Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 73.8 MPa | 10700 psi | ASTM D790 |
PolyOne Geon™ Vinyl Rigid Molding M5005 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
Flexural Strength | 74.0 MPa | 10700 psi | ISO 178 |
Nilit FRIANYL B63 SG 10 Nylon 6 for injection molding, 10% mineral filled Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Strength | 74.0 MPa | 10700 psi | |
Manifattura Cattaneo PVDF Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | 2mm/min; ASTM D790 |
Kingfa PA66-R0N Flame Retardant PA66 Features:Flame retardantHigh strengthHigh temperature propertiesGood electric propertiesNo bloomingApplications:Injection moldingConnectorsRelay, bobbins, plugsHousehold appliance partsE & E partsIn.. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | ASTM D790 |
Kolon KOCETAL® SO301 Wear Modified Acetal Resin Silicone Oil added, improved wear property. Information provided by API-Kolon. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP IAL12 PA6.12 LNP* LUBRICOMP* IAL12 is a compound based on Nylon 6/12 resin containing 5% PTFE, 10% Aramid Fiber. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRILOY RX05498 PA 66 (Asia Pacific) LNP LUBRILOY* RX05498 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: High Impact. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRILOY RX99650 PA 66 (Asia Pacific) LNP LUBRILOY* RX99650 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | ASTM D 790 |
SABIC Innovative Plastics LNP Lubriloy Z2000 PPE+PS LNP* Lubriloy* Z2000 is a compound based on PPE+PS Blend resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP fo.. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRILOY Z2000 PPE+PS (Asia Pacific) LNP* Lubriloy* Z2000 is a compound based on PPE+PS Blend resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 73.8 MPa | 10700 psi | ASTM D790 |
Techmer ES Plastiblend® ABS 8005 Availability: North AmericaForms: PelletsFeatures: High Heat ResistanceInformation provided by TP Composites, Inc. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP KZ002 Acetal LNP* THERMOCOMP* KZ002 is a compound based on Acetal containing 10% Milled Glass. |
|||
Flexural Strength | 73.5 MPa | 10700 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® BF-0670T MABS, Unreinforced Scratch Resistant Scratch resistant material that is used in the exterior of electric products and household appliancesInformation provided by Samsung Cheil Industries. |
|||
Flexural Strength | 73.5 MPa | 10700 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® SF-0950 MABS, Unreinforced Scratch Resistant Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 73.5 MPa | 10700 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® HP-1000H PC/ABS, Unreinforced Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 73.5 MPa | 10700 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® HP-1000XA PC/ABS, Unreinforced PC/ABS material for automobile IP-coreInformation provided by Samsung Cheil Industries. |
|||
Flexural Strength | 73.5 MPa | 10700 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® HP-1011 PC/ABS, Unreinforced Material with superior flowability and small gas generation that can be used in the exterior material of mobile phonesInformation provided by Samsung Cheil Industries. |
|||
Flexural Strength | 73.5 MPa | 10700 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® BF-0670T MABS, Unreinforced Scratch Resistant Scratch resistant material that is used in the exterior of electric products and household appliancesInformation provided by Samsung Cheil Industries. |
|||
Flexural Strength | 73.5 MPa | 10700 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® SF-0950 MABS, Unreinforced Scratch Resistant Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOTUF V1000 PA 66 LNP THERMOTUF* V1000 is a compound based on Nylon resin. Added features of this material include: High Impact. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | ASTM-D790 |
Polyram RamShine PV801 ABS, Impact Modified Impact modified ABS for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | Outer Fiber Stress at 3.5% Outer Fiber Strain; DIN EN ISO 178 |
Wolf Kunststoff ZEDEX® ZX-530 A5D Polymer Alloy Main Characteristics: Low Creep; Low moisture absorption; Flame retardant; Low impurity ions; Good machinability; FDA compliant LABS; Extremely low outgassing; Less expensive than PEEK; Stress resis.. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | ASTM D790 |
Plenco 4504 Phenolic, Granular, Compression Molded Plenco 04504 is a renumber of Plaslok 504. Plenco 04504 is a two-stage, mineral and cellulose-filled phenolic molding compound having better impact and heat resistance than general purpose molding c.. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | ISO 178 |
Cyclics CBT® 100 Thermoplastic Resin CBT® 100 resin melts to a water-like viscosity when heated, then polymerizes into the engineering thermoplastic resin polybutylene terephthalate (PBT). CBT 200 resin has a processing range between.. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | ISO 178 |
Cyclics CBT® 200 Thermoplastic Resin CBT® 200 resin melts to a water-like viscosity when heated, then polymerizes into the engineering thermoplastic resin polybutylene terephthalate (PBT). CBT 200 resin has a processing range between.. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | 15mm/min; ASTM D790 |
Denka MALECCA K-100 ABS A heat-resistant ABS resin based on "DENKA IP" – a Styrene-N-Phenylmaleimide copolymer. It has been designed as an easy-to-use resin by improving conventional heat-resistant ABS resins which had de.. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | ISO 178 |
Azoty Tarnow™ TARNOFORM 300 GB6 POM 30% glass beads filled grade with increased stiffness and hardness with lowered shrinkageInformation provided by Zakłady Azotowe w Tarnowie-Moscicach S.A. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | 23°C, 50% RH; ASTM D790 |
Asahi Kasei Xyron® 240V Modified Polyphenylene Ether Flame RetardantInformation provided by Asahi Kasei |
|||
Flexural Strength | 74.0 MPa @Strain 5.00 %, Temperature 23.0 °C |
10700 psi @Strain 5.00 %, Temperature 73.4 °F |
ASTM D790 |
DuPont Performance Polymers Delrin® 577 BK000 Acetal Homopolymer
(Unverified Data**) Delrin® 577 BK000 is a medium viscosity acetal homopolymer containing 20% glass fiber filler, with high stiffness, low warpage and low creep for superior performance at elevated temperature. It con.. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP JF002R PES (Europe-Africa-Middle East) LNP* Thermocomp* JF002R is a compound based on Polyethersulfone resin containing Glass Fiber, Glass Bead. Added features of this material include: Mold Release. |