Unitika B2040G50 PA66, 50% Glass Fiber Reinforced, Conditioned
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Glass Fiber Filled |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika B2040G50 PA66, 50% Glass Fiber Reinforced, Conditioned.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.4 % | 1.4 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 3.20 mm |
0.0020 in/in @Thickness 0.126 in |
|
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm @Thickness 3.20 mm |
0.0060 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 165 MPa | 23900 psi | ISO 527-1/-2 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1/-2 |
| Tensile Modulus | 11.2 GPa | 1620 ksi | ISO 527-1/-2 |
| Flexural Strength | 230 MPa | 33400 psi | ISO 178 |
| Flexural Modulus | 10.3 GPa | 1490 ksi | ISO 178 |
| Charpy Impact Unnotched | 10.2 J/cm² | 48.5 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 2.00 J/cm² | 9.52 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 20.0 µm/m-°C | 11.1 µin/in-°F | ISO 11359-2 |
Users viewing this material also viewed the following:
- Raschig Group EPOXIDUR® 3585 EP Epoxy, Molded, Glass Fiber Filler
- PolyOne Geon™ HC 3180G Polyvinyl Chloride, Flexible (PVC, Flexible)
- ExxonMobil Santoprene® 273-50 Thermoplastic Elastomer (discontinued **)
- Covestro Apec® DP 1-9389 Polycarbonate (discontinued **)
- Inno-Comp INNOPOL® CS 1-5120 BLH 20% Talc-Filled Polypropylene Homopolymer
- H.C. Starck Ampersint® MAP FeCoNi 40/20/40 For Hardmetals
- Latrobe CSS-42Lâ„¢ VIM-VAR High Performance Carburizing Stainless Steel; Bearing and Gear Steel
- Formosa Plastics Formolene® 5143H Homopolymer Polypropylene
- LATI LARAMID G/30 30% Glass Filled Polyphthalamide (PPA) Based Compound (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved