SABIC Innovative Plastics LNP Thermocomp DF0069E PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp DF0069E PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* DF0069E is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ASTM D 792 |
| 1.47 g/cc | 0.0531 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0018 cm/cm @Time 86400 sec |
0.0018 in/in @Time 24.0 hour |
ISO 294 |
| 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D 955 | |
| Linear Mold Shrinkage, Transverse | 0.0069 cm/cm @Time 86400 sec |
0.0069 in/in @Time 24.0 hour |
ISO 294 |
| 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 114 MPa | 16500 psi | ASTM D 638 |
| 120 MPa | 17400 psi | ISO 527 | |
| Elongation at Break | 6.8 % | 6.8 % | ASTM D 638 |
| 7.0 % | 7.0 % | ISO 527 | |
| Tensile Modulus | 11.18 GPa | 1622 ksi | 1 mm/min; ISO 527 |
| 14.47 GPa | 2099 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 172 MPa | 24900 psi | ASTM D 790 |
| 183 MPa | 26500 psi | ISO 178 | |
| Flexural Modulus | 7.58 GPa | 1100 ksi | ASTM D 790 |
| 8.80 GPa | 1280 ksi | ISO 178 | |
| Izod Impact, Notched | 1.38 J/cm @Temperature 23.0 °C |
2.59 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 8.43 J/cm @Temperature 23.0 °C |
15.8 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² @Temperature 23.0 °C |
6.66 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 53.0 kJ/m² @Temperature 23.0 °C |
25.2 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
28.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 51.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
28.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 30.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 31.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 148 °C | 298 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 143 °C @Thickness 3.20 mm |
289 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 144 °C | 291 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- LNP Thermocomp® UF-1009 HS Polyphthalamide, Glass Fiber Reinforcement (discontinued **)
- LATI LATISTAT 30/R-05 High Impact Strength Polystyrene Base Conductive Plastic (discontinued **)
- TSE Industries Millathane® 97 Millable Polyester Polyurethane Rubber, Hardness 95A
- Resinlab® CYNERGY CA6306 Adhesive
- LG Chemical Phenol
- Dow Corning SILASTIC® 9416/50 KIT PARTS A&B
- CP-Polymer-Technik Wellamid® 6000 GS 15 HWCP 15% Glass Sphere Filled Nylon 6, Heat Stabilized, Conditioned
- ExxonMobil Escorene™ UL 40028EM1 Ethylene Vinyl Acetate Copolymer (European Grade)
- ExxonMobil Exxtral™ BNT 011 Performance Polyolefin
- DuPont™ Surlyn® 1601 Sodium Ionomer Resin for Blown and Cast Film
Copyright © lookpolymers.com All Rights Reserved