Solvay Specialty Polymers Solef® 1009 PVDF Homopolymer  (discontinued **)

Category Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), Molded/Extruded
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Solef® 1009 PVDF Homopolymer  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Key features of this grade: Mean Viscosity, All Purpose, Injection/Extrusion, Virgin. Recommended processing is extrusion. Available as powder & granules.General information about SOLEF® PVDF: SOLEF® PVDF is a fluorinated semi-crystalline thermoplastic which is obtained by polymerizing vinylidene fluoride. Important properties include excellent chemical resistance to most aggressive substances and solvents, excellent mechanical strength and toughness, high abrasion resistance, high temperature capabilities, excellent aging resistance, high purity, resistance to UV and nuclear radiation, excellent intrinsic fire resistance, resistance to weathering, low permeability to most gases and liquids, and easily melt-processed by standard methods of molding and extrusion.Tensile properties are achieved with varying methods of sample fabrication. Information provided by Solvay Solexis, Inc.
Physical Properties Metric English Comments
Density 1.78 g/cc
0.0643 lb/in³
ISO 1183
Water Absorption <= 0.040 %
<= 0.040 %
ISO 62 (method 1)
Linear Mold Shrinkage 0.020 - 0.030 cm/cm
0.020 - 0.030 in/in
Melt Flow 3.5 g/10 min

@Load 2.16 kg,
Temperature 230 °C
3.5 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
10 g/10 min

@Load 5.00 kg,
Temperature 230 °C
10 g/10 min

@Load 11.0 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 78

@Thickness 2.00 mm
78

@Thickness 0.0787 in
ASTM D2240
Tensile Strength, Ultimate 35.0 - 50.0 MPa
5080 - 7250 psi
50 mm/min; ASTM D638
Tensile Strength, Yield 53.0 - 57.0 MPa
7690 - 8270 psi
50 mm/min; ASTM D638
Elongation at Break 20 - 50 %
20 - 50 %
50 mm/min; ASTM D638
Elongation at Yield 5.0 - 10 %
5.0 - 10 %
50 mm/min; ASTM D638
Modulus of Elasticity 2.50 GPa
363 ksi
1 mm/min; ASTM D638
Flexural Yield Strength 77.0 MPa
11200 psi
2 mm/min; ASTM D790
Flexural Modulus 2.10 GPa
305 ksi
2 mm/min; ASTM D790
Izod Impact, Notched 0.650 J/cm

@Thickness 4.00 mm,
Temperature 23.0 °C
1.22 ft-lb/in

@Thickness 0.157 in,
Temperature 73.4 °F
Notched V 10 mm; ASTM D256
Coefficient of Friction 0.20 - 0.30
0.20 - 0.30
ASTM D1894
Coefficient of Friction, Static 0.20 - 0.40
0.20 - 0.40
ASTM D1894
Taber Abrasion, mg/1000 Cycles 5.0 - 10
5.0 - 10
CS10 / 1 kg
Thermal Properties Metric English Comments
Heat of Fusion 58.0 J/g
25.0 BTU/lb
Crystallization Heat
67.0 J/g
28.8 BTU/lb
80°C to end of melting
CTE, linear 120 - 140 µm/m-°C

@Temperature 20.0 °C
66.7 - 77.8 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Specific Heat Capacity 1.20 J/g-°C
0.287 BTU/lb-°F
1.60 J/g-°C

@Temperature 100 °C
0.382 BTU/lb-°F

@Temperature 212 °F
Thermal Conductivity 0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
ASTM C177
Melting Point 174 °C
345 °F
Crystallinity by DSC; ASTM D 3418
Crystallization Temperature 140 °C
284 °F
Deflection Temperature at 0.46 MPa (66 psi) 147 °C

@Thickness 4.00 mm
297 °F

@Thickness 0.157 in
after annealing 150°C 16 hr; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 113 °C

@Thickness 4.00 mm
235 °F

@Thickness 0.157 in
after annealing 150°C 16 hr; ASTM D648
Vicat Softening Point 171 °C

@Load 1.00 kg,
Thickness 4.00 mm
340 °F

@Load 2.20 lb,
Thickness 0.157 in
ISO 306
Brittleness Temperature 0.000 - 10.0 °C
32.0 - 50.0 °F
ASTM D746A
Glass Transition Temp, Tg -30.0 °C
-22.0 °F
DMTA
Decomposition Temperature 375 - 400 °C
707 - 752 °F
Thermal Stability via TGA : beginning - and at 1% weight loss in air
Oxygen Index 44 %

@Thickness 3.00 mm
44 %

@Thickness 0.118 in
sheet; ASTM D2863
Electrical Properties Metric English Comments
Electrical Resistivity >= 1.00e+14 ohm-cm
>= 1.00e+14 ohm-cm
Intensity = 10 mA after 2 min @ 23°C; ASTM D 257; DIN 53483
Surface Resistance >= 1.00e+14 ohm
>= 1.00e+14 ohm
Voltage < 1 V after 2 min - 500 V; ASTM D 257/DIN 53483