Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 2.50 GPa | 363 ksi | |
Murtfeldt Murlubric® [FS] Oil Modified Nylon 6 Murlubric® is a modified cast polyamide that mineral oil is integrated into during polymerization. As a result, the material has self lubricating properties and retains its excellent characteristi.. |
|||
Modulus of Elasticity | 2.50 GPa | 363 ksi | 4 mm thick;10.0 mm wide molded rod; ISO 178 |
Premix Thermoplastics PRE-ELEC® PC 1431 PRE-ELEC PC 1431 is a conductive thermoplastic compound based on polycarbonate. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELE.. |
|||
Modulus of Elasticity | 2.50 GPa | 363 ksi | DIN 53457 |
Ineos Nova S-3400 Medium Impact Compact Polystyrene
(discontinued **) Impact polystyrene with good flow characteristics and a high elongation. Generally used for applications where a tough material is required. For injection molding generally a lubricated type is us.. |
|||
Modulus of Elasticity | 2.50 - 8.10 GPa @Temperature 40.0 - 140 °C |
363 - 1170 ksi @Temperature 104 - 284 °F |
Average value: 5.10 GPa Grade Count:2 |
Overview of materials for Acetal Copolymer, 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% ar.. |
|||
Modulus of Elasticity | 2.50 - 5.88 GPa | 363 - 853 ksi | Average value: 3.66 GPa Grade Count:21 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled". Specific grades with glass content betwe.. |
|||
Modulus of Elasticity | 2.50 - 3.00 GPa | 363 - 435 ksi | Average value: 2.75 GPa Grade Count:4 |
Overview of materials for PVC, Uncompounded This property data is a summary of similar materials in the MatWeb database for the category "PVC, Uncompounded". Each property range of values reported is minimum and maximum values of appropriate .. |
|||
Modulus of Elasticity | 2.50 GPa | 363 ksi | |
Lehmann & Voss LUVOCOM® 1301-8148 PPS, linear, with PTFE Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.Improved friction and wear behaviour. Emergency running property.Low warpage, isotropic shrinkage .. |
|||
Modulus of Elasticity | 2.50 GPa | 363 ksi | |
Lehmann & Voss LUVOCOM® 1502-7866/GN4 PPSU, unreinforced Applications: Automotive industry, medical- and precision engineering, aircraft industry.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistanceHigh chemical res.. |
|||
Modulus of Elasticity | 2.50 GPa | 363 ksi | |
Lehmann & Voss LUVOCOM® 1700-8541 PPO, unreinforced Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Dynamic stressed parts.Isotropic shrinkage characteristics.Superheated steam sterilizable.Infor.. |
|||
Modulus of Elasticity | 2.50 GPa | 363 ksi | |
Lehmann & Voss LUVOCOM® 1850/TF/30 PBT, with PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri.. |
|||
Modulus of Elasticity | 2.50 GPa | 363 ksi | |
Lehmann & Voss LUVOCOM® 1850-7795 PBT, with PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri.. |
|||
Modulus of Elasticity | 2.50 GPa | 363 ksi | |
Lehmann & Voss LUVOCOM® 50-8479/BL-1 Polycarbonate, unreinforced Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Isotropic shrinkage characteristics.Reduced moment of inertia .. |
|||
Modulus of Elasticity | 2.50 GPa | 363 ksi | ISO 527 |
GEHR Plastics Corzan® PVC-C Polyvinylchloride Polyvinyl chloride is a flame retardant material with an exceptional chemical resistance and also with lower stress cracking. PVC-U shows high mechanical strength, tensile strength and the continuou.. |
|||
Modulus of Elasticity | 2.50 GPa | 363 ksi | |
Lehmann & Voss LUVOCOM® 1502-7865/BK2 PPSU, unreinforced Applications: Automotive industry, medical- and precision engineering, aircraft industry.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistanceHigh chemical res.. |
|||
Modulus of Elasticity | 2.50 GPa | 363 ksi | ISO 527-2 |
