SABIC PP 520L Polypropylene Homopolymer for Tubular Water Quenched Film

Category	Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer	SABIC
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC PP 520L Polypropylene Homopolymer for Tubular Water Quenched Film.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Product Description: PP 520L is specially developed for tubular water quenched blown film applications with a suitable dosage of slip and antiblock additives.Films produced using PP 520L will exhibit:Consistent processabilityGood optical propertiesHigh melt strengthExcellent runnability on bagging and sealing machinesTypical Applications: PP 520L can be used for producing garment, textiles, magazine covers and for food packaging.Information provided by SABIC.

Physical Properties	Metric	English	Comments
Density	0.905 g/cc	0.0327 lb/in³	ASTM D792
Melt Flow	10 g/10 min @Load 2.16 kg, Temperature 230 °C	10 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	102	102	ASTM D785
Tensile Strength, Yield	35.0 MPa	5080 psi	ASTM D638
Elongation at Yield	10 %	10 %	ASTM D638
Flexural Modulus, 1% Secant	1600 MPa	232000 psi	ASTM D790A
Izod Impact, Notched	0.230 J/cm	0.431 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	105 °C	221 °F	ASTM D648
Vicat Softening Point	155 °C	311 °F	ASTM D1525B

Processing Properties	Metric	English	Comments
Processing Temperature	205 - 215 °C	401 - 419 °F	Barrel Temperature