SABIC Innovative Plastics NORYL WCP700 PPE-TPE
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL WCP700 PPE-TPE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flexible PPE-TPE injection grade suitable for over-molding applications such as plugs, strain relief's, and connectors. Good processability. 70 Shore A hardness.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.930 g/cc | 0.930 g/cc | ASTM D792 |
| Water Absorption | 0.050 % @Time 173000 sec |
0.050 % @Time 48.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0048 cm/cm @Time 86400 sec |
0.0048 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0033 cm/cm @Time 86400 sec |
0.0033 in/in @Time 24.0 hour |
ASTM D955 |
| Melt Flow | 10 g/10 min @Load 5.00 kg, Temperature 200 °C |
10 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| 17 g/10 min @Load 5.00 kg, Temperature 210 °C |
17 g/10 min @Load 11.0 lb, Temperature 410 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 70 | 70 | 30S reading; ASTM D2240 |
| Tensile Strength at Break | 4.00 MPa | 580 psi | 50 mm/min; ISO 527 |
| 5.00 MPa | 725 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | >= 400 % | >= 400 % | Type I, 50 mm/min; ASTM D638 |
| >= 400 % | >= 400 % | 50 mm/min; ISO 527 | |
| Flexural Modulus | 0.0500 GPa | 7.25 ksi | 12.5 mm/min, 100 mm span; ASTM D790 |
| 0.0500 GPa | 7.25 ksi | 12.5 mm/min; ISO 178 | |
| Tear Strength | 46.0 kN/m | 262 pli | ISO 6383 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | <= -40.0 °C | <= -40.0 °F | ASTM D746 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.70e+16 ohm-cm | 1.70e+16 ohm-cm | IEC 60093 |
| Dielectric Constant | 2.4 @Frequency 1.00e+6 Hz |
2.4 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 2.4 @Frequency 50.0 - 60.0 Hz |
2.4 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 26.0 kV/mm @Thickness 2.00 mm |
660 kV/in @Thickness 0.0787 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.00050 @Frequency 1.00e+6 Hz |
0.00050 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 0.037 @Frequency 50.0 - 60.0 Hz |
0.037 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
Users viewing this material also viewed the following:
- Premix Thermoplastics PREBLACK CP 731-40 Black Universal Masterbatch, 40% Carbon Black
- Polimeri Europa SINKRAL B733/E ABS, Impact & Heat Stabilized Grade (discontinued **)
- Huntsman PE1503 EVA Film Extrusion (discontinued **)
- Haynes HR-160® alloy, hot rolled and solution annealed plate
- Formosa Plastics Formolene® 3335E Random Copolymer Polypropylene
- CP-Polymer-Technik Wellamid® 6600 MZ 315 CP Combination Nylon 66, Conditioned
- Dow 662I Low Density Polyethylene Resin
- BASF Elastollan® 1185A10W Wire & Cable Grade Polyurethane Elastomer
- LNP Lubricomp® OCL-4536 Polyphenylene Sulfide, Carbon Fiber Reinforced, PTFE + Silicone Lubricant (discontinu
Copyright © lookpolymers.com All Rights Reserved