Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 93.5 MPa | 13600 psi | ASTM D790 |
PolyOne Geon™ Vinyl Rigid Extrusion 87717 Polyvinyl Chloride, Rigid (PVC, Rigid) The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne |
|||
Flexural Strength | 93.9 MPa | 13600 psi | X, Y direction; Condition A; ASTM D790 |
Rogers Corporation TMM® TMM10 Ceramic Thermoset Polymer Composite TMM® Thermoset microwave materials are ceramic thermoset polymer composites designed for high plate-thru-hole reliability stripline and microstrip applications. The electrical and mechanical prope.. |
|||
Flexural Strength | 94.0 - 101 MPa | 13600 - 14600 psi | ASTM D790 |
Proto3000 Accura® 45HC Plastic Stereolithography (SLA) Prototyping Polymer A high speed material, with excellent thermal and moisture resistance for producing functional prototypes in 3D Systems' SLA 250 systems.Benefits:Fast build speed:Provides build speeds that are sign.. |
|||
Flexural Strength | 94.0 MPa | 13600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® 500ECR PC (Europe-Africa-Middle East) Lexan* 500ECR Polycarbonate (PC) resin is a 10% glass fiber filled, injection moldable grade. It is of non-chlorinated & non-brominated flame retardant systems with UL-94 V0 rating at 2.3mm. It is a.. |
|||
Flexural Strength | 93.8 MPa | 13600 psi | ASTM D790 |
Polymer Resources PC-G10-IM Polycarbonate, 10% Glass Reinforced, Impact Modified Polycarbonate, 10% Glass Reinforced, Impact ModifiedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information .. |
|||
Flexural Strength | 93.77 MPa | 13600 psi | |
Abatron AboCast 8-4/Abocure 8-4 Epoxy
(discontinued **) 2-part solvent-free dielectric epoxy casting compound.Processing: 100/60 ratio (pbw); Gel time, 100 g (3.5 oz.): 240 minutes; cures in 3 weeks at 25°C (77°F).Applications: solventless casting, adh.. |
|||
Flexural Strength | 94.0 MPa | 13600 psi | |
Misumi Machinable SiO2-MgO Ceramic Information provided by MISUMI Corporation. |
|||
Flexural Strength | 94.0 MPa | 13600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP KFP032 Acetal Copolymer LNP LUBRICOMP* KFP032 is a compound based on Acetal Copolymer resin containing 10% Glass Fiber, 15% PTFE/Silicone. Added feature of this material is: Wear Resistant. |
|||
Flexural Strength | 94.0 MPa | 13600 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP ZX05506 PPE+PS LNP LUBRICOMP* ZX05506 is a compound based on PPE+PS Blend resin containing Graphite Powder, PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 94.0 MPa | 13600 psi | 2mm/min; ISO 178 |
Teijin Multilon TN-7100F Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy Halogen-free flame retardant PC/ABS polymer alloy, and is also antimony-free. High stiffness and flowability realize the thin wall of large-scale business machine chassis.Information provided by Tei.. |
|||
Flexural Strength | 94.1 MPa | 13600 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® NE-1010 PC/ABS, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 94.0 MPa | 13600 psi | 2mm/min; ISO 178 |
Teijin Panlite® L-1225Z100 Transparent and Weather Resistant grade Polycarbonate Resin Conforms to SAE regulations. It is an injection molding grade that has slightly high fluidity, weather resistance and mold release property and is bluish-tinted to exhibit clear colorApplications:Co.. |
|||
Flexural Strength | 94.1 MPa | 13600 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® TH-1100 PC, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 94.1 MPa | 13600 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® NE-1010 PC/ABS, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 93.8 MPa | 13600 psi | Method I (3 point load), 2.0 mm/min; ISO 178; ASTM D790 |
Styron CALIBREâ„¢ 5101-15 Polycarbonate Resin Overview: CALIBREâ„¢ 5101 Polycarbonate resin is 10% glass-reinforced and provides increased modulus and improved heat distortion resistance with minimal shrinkage. This resin offers outstanding .. |
|||
Flexural Strength | 93.8 MPa | 13600 psi | Method I (3 point load), 2.0 mm/min; ISO 178; ASTM D790 |
