Solvay Specialty Polymers RytonÂ® QA200P Polyphenylene Sulfide (PPS)

Category	Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS); Molded
Manufacturer	Solvay Specialty Polymers
Trade Name
Port	Ningbo port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	Solvay Specialty Polymers RytonÂ® QA200P Polyphenylene Sulfide (PPS).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

RytonÂ® QA200P (pelletized) unfilled polyphenylene sulfide exhibits excellent thermal stability and chemical resistance and may be used in injection molding processes.Features: Good Chemical Resistance; Good Thermal StabilityAdditional Properties: Ash Content - ISO 3451-1 0.1 wt%; Volatiles - (150Â°C): < 0.3 wt%Information provided by Solvay Specialty Polymers.

Physical Properties	Metric	English	Comments
Density	1.34 g/cc	0.0484 lb/inÂ³	ASTM D792
Water Absorption	0.050 % <br>@Time 86400 sec	0.050 % <br>@Time 24.0 hour	ISO 62
Linear Mold Shrinkage, Flow	0.010 cm/cm <br>@Thickness 3.18 mm	0.010 in/in <br>@Thickness 0.125 in
Melt Flow	100 g/10 min <br>@Load 5.00 kg,<br> Temperature 316 Â°C	100 g/10 min <br>@Load 11.0 lb,<br> Temperature 601 Â°F	Procedure B; ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Stress	80.0 MPa	11600 psi	ISO 527-2
Elongation at Break	4.0 %	4.0 %	ISO 527-2
Tensile Modulus	3.40 GPa	493 ksi	ISO 527-2
Flexural Strength	140 MPa	20300 psi	ISO 178
Flexural Modulus	3.40 GPa	493 ksi	ISO 178
Izod Impact, Notched	0.530 J/cm <br>@Thickness 3.18 mm	0.993 ft-lb/in <br>@Thickness 0.125 in	ASTM D256
Izod Impact, Notched (ISO)	4.00 kJ/mÂ²	1.90 ft-lb/inÂ²	Notch A; ISO 180

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	50.0 Âµm/m-Â°C <br>@Temperature -50.0 - 50.0 Â°C	27.8 Âµin/in-Â°F <br>@Temperature -58.0 - 122 Â°F	2
	120 Âµm/m-Â°C <br>@Temperature 100 - 200 Â°C	66.7 Âµin/in-Â°F <br>@Temperature 212 - 392 Â°F	2
Thermal Conductivity	0.290 W/m-K	2.01 BTU-in/hr-ftÂ²-Â°F	ASTM C177
Melting Point	280 Â°C	536 Â°F	ISO 11357-3
Deflection Temperature at 0.46 MPa (66 psi)	160 Â°C	320 Â°F	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	95.0 Â°C	203 Â°F	Unannealed; ASTM D648
Vicat Softening Point	>= 180 Â°C	>= 356 Â°F	ISO 306
Glass Transition Temp, Tg	90.0 Â°C	194 Â°F	ISO 11357-2
Flammability, UL94	V-0 <br>@Thickness 1.60 mm	V-0 <br>@Thickness 0.0630 in
Oxygen Index	44 %	44 %	ASTM D2863

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+16 ohm-cm	1.00e+16 ohm-cm	ASTM D257
Surface Resistance	1.00e+16 ohm	1.00e+16 ohm	ASTM D257
Dielectric Constant	3.2 <br>@Frequency 1.00e+6 Hz	3.2 <br>@Frequency 1.00e+6 Hz	ASTM D150
Dielectric Strength	24.0 kV/mm	610 kV/in	ASTM D149
Dissipation Factor	0.0020 <br>@Frequency 1.00e+6 Hz	0.0020 <br>@Frequency 1.00e+6 Hz	ASTM D150

Descriptive Properties	Value	Comments
Availability	Asia Pacific
	Europe
	Latin America
	North America
Color	Natural
Form	Pellets
Processing Technique	Injection Molding
RoHS Compliance	RoHS Compliant