Multibase Multi-Pro® 4013 CU Yellow 40% Filler Content Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Multibase |
| Trade Name | Multi-Pro® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-Pro® 4013 CU Yellow 40% Filler Content Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Multibase.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM D955-89 |
| Melt Flow | 13 g/10 min | 13 g/10 min | (Condition L) ASTM D-1238-94a |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 20.7 MPa | 3000 psi | ASTM D638-95 |
| Elongation at Break | 200 % | 200 % | ASTM D638-95 |
| Flexural Strength | 35.9 MPa | 5210 psi | ASTM D790-95 |
| Flexural Modulus | 2.241 GPa | 325.0 ksi | Method 1, Proc. B; ASTM D-790-95 |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256-93a |
| Gardner Impact | 11.3 J | 8.33 ft-lb | ASTM D5420-93 |
Users viewing this material also viewed the following:
- NYC YT3W Y2O3 Powder
- Lehmann & Voss LUVOCOM® 1105-8416 PEEK, with carbon fiber
- ICO Polymers ICORENEâ„¢ 195-1325 LMDPE Rotational Molding Resin
- Teknor Apex Tekbond® TB 1176A Thermoplastic Elastomer
- Master Bond Supreme 10HT One Component, Low Outgassing, Toughened Epoxy System
- ExxonMobil Santoprene® 121-80B230 Thermoplastic Elastomer
- ExxonMobil Mobil Polyrex EM
- 3M FM06E Indoor UL Recognized Brite Silver Polyester Label Products
- Amco PRIMATOP HDPE 003952 Phillips Process Hexene Copolymer
- Arlon 48571R006 0.0055" (0.140 mm) Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved