SABIC Innovative Plastics LNP Thermocomp JF003L PES
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp JF003L PES.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* JF003L is a compound based on Polyethersulfone (PES) containing Glass Fiber. Characteristics of this grade are Low Extractable.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.49 g/cc | 1.49 g/cc | ASTM D 792 |
| Density | 1.48 g/cc | 0.0535 lb/in³ | ASTM D 792 |
| Moisture Absorption at Equilibrium | 0.66 % | 0.66 % | 23°C / 50% RH; ISO 62 |
| 0.43 % @Time 86400 sec |
0.43 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 96.0 MPa | 13900 psi | 5 mm/min; ISO 527 |
| 103 MPa | 14900 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 2.6 % | 2.6 % | 5 mm/min; ISO 527 |
| 2.7 % | 2.7 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 5.89 GPa | 854 ksi | 1 mm/min; ISO 527 |
| 5.98 GPa | 867 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 155 MPa | 22500 psi | ISO 178 |
| 157 MPa | 22800 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Yield Strength | 157 MPa | 22800 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 5.56 GPa | 806 ksi | 2 mm/min; ISO 178 |
| 5.65 GPa | 819 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.410 J/cm @Temperature 23.0 °C |
0.768 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 5.18 J/cm @Temperature 23.0 °C |
9.70 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| 10.0 J @Temperature 23.0 °C |
7.38 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 34.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
18.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
25.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 221 °C @Thickness 3.20 mm |
430 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 216 °C @Thickness 3.20 mm |
421 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Oceanchem Group Zinc Borate
- Polimersan Plastics POLIKES® (PA 6 G) Cast Polyamide
- Polymer Industries Densetec HDPE Partition Board
- NIZHNEKAMSKNEFTEKHIM PE 4028X (28435) Linear Low Density Polyethylene
- Lotte Chemical Titan TITANEX® HB0972 High density polyethylene Hexene-1 resin
- SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1010 PC (Asia Pacific)
- A. Schulman PP 1255-01 Polypropylene General Purpose Homopolymer Polypropylene
- Unitika elitel UE3210 Polyester, Pellet
- Elgiloy® Co-Cr-Ni Alloy, Wire, Heat Treated
Copyright © lookpolymers.com All Rights Reserved