Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.75 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Polimeri Europa Clearflex® FF D0 Very Low Density Polyethylene Clearflex FF D0 is a linear low density polyethylene, with antioxidants, suitable for blown film technology.Films made with Clearflex FF D0 are highly transparent, have excellent sealing properties,.. |
|||
Melt Flow | 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.75 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Polimeri Europa Clearflex® H&T LFH 208 Octene Copolymer Linear Low Density Polyethylene Clearflex H&T LFH 208 is an octene copolymer linear low density polyethylene (C8-LLDPE), with antioxidants and processing aid, suitable for blown film extrusion.Films obtained from Clearflex H&T LFH.. |
|||
Melt Flow | 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.75 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Polimeri Europa Clearflex® H&T LFH 238 Octene Copolymer Linear Low Density Polyethylene Clearflex H&T LFH 238 is an octene copolymer linear low density polyethylene (C8-LLDPE), with antioxidants and processing aid, suitable for blown film extrusion. It contains slip and antiblocking a.. |
|||
Melt Flow | 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.75 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Polimeri Europa Riblene® FF 34 Low Density Polyethylene - Blown Film Extrusion Riblene FF 34 is a high molecular weight low density polyethylene (LDPE), with added slip and antiblocking agents, suitable for blown film extrusion. Riblene FF 34 is characterized by a good melt s.. |
|||
Melt Flow | 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.75 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
NOVA Chemicals Novapol® LF-Y819-D LDPE Film Resin Film Properties. Features: Good strength and toughness, excellent shrink film characteristics, excellent processability.Applications: Industrial packaging, liners, shrink film, blends with LLDPE.Da.. |
|||
Melt Flow | 0.75 g/10 min @Load 21.6 kg, Temperature 190 °C |
0.75 g/10 min @Load 47.6 lb, Temperature 374 °F |
ASTM D1238 |
SABIC HP0722N Low Density Polyethylene for Blown Film Product Description: HP0722N is a Low Density Polyethylene grade suitable for producing medium duty films and contains no slip or antiblock additives. It yields good toughness and optical properti.. |
|||
Melt Flow | 0.75 g/10 min | 0.75 g/10 min | Exxon Method |
ExxonMobil Exceed™ 399L60 LDPE/Hexene Premium Blown Film Resin, 3 mil Film
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A hexene copolymer produced using Exxon Chemical's EXXPOL® technology. Films made from EXCEED 399L60 resin have balanced tensile, impact strength,.. |
|||
Melt Flow | 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.75 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
NOVA Chemicals Novapol® LF-Y824-C LDPE Clarity Film Resin
(discontinued **) Features: High optical clarityExcellent processabilityExcellent shrink film characteristics Applications: High clarity shrink filmProduce and bakery filmTextile packaging filmInformation provided by.. |
|||
Melt Flow | 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.75 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
NOVA Chemicals Novapol® LF-Y819-A LDPE Film Resin Film Properties. Features: Good strength and toughness, excellent shrink film characteristics, excellent processability.Applications: Industrial packaging, shrink film, blends with LLDPE, small dia.. |
|||
Melt Flow | 0.75 g/10 min @Load 5.00 kg |
0.75 g/10 min @Load 11.0 lb |
ISO 1133 |
Total Lacqtene® 2002 TBL 40 HDPE pipe
(discontinued **) LACQTENE® 2002 TBL 40 is a blue stripe compound designed to be used in combination with LACQTENE® 2002 TBK 40 for gas pipe application. The base polymer of LACQTENE® 2002 TBL 40 is the same as th.. |
|||
Melt Flow | 0.75 g/10 min | 0.75 g/10 min | ASTM D1238 |
LyondellBasell Petrothene® GA818073 Linear Low Density Polyethylene ApplicationsPETROTHENE GA 818-073 offers the high environmental stress crack resistance characteristics of linear low density polyethylene with the processing properties needed for blowmolding and e.. |
|||
Melt Flow | 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.75 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Iran Petrochemical (PCC) LH0075 Low Density Polyethylene LH0075 is a high molecular weight low density polyethylene film grade combining good flexible extrusion behavior and superior mechanical properties.Applications: carrier bags, shrink film, industria.. |
|||
Melt Flow | 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.75 g/10 min @Load 4.76 lb, Temperature 374 °F |
|
JPJ Technologies LD 150 LDPE Virgin Applications: Used for heavy duty packaging, packaging bags, general film bag, etc.Information provided by JPJ Technologies |
|||
Melt Flow | 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.75 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Borealis FT5230 Low Density Polyethylene FT5230 is a Low Density Polyethylene for Film Extrusion. This grade is developed for the production of packaging film with good optical properties for medium duty film applications. Applications: .. |
|||
