Polymer Property : Flexural Strength = 5950 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	<= 41.0 MPa	<= 5950 psi	ISO 178
Polykemi AB POLYfill PPC K2040 Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB
Flexural Strength	41.0 MPa	5950 psi	ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP CBL36XXC PS (Asia Pacific) LNP* Lubricomp* CBL36XXC is a compound based on Polystyrene resin containing Glass Bead, PTFE. Added features of this material include: Internally Lubricated.
Flexural Strength	41.0 MPa	5950 psi	0.1 in/min; 0.250" thickness; ASTM D-790B
Chevron Phillips MA5350 HIPS - High Impact Polystyrene (discontinued **) Rubber modified high impact polystyrene.Applications:Floppy diskettesDurable household applicationsThin to medium parts that require a combination of high gloss and good toughnessFeatures:Low coeffi..
Flexural Strength	41.0 MPa	5950 psi	0.1 in/min; 0.250" thickness; ASTM D-790B
Chevron Phillips MD6800 HIPS - High Impact Polystyrene (discontinued **) Rubber modified high impact polystyrene.Applications:Displays and retail product shelvingDurable household applicationsThin to medium thickness parts that require a combination of high flow and good..
Flexural Strength	41.0 MPa	5950 psi	ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP CBL36XXC PS LNP* LUBRICOMP* CBL36XXC is a compound based on Polystyrene resin containing 30% Glass Bead and 15% PTFE. Added features of this material include: Wear Resistant.
Flexural Strength	41.0 - 46.0 MPa	5950 - 6670 psi	ASTM D790M
DSM Somos® 9120 Epoxy Photopolymer (Unverified Data**) DescriptionDSM Somos® 9120 is a liquid photopolymer that produces robust, functional and accurate parts using stereolithography machines. The material offers superior chemical resistance, a wide p..
Flexural Strength	41.0 MPa	5950 psi	ASTM D790
Kolon KOCETALÂ® EL306 Toughened Grade Acetal Resin Flexible grade. Applications: Flexible products. Information provided by API-Kolon.
Flexural Strength	41.0 MPa	5950 psi	at 5% strain; ASTM D790
Ineos Nova FX530 Impact Polystyrene Features: Excellent environmental stress crack resistanceExcellent Izod impact strengthUL Classification 94 HBBalanced physical propertiesApplications: ExtrusionThermoformingSelected injection moldi..
Flexural Strength	41.0 MPa	5950 psi	ASTM D790
LG Chemical LUPOL HM-5204B High Modulus Polypropylene, 20% Polymer Alloy, High Strength, High Flow, High Modulus LUPOL resins, based on polyolefin with a wide range of characteristics, are a family of low cost engineering plastics.Applications: Automotive: Bumper cover, instrument panel, glove box, air cleaner..
Flexural Strength	41.0 MPa	5950 psi	ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP ML004S PP (Asia Pacific) LNP* Lubricomp* ML004S is a compound based on Polypropylene resin containing PTFE. Added features of this material include: Internally Lubricated, Heat Stabilized.
Flexural Strength	41.0 MPa	5950 psi	ASTM D790
SABIC Innovative Plastics LNP STAT-KON CD000I PS (Asia Pacific) LNP* Stat-kon* CD000I is a compound based on Polystyrene resin containing Carbon Powder. Added features of this material include: Electrically Conductive, High Impact.
Flexural Strength	41.0 MPa	5950 psi	ASTM D790
SABIC Innovative Plastics LNP STAT-LOY A30009 ABS LNP* STAT-LOY* A30009 is a compound based on ABS. Added features of this material include: Antistatic, Flame Retardant.
Flexural Strength	41.0 MPa	5950 psi	ASTM D790
SABIC Innovative Plastics LNP STAT-LOY A30009 ABS (Asia Pacific) LNP* Stat-loy* A30009 is a compound based on Acrylonitrile Butadiene Styrene resin containing Flame Retardant. Added features of this material include: Antistat, Flame Retardant.
Flexural Strength	41.0 MPa	5950 psi	ASTM D790
SABIC Innovative Plastics LNP STAT-LOY A3000T ABS (Asia Pacific) LNP* Stat-loy* A3000T is a compound based on Acrylonitrile Butadiene Styrene resin containing Anti-Static. Added features of this material include: Antistat.
Flexural Strength	41.0 MPa	5950 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP MB006HS PP (Asia Pacific) LNP* Thermocomp* MB006HS is a compound based on Polypropylene resin containing Glass Fiber. Added features of this material include: Heat Stabilized.
Flexural Strength	41.0 MPa	5950 psi	ASTM D790
StratasysÂ® ABS ABS is a strong, durable production-grade thermoplastic used across many industries. ABS is an ideal material for conceptual prototyping through design verification through direct digital manufactur..
Flexural Strength	41.0 MPa	5950 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP MB006HS PP LNP* THERMOCOMP* MB006HS is a compound based on Polypropylene resin containing 30% Glass Bead. Added features of this material include: Heat Stabilized, Healthcare.
Flexural Strength	41.0 MPa	5950 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP MFB71L PP LNP* THERMOCOMP* MFB71L is a compound based on Polypropylene resin containing 35% Glass Bead, 5% Glass Fiber. Added features of this material include: Low Extractible.
Flexural Strength	41.0 MPa	5950 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP MFB71L PP (Asia Pacific) LNP* Thermocomp* MFB71L is a compound based on Polypropylene resin. Added features of this material include: Low Extractible.
Flexural Strength	41.0 MPa	5950 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOTUF MF004AI PP LNP* Thermotuf* MF004AI is a compound based on Polypropylene resin containing Glass Fiber. Added features of this material include: High Impact.
Flexural Strength	41.0 MPa	5950 psi	ASTM D790
Lubrizