PolyOne LubriOne™ PC-000/15T-S2 NATURAL Polycarbonate (PC)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | PolyOne Corporation |
| Trade Name | LubriOne™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne LubriOne™ PC-000/15T-S2 NATURAL Polycarbonate (PC).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 48.3 MPa | 7010 psi | Type I, 5.1 mm/min; ASTM D638 |
| Elongation at Break | 7.0 % | 7.0 % | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 2.41 GPa | 350 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 75.8 MPa | 11000 psi | ASTM D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D790 |
| Izod Impact, Notched | 1.00 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.87 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 121 °C @Thickness 6.35 mm |
250 °F @Thickness 0.250 in |
Annealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 288 - 316 °C | 550 - 601 °F | |
| Mold Temperature | 87.8 - 121 °C | 190 - 250 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 4.00 hour | 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Lubricated | |
| Forms | Pellets | |
| Generic Material | PC | |
| Generic Name | Polycarbonate (PC) | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| South America | ||
| Uses | Appliance Components | |
| Conveyor Parts | ||
| Printer Parts |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PQ 83 N PP, imp. strength
- Plansee DENAL® 917 108 XXX (1) Tungsten-Nickel-Iron-Cobalt Alloy
- MetalTek MTEK 6 UNS R30006 Cobalt Base Alloy
- LATI Latamid 6 H2 G/65 PA 6, 65% Glass Fiber Reinforced, Heat Stabilized
- SABIC Innovative Plastics LNP THERMOCOMP RF006L PA 66 (Asia Pacific)
- Fainplast Compounds GS 70/AT Flexible PVC, Injection Molding for Transparent Technical Items
- Dow Corning 2-8839 EMULSION
- 3A Composites Core Materials AIREX® R63.80 Damage Tolerant Foam
- Mitsui UNISTOLE™ R-200 Polyolefinic Primer/ Adhesive
Copyright © lookpolymers.com All Rights Reserved