Samsung Cheil Industries Infino® EM-8240C MPPE, Glass Filled
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Shanghai port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | Samsung Cheil Industries Infino® EM-8240C MPPE, Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
MPPE/GF material that is used in the main frame of banknote sortersInformation provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0030 cm/cm <br>@Thickness 3.20 mm |
0.0020 - 0.0030 in/in <br>@Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 25 g/10 min <br>@Load 10.0 kg,<br> Temperature 280 °C |
25 g/10 min <br>@Load 22.0 lb,<br> Temperature 536 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 98.1 MPa | 14200 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | 5 mm/min; ASTM D638 |
| Flexural Strength | 118 MPa | 17100 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 9.32 GPa | 1350 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.490 J/cm <br>@Thickness 3.17 mm |
0.918 ft-lb/in <br>@Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C <br>@Thickness 6.40 mm |
266 °F <br>@Thickness 0.252 in |
ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+6 ohm-cm <br>@Temperature 23.0 °C |
1.00e+6 ohm-cm <br>@Temperature 73.4 °F |
50% RH; ASTM 257 |
| Static Decay | <= 1.0 sec <br>@Temperature 23.0 °C |
<= 1.0 sec <br>@Temperature 73.4 °F |
50% RH; JIS L1049 |
Users viewing this material also viewed the following:
- Dielectric Polymers NT-240APS High Temperature Laminating Adhesive (discontinued **)
- LG Chemical LUTENE XL8080NT PE Compound
- Iran Petrochemical (PCC) TPC - 422 FC Expandable Polystyrene
- Covestro Desmopan® DP 9665DU Polyurethane
- Alliance S-20B Samarium Cobalt Magnetic Material
- Aclo Accutech Polypropylene Homopolymer HP0339M30CL Mica Reinforced Coupled
- Resinlab® EP1026R Rubber Modified Epoxy Adhesive
- Chesterton ARC S1HB Sprayable high-viscosity, 100% solids, advanced coating
Copyright © lookpolymers.com All Rights Reserved