD g/micron | 8.5 | ASTM D1938 |
Users viewing this material also viewed the following:
- Pyrotek Pyrocast AR-S Castable Refractory
- PolyOne FireCon™ CPE 30-11 RoHS BLACK Polyethylene, Chlorinated (CPE)
- Lord Adhesives Thermosetâ„¢ MD-130 Electrically Insulating Die-Attach Adhesive
- Samyang Triloy® 230NH PC/ABS alloy, Flame Retardant
- Solvay MIRATAINE® BET C-30 Surfactant
- American Polymers API 410 Polystyrene
- Borealis Daplen™ EF267AI Polypropylene TPO Compound
- Crucible Steel REX® M2 S High Speed Steel
- Eurotec® Tecodur® PB70 GR50 BK002 CA01 PBT/PET, 50% glass fiber reinforced, heat & UV stabilized, natural
Copyright © lookpolymers.com All Rights Reserved