SABIC Innovative Plastics LNP THERMOCOMP KF005 Acetal Copolymer
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 30% Glass Fiber Reinforced |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP KF005 Acetal Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* KF005 is a compound based on Acetal Copolymer resin containing 25% Glass Fiber. Added features of this material include: Chemically Coupled.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.280 % | 0.280 % | 50% RH, 24 hrs; ASTM D570 |
| 0.280 % | 0.280 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0090 cm/cm @Time 86400 sec |
0.0060 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.040 cm/cm @Time 86400 sec |
0.010 - 0.040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 100 MPa | 14500 psi | 5 mm/min; ISO 527 |
| 107 MPa | 15500 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 3.5 % | 3.5 % | 5 mm/min; ISO 527 |
| 4.2 % | 4.2 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 12.92 GPa | 1874 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 38.0 MPa | 5510 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 10.16 GPa | 1474 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.01 J/cm | 13.1 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 38.0 kJ/m² | 18.1 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 71.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
39.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 73.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
40.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 164 °C | 327 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 163 °C @Thickness 3.20 mm |
325 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 161 °C | 322 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 162 °C @Thickness 3.20 mm |
324 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- NanoAmor 95%, OD/ID/L: 20-30/5-10 nm/0.5-2 um Short Multi-Walled Carbon Nanotubes
- Resin Technology Group KONA 877 Low Viscosity, Low Shrinkage, Vacuum Grade Casting Resin
- Poco Graphite AXM-5Q Industrial Grade Graphite
- Kazanorgsintez 107-19 Composition of Low Density Polyethylene, Crack-Proof
- Lehmann & Voss LUVOCOM® 1106-8087/BL Polyether imide, unreinforced, laser markable
- SABIC Innovative Plastics Valox® 830R PBT (Asia Pacific)
- A. Schulman POLYBATCH™ Red 5670 Concentrate Based In Polyethylene
- Eurostar Staramide RF00ASXP PA66, 50% Glass Filled, Injection Molded
Copyright © lookpolymers.com All Rights Reserved