Proto3000 Objet RGD525 High Temperature Prototyping Polymer
| Category | Polymer , Rapid Prototyping Polymer |
| Manufacturer | Proto3000 |
| Trade Name | Objet |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Proto3000 Objet RGD525 High Temperature Prototyping Polymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Proto3000 for their protoyping engineering services.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.970 - 0.980 g/cc | 0.0350 - 0.0354 lb/in³ | Polymerized; ASTM D792 |
| Water Absorption | 1.2 - 1.4 % @Time 86400 sec |
1.2 - 1.4 % @Time 24.0 hour |
ASTM D570-98 |
| Ash | 0.38 - 0.42 % | 0.38 - 0.42 % | USP281 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 73 - 83 | 73 - 83 | |
| Hardness, Shore D | 87 - 88 | 87 - 88 | |
| Tensile Strength at Break | 70.0 - 80.0 MPa | 10200 - 11600 psi | ASTM D638-03 |
| Elongation at Break | 10 - 15 % | 10 - 15 % | ASTM D638-05 |
| Modulus of Elasticity | 3.20 - 3.50 GPa | 464 - 508 ksi | ASTM D638-04 |
| Flexural Strength | 110 - 130 MPa | 16000 - 18900 psi | ASTM D790-03 |
| Flexural Modulus | 3.10 - 3.50 GPa | 450 - 508 ksi | ASTM D790-04 |
| Izod Impact, Notched | 0.140 - 0.160 J/cm | 0.262 - 0.300 ft-lb/in | ASTM D256-06 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 63.0 - 67.0 °C | 145 - 153 °F | ASTM D648-06 |
| 75.0 - 80.0 °C | 167 - 176 °F | after thermal post treatment procedure A; ASTM D648-06 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 - 57.0 °C | 131 - 135 °F | ASTM D648-07 |
| Glass Transition Temp, Tg | 62.0 - 65.0 °C | 144 - 149 °F | DMA, E |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers Aquivion® E98-05 Tetrafluoroethylene + SFVE (TFE+SFVE)
- Teknor Apex Sinpolene MBB3131 Linear Low Density Polyethylene
- Total HDPE XT25N High Density Polyethylene, Pipe Resin
- Ecomass® 4703TU95 Tungsten Filled Polyurethane
- BASF Ultramid® A3L HP PA66 (Dry)
- Ashley Polymers Ashlene® 264-15 PPO, 15% Glass Reinforced
- Bulk Molding Compounds BMC 1608 Very High Strength, Corrosion Resistant
- LATI Latimass 52/11-01 D020 PP Homopolymer
- Chevron Phillips 6109L LLDPE Blown Film Resin, Butene Copolymer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved