Polymer Property : Compressive Strength = 40000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Compressive Strength	276 MPa	40000 psi
Mykroy/Mycalex MM 500 Machining Grade Glass-bonded Mica Composite Synthetic mica filler. Does not burn. Better radiation resistance (3 x 10^10 Rads-Cobalt) than grade 400.This ceramoplastic material is a versatile and efficient insulating material designed to me..
Compressive Strength	276 MPa	40000 psi
Mykroy/Mycalex MM 800 Machining Grade Glass-bonded Mica Composite MM 800 (formerly MM 1600) is a compression molded glass mica composite that is the perfect alternative to high performance plastics where high temperature, good dielectric strength and good arc resi..
Compressive Strength	276 MPa @Temperature 23.9 °C	40000 psi @Temperature 75.0 °F	Dry; 325°F 2kpsi; ASTM D695
Park Electrochemical Nelcote® F-554 Phenolic Prepreg, Chopped Molding Compound Reinforced Nelcote® F-554 is a high purity silica filled phenolic resin coated on Commercial or Aerospace grade silica fabric. F-554 is used in the manufacture of intermediate temperature ablative rocket nozz..
Compressive Strength	276 MPa	40000 psi
Novum Glass Solid Soda-lime Industrial Series Glass Microspheres Solid soda-lime glass microspheres in colorless powder form. Industrial Series Microspheres are solid glass microspheres (also referred to as soda lime glass beads, glass spheres, or microbeads) us..
Compressive Strength	276 MPa	40000 psi
Novum Glass Solid Soda-lime Technical Series Glass Microspheres Solid soda-lime glass microspheres in colorless powder form. Technical Series Microspheres are solid glass microspheres that have a narrow particle size distribution. Used for chromatography, colum..
Compressive Strength	276 MPa	40000 psi	ASTM D695
Resinoid 7051 Phenolic Molding, Glass Reinforced Data provided by the manufacturer.The Resinoid 1300 and 7000 glass fiber reinforced series compounds feature mechanical strength, dimensional stability, electrical insulation, and heat resistance
Compressive Strength	276 MPa	40000 psi	ASTM D695
Solvay Specialty Polymers Amodel® AS-1133 HS Polyphthalamide (PPA) (Unverified Data**) Amodel AS-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts, even those with wall thicknesses greater than 0..
Compressive Strength	276 MPa	40000 psi	10% Def.; ASTM D695
Quadrant EPP Duratron® PAI T5030 Polyamide-imide, glass reinforced, extruded (ASTM Product Data Sheet)
Compressive Strength	276 MPa	40000 psi
Novum Glass Solid Soda-lime Uniform Series Glass Microspheres Solid soda-lime glass microspheres in colorless powder form. Uniform Series Microspheres are used for controlling a bond line thickness in adhesive bonding. Solid glass microspheres are used in a v..
Compressive Strength	276 MPa @Thickness 12.7 mm	40000 psi @Thickness 0.500 in	ASTM D695
Industrial Laminates/Norplex NP613 Paper Base Laminate Description: NP613 is constructed from electrical grade of kraft paper and a specially modified epoxy resin system. It is designed to be used in tap changers, coil support plates and terminal panels..
Compressive Strength	276 MPa @Thickness 12.7 mm	40000 psi @Thickness 0.500 in	ASTM D695
Industrial Laminates/Norplex NP639 Paper Base Laminate Description: Economical paper reinforced laminate developed with capacity to withstand temperatures to 150Â° C without blistering. High compressive strength and low moisture absorption.Thickness T..
Compressive Strength	276 MPa	40000 psi
Haysite H755 Glass Reinforced Polyester Sheet, Electrical Grade (GPO1) A new generation of IEEE Class F, 155ÂºC /165ÂºC NEMA GPO- 1 material. H755 is designed to bridge the gap between 130ÂºC Class B GPO-1 materials and Class H 180ÂºC grades. H755 has quickly g..
Compressive Strength	276 MPa	40000 psi	Axial; ASTM D695
Glastic Laminates/Shapes MTS Grade MTS Fiberglass-Reinforced Polyester Rod Data provided by Glastic Corporation.A continuous-filament fiberglass-roving provides superior strength.
Compressive Strength	276 MPa	40000 psi	ASTM D695
Solvay Specialty Polymers AmodelÂ® AS-1133 HS Polyphthalamide (PPA), 33% Glass Fiber (Dry) AmodelÂ® AS-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts, even those with wall thicknesses greater th..
Compressive Strength	276 MPa	40000 psi	ASTM D695
Sumitomo Bakelite DurezÂ® 32633 Glass Filled Phenolic, Injection Grade Durez 32633 Black Phenolic is a two-stage, glass filled, special purpose molding compound. It is designed for applications requiring high physical strengths, dimensional stability, and heat resista..
Compressive Strength	276 MPa	40000 psi	Maximum Static Bearing Load
TriStar TriSteel PE Metal Backed PTFE Bearing System Ultraflon 603 PE lined metal backed bearing system, with or without lube, high PV, high temperature... Ultraflon 603 PE Liner is a bearing grade polymer for use in lubricated or unlubricated environ..
Compressive Strength	276 MPa	40000 psi	10% Deformation; ASTM D695
Ensinger Tecapeek® XP-111 Compression Molded PEEK Compound, 50% Carbon Fiber Ensinger Special Polymers offers over twenty different VICTREX® PEEK blends to choose from and has the capability to blend custom compounds for specific applications. Compression molding results in..
Compressive Strength	276 MPa	40000 psi	ASTM D695
Resinoid 7051 SS Phenolic Molding, Glass Reinforced Data provided by the manufacturer.The Resinoid 1300 and 7000 glass fiber reinforced series compounds feature mechanical strength, dimensional stability, electrical insulation, and heat resistance