Tisan TISAKRIL® Flame Retardant (V0) ABS TISAKRIL has a wide area of application in automotive, electronics, computer, construction, and furniture industries. General Specifications include: High surface luminosityEasy processabilityDimens.. |
|||
Modulus of Elasticity | 2.50 GPa | 363 ksi | ISO 527-2 |
Tisan TISESTER® UNR Polybutylene Terephthalate TISESTER has a wide area of application in automotive, electric/electronics and durable goods industries. General Specifications include: Excellent surface appearanceHigh corrosion and abrasion resi.. |
|||
Modulus of Elasticity | 2.50 GPa | 363 ksi | ISO 527-2 |
Tisan TISOPLEN® 15% Mineral Filled Flame Retardant (V0). Heat Stabilized Polypropylene TISOPLEN has a wide area of application in furniture, durable goods, household appliances, electrics/electronics, and telecommunication industries. General specifications include Low densityLow mois.. |
|||
Modulus of Elasticity | 2.50 GPa | 363 ksi | MD; ExxonMobil Method |
ExxonMobil Metallyte™ 15MM288 OPP Film Product Description: A high barrier, non-sealable OPP film with one-side metalized and one-side treated. MM288 is designed for use as the center web of a triplex lamination. The treated surface offe.. |
|||
Modulus of Elasticity | 2.50 GPa | 363 ksi | TD; ExxonMobil Method |
ExxonMobil Oppalyte™ 50MO747 OPP Film Product Description: A white opaque biaxially oriented polypropylene film, coated on one side acrylic, one side PVdC. Provides excellent performance on all packaging machines.Availability: Africa & .. |
|||
Modulus of Elasticity | 2.50 GPa | 363 ksi | ISO 178 |
Addiplast Addilene J 522 N30 Polypropylene Copolymer Mineral reinforced, improved scratch resistanceInformation provided by Addiplast. |
|||
Modulus of Elasticity | 2.50 GPa @Temperature 140 °C |
363 ksi @Temperature 284 °F |
SIO 527 |
BASF Ultraform N 2200 G53 UNC Q600 25% Glass Filled POM Ultraform N2200 G53 UNC Q600 is a 25% glass fiber reinforced POM injection molding grade with enhanced stiffness and toughness. |
|||
Modulus of Elasticity | 2.50 GPa @Temperature 60.0 °C |
363 ksi @Temperature 140 °F |
ISO 527 |
BASF Ultrason E 2010 PES Ultrason E 2010 is an unreinforced, medium viscosity standard injection molding PES grade. It flows readily and offers outstanding heat resistance and dimensional stability. It conforms to FDA req.. |
|||
Modulus of Elasticity | 2.50 GPa | 363 ksi | 1 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 1009 PVDF Homopolymer
(discontinued **) Key features of this grade: Mean Viscosity, All Purpose, Injection/Extrusion, Virgin. Recommended processing is extrusion. Available as powder & granules.General information about SOLEF® PVDF: SO.. |
|||
Modulus of Elasticity | 2.50 GPa | 363 ksi | 1 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 1010 PVDF Homopolymer
(discontinued **) Key features of this grade: Med Viscosity, All Purpose, Extrusion, Virgin. Recommended processing is extrusion. Available as powder & granules.General information about SOLEF® PVDF: SOLEF® PVDF .. |
|||
Modulus of Elasticity | 2.50 - 3.80 GPa | 363 - 551 ksi | Average value: 3.12 GPa Grade Count:5 |
Overview of materials for Nylon 66, Nucleated This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Nucleated". Each property range of values reported is minimum and maximum values of appropriat.. |
|||
Modulus of Elasticity | 2.50 GPa | 363 ksi | ISO 178 |
Addiplast Addilene H 462 M20 Polypropylene Homopolymer High heat resistance, detergent stabilized, anti-yellowingInformation provided by Addiplast. |
|||
Modulus of Elasticity | 2.50 - 4.83 GPa | 363 - 700 ksi | Average value: 3.86 GPa Grade Count:12 |
Overview of materials for Polypropylene with 40% Mica Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 40% Mica Filler". Specific grades with primary filler content between 35% and 44% are.. |