Melt Flow | 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.75 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Borealis FT5231 Low Density Polyethylene FT5231 is a Low Density Polyethylene for blown film. Tubular technology. Contains Antioxidant. This grade is developed for the production of packaging film with good optical properties for medium d.. |
|||
Melt Flow | 0.75 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.75 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Borealis HA104E Polypropylene Homopolymer HA104E is a natural high molecular weight, high melt flow rate polypropylene homopolymer characterized by well-balanced stiffness to impact strength ratio at increased processing properties. Applica.. |
|||
Melt Flow | 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.75 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Borealis Himod™ FT5270 LDPE for Film Himod FT5270 is a tubular, low-density polyethylene grade for the production of packaging films. Compared to standard LDPE grades, the Himod products provide a combination of higher stiffness and i.. |
|||
Melt Flow | 0.75 g/10 min @Temperature 230 °C |
0.75 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
A. Schulman POLYFORT™ FPP 1512E Talc Filled, High Impact Copolymer Polypropylene DescriptionPolyfort® FPP 1512E is a 10% talc-filled, high impact copolymer polypropylene. ApplicationPolyfort® FPP 1512E is suitable for extrusion or blow molding applications. Information provid.. |
|||
Melt Flow | 0.75 g/10 min | 0.75 g/10 min | ASTM D1238 |
A. Schulman POLYFORT™ PP 7001 Information provided by A. Schulman. |
|||
Melt Flow | 0.75 g/10 min | 0.75 g/10 min | ASTM D1238 |
A. Schulman POLYFORT™ PP 7001 Information provided by A. Schulman. |
|||
Melt Flow | 0.75 g/10 min | 0.75 g/10 min | ASTM D1238 |
A. Schulman POLYFORT™ PP 7001 Information provided by A. Schulman. |
|||
Melt Flow | 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.75 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Total EVA 1005 VN 5 Ethylene Vinyl Acetate Copolymer - Blown Film EVA 1005 VN 5 is made by a high pressure tubular process. Grade for films with high transparency and good mechanical properties. Contains an antioxidant.Application examples: Coextrusion, stretch .. |
|||
Melt Flow | 0.75 g/10 min | 0.75 g/10 min | ASTM D1238E |
Chevron Phillips MarFlex® 9656 HDPE Blown Film Resin Resin Type: high density, linear polyethylene.Characteristics: copolymerization enhances film toughness, good drawdown, density level gives good machinability, blend well with LLDPEApplications: not.. |
|||
Melt Flow | 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.75 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ExxonMobil LDPE LD 150AC Low Density Polyethylene Resin Product Description: LD 150 series are LDPE grades, offering good blend mechanical properties and stiffness. Several additive packages are available according to the required surface properties.Avai.. |
|||
Melt Flow | 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.75 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ExxonMobil LDPE LD 156BW Low Density Polyethylene Resin Product Description: LD 156 series are LDPE grades, specially designed for lamination films and co-extruded films. They offer good mechanical, stiffness and optical properties, combined with very lo.. |
|||
Melt Flow | 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.75 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM-D1238 |
Braskem FC31D LLDPE Blown Film Extrusion Polyethylene Copolymer The FC31D resin is a linear low-density polyethylene, copolymer of butene -1, produced by the solution process for blow film extrusion. It has excellent mechanical properties, especially hot tack. I.. |
|||
Melt Flow | 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.75 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM-D1238 |
Braskem LL6800N LLDPE Blown Film Extrusion Polyethylene Copolymer LL6800N resin is a linear low-density polyethylene, copolymer of octene-1, produced by the solution process for blown film extrusion with excellent mechanical properties. It contains antiblock, proc.. |
|||
Melt Flow | 0.75 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.75 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM-D1238 |
Braskem PCD 0140 HECO Polypropylene Heterophasic Copolymer PCD 0140 is a low melt flow rate heterophasic copolymer with high impact resistance. This resin was developed for steel pipe coating extrusion. PCD 0140 is highly protected against thermal aging and.. |
|||
Melt Flow | 0.75 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.75 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM-D1238 |
Braskem PCD 0140BR HECO Polypropylene Heterophasic Copolymer PCD 0140BR is a low melt flow rate heterophasic copolymer with high impact resistance. This resin was developed for steel pipe coating extrusion. PCD 0140BR is highly protected against thermal aging.. |
|||
Melt Flow | 0.75 g/10 min @Temperature 230 °C |
0.75 g/10 min @Temperature 446 °F |
ASTM D1238 |
Total PPC 4170 Polypropylene, Impact Copolymer, Blown Film Grade TOTAL Petrochemicals Polypropylene 4170 is a polypropylene impact copolymer grade with good melt strength for use in the extrusion of blown films.Benefits. 4170 forms tough films with high dart imp.. |