Styron CALIBREâ„¢ 5101-8 Polycarbonate Resin Overview: CALIBREâ„¢ 5101 Polycarbonate resins 10% glass-reinforced and provides increased modulus and improved heat distortion resistance with minimal shrinkage. This resin offers outstanding UL.. |
|||
Flexural Strength | 94.0 MPa @Thickness 4.00 mm |
13600 psi @Thickness 0.157 in |
2mm/min, injection molded, unannealed; ISO 178 |
Styron EMERGEâ„¢ 8600-20 Polycarbonate EMERGEâ„¢ PC 8600-20 is a translucent, ignition-resistant and easy flow polycarbonate resin. The resin contains no bromine, chlorine or phosphate additives and is intended to comply with global .. |
|||
Flexural Strength | 94.0 MPa | 13600 psi | at rupture; ASTM D790 |
Sumitomo Bakelite North America E 3812M-1 Mineral and Glass Filled Electrical Encapsulation Grade Epoxy E 3812M-1 is a mineral and short fiberglass filled epoxy molding compound for low pressure encapsulation molding, featuring excellent dimensional stability, good thermal shock resistance, and good e.. |
|||
Flexural Strength | 94.0 MPa | 13600 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP NF001XXX PC+ABS LNP* THERMOCOMP* PCA-F-1001 is a compound based on PC+ABS resin containing 5% Glass Fiber. |
|||
Flexural Strength | 94.0 MPa | 13600 psi | 2mm/min; ISO 178 |
Teijin Panlite® LV-2225Z Transparent and Weather Resistant grade Polycarbonate Resin Injection molding grade that is necessary to be slightly high fluidity. It has weather resistance, mold release property and is bluish-tinted to exhibit clear color.Applications:Components of electr.. |
|||
Flexural Strength | 94.0 MPa | 13600 psi | ASTM D790 |
Plenco 2482 Phenolic, Granular, Transfer Molded PLENCO 02482 is a general purpose, organic filled phenolic molding compound offering excellent mechanical strength while maintaining dielectric properties at elevated humidity levels. UL recognized .. |
|||
Flexural Strength | 94.0 MPa | 13600 psi | ASTM D790 |
Plenco 4414 Phenolic, Granular, Transfer Molded PLENCO 04414 is a flock and mineral filled phenolic molding compound. It is formulated for use in electrical applications that require improved heat resistance, mechanical strength, and dimensional .. |
|||
Flexural Strength | 94.0 MPa | 13600 psi | 2 mm/min; ISO 178 |
Covestro Makrolon® 1954 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Low viscosity• UV st.. |
|||
Flexural Strength | 93.8 MPa | 13600 psi | ASTM D790 |
Ensinger Tecapeek® XP-105 Compression Molded PEEK Compound, 15% Graphite Filled Ensinger Special Polymers offers over twenty different VICTREX® PEEK blends to choose from and has the capability to blend custom compounds for specific applications. Compression molding results in.. |
|||
Flexural Strength | 93.7 MPa @Thickness 6.35 mm |
13600 psi @Thickness 0.250 in |
tangent; chs 2.5 in/min; 100 mm SL; ASTM D790 |
Diamond Polymers ABSPC 7030-HES ABS/PC Injection Molding Grade, High Impact Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Flexural Strength | 94.0 - 101 MPa | 13600 - 14600 psi | ASTM D790 |
3D Systems Accura® 45HC Plastic for SLA® Systems A high speed material, with excellent thermal and moisture resistance for producing functional prototypes in 3D Systems' SLA 250 systems.ApplicationsHigh temperature testing:Automotive "under-the-ho.. |
|||
Flexural Strength | 93.8 MPa | 13600 psi | ASTM D790 |
Asahi Kasei Thermylene® P6-20FG-0753 20% Glass Fiber Reinforced, Heat Stabilized Information provided by Asahi Thermofil |
|||
Flexural Strength | 94.0 MPa | 13600 psi | ASTM D790 |
Plenco 4485 Phenolic, Granular, Transfer Molded PLENCO 04485 is a mineral filled phenolic molding compound offering excellent heat resistance, electrical resistance, and dimensional stability. UL recognized under component file E40654. 04485 is a.. |
|||
Flexural Strength | 94.0 MPa | 13600 psi | ASTM D790 |
Plenco 7697 Phenolic, Granular, Compression Molded PLENCO 07697 is a black, two stage, improved impact phenolic molding compound. It has been specifically formulated for automotive pulleys. PLENCO 07697 is the same formulation as VALITE 697-A.Inform.. |
|||
Flexural Strength | 94.0 MPa | 13600 psi | ISO 178 |
Polyplastics Duracon® GM-20 Acetal Co-polymer (POM), Low warpage, GF 20% reinforced DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O).. |