Physical Properties | Metric | English | Comments |
---|---|---|---|
Particle Size | 31 - 38 µm | 31 - 38 µm | 50% |
H.C. Starck Amperit® 110.2 Agglomerated Sintered (Mo-Mo2C) |
|||
Particle Size | 30 - 38 µm | 30 - 38 µm | 50% |
H.C. Starck Amperit® 512.074 Agglomerated Sintered Tungsten Carbide - Cobalt (WC-Co) 88-12 |
|||
Particle Size | 30 - 38 µm | 30 - 38 µm | 50% |
H.C. Starck Amperit® 519.074 Agglomerated, Sintered Tungsten Carbide-Cobalt 88-12 (WC-CO) |
|||
Particle Size | 32 - 38 µm | 32 - 38 µm | 50% |
H.C. Starck Amperit® 526.062 Agglomerated, Sintered Tungsten Carbide-Cobalt (WC-Co) 83-17 |
|||
Particle Size | 32 - 38 µm | 32 - 38 µm | 50% |
H.C. Starck Amperit® 526.074 Agglomerated, Sintered Tungsten Carbide-Cobalt (WC-Co) 83-17 |
|||
Particle Size | 30 - 38 µm | 30 - 38 µm | 50% |
H.C. Starck Amperit® 527.074 Agglomerated, Sintered Tungsten Carbide-Cobalt (WC-Co) 83-17 |
|||
Particle Size | 28 - 38 µm | 28 - 38 µm | 50% |
H.C. Starck Amperit® 539.054 Agglomerated, Sintered Tungsten Carbide-Tungsten Boride-Cobalt-Chromium (WC-WB-Co-Cr) 60-30-5-5 |
|||
Particle Size | 32 - 38 µm | 32 - 38 µm | 50% for WC-Co 83-17 |
H.C. Starck Amperit® 560.062 Tungsten Carbide-Cobalt(83-17)-Nickel-SF RC 60 50-50 (Wc-Co / NiSF RC 60) Composition is of NiSF RC 60 only |
|||
Particle Size | 30 - 38 µm | 30 - 38 µm | 50% |
H.C. Starck Amperit® 586.1 Chromium Carbide-Nickel Chromium 80-20 (Cr3C2-NiCr) |
|||
Particle Size | 14 - 38 µm | 14 - 38 µm | d90 |
Indium Corp. In2O3 Type A Indium Oxide, Crystalline Powder Indium Sesquioxide is a yellow colored powder. It is a stable ceramic-like material, insoluble in water and volatizes at 850°C. Indium sesquioxide is a n-type semiconductor and as such is used .. |
|||
Particle Size | 30 - 38 µm | 30 - 38 µm | MV |
H.C. Starck Amperit® 553.074 Tungsten Carbide-Cobalt-Chromium 86-10-4 (WC-Co-Cr) |
|||
Particle Size | 30 - 38 µm | 30 - 38 µm | 50% |
H.C. Starck Amperit® 558.074 Tungsten Carbide-Cobalt-Chromium 86-10-4 (WC-Co-Cr) |
|||
Particle Size | 31 - 38 µm | 31 - 38 µm | 50% |
H.C. Starck Amperit® 599.074 Agglomerated Sintered Molybdenum Carbide (Cr2O3) |
|||
Particle Size | 28 - 38 µm | 28 - 38 µm | D(0.5) |
Akzo Nobel Expancel® 093 DU 120 Dry unexpanded microspheres Expancel microspheres are thermoplastic hollow spheres. The microspheres are white spherically formed particles with a thermoplastic shell encapsulating a gas. When the microspheres are heated the.. |
|||
Particle Size | 28 - 38 µm | 28 - 38 µm | D(0.5) |
Akzo Nobel Expancel® 930 DU 120 Dry unexpanded microspheres Expancel microspheres are thermoplastic hollow spheres. The microspheres are white spherically formed particles with a thermoplastic shell encapsulating a gas. When the microspheres are heated the.. |
|||
Particle Size | 28 - 38 µm | 28 - 38 µm | D(0.5) |
Akzo Nobel Expancel® 092 DU 120 Dry unexpanded microspheres Expancel microspheres are thermoplastic hollow spheres. The microspheres are white spherically formed particles with a thermoplastic shell encapsulating a gas. When the microspheres are heated the.. |
|||
Particle Size | 28 - 38 µm | 28 - 38 µm | D(0.5) |
Akzo Nobel Expancel® 950 DU 120 Dry unexpanded microspheres Expancel microspheres are thermoplastic hollow spheres. The microspheres are white spherically formed particles with a thermoplastic shell encapsulating a gas. When the microspheres are heated the.. |
|||
Particle Size | 30 - 38 µm | 30 - 38 µm | 50% |
H.C. Starck Amperit® 547.059 Tungsten Carbide-Nickel 88-12 (WC-Ni) |
|||
Particle Size | 30 - 38 µm | 30 - 38 µm | 50% |
H.C. Starck Amperit® 551.074 Tungsten Carbide - Chromium Carbide - Nickel 70-20-7 (W-CrC-Ni) |