ExxonMobil LDPE LD 156BW Low Density Polyethylene Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer Exxon Chemical
Trade Name LDPE
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LDPE LD 156BW Low Density Polyethylene Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: LD 156 series are LDPE grades, specially designed for lamination films and co-extruded films. They offer good mechanical, stiffness and optical properties, combined with very low gel level. These grades have a Film Appearance specification. Two additive packages are available tailored to the needs of the laminator. LD 156 is manufactured with narrow specifications to suit the high consistency requirements of lamination films.Availability: Africa & Middle East and Europe Additive: Antiblock: NoSlip: NoThermal Stabilizer: YesApplications: Blend PartnerCo-Extrusion FilmsCollation ShrinkForm Fill and Seal PackagingFreezer FilmHigher Quality LaminationLamination FilmMedium Duty Shrink FilmShoppersInformation provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.926 g/cc
0.0335 lb/in³
ExxonMobil method
Melt Flow 0.75 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.75 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 420 %
420 %
ASTM D882
Film Elongation at Break, TD 560 %
560 %
ASTM D882
Elmendorf Tear Strength MD 280 g
280 g
ASTM D1922
Elmendorf Tear Strength TD 200 g
200 g
ASTM D1922
Dart Drop Test 120 g
0.265 lb
ASTM D1709A
Film Tensile Strength at Break, MD 30.3 MPa
4400 psi
ASTM D882
Film Tensile Strength at Break, TD 24.8 MPa
3600 psi
ASTM D882
1% Secant Modulus, MD 248 MPa
36000 psi
ASTM D882
1% Secant Modulus, TD 290 MPa
42000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point <= 235 °C
<= 455 °F
Peak Melting Point; ExxonMobil method
Optical Properties Metric English Comments
Haze 6.0 %
6.0 %
ASTM D1003
Gloss 68 %
68 %
45°; ASTM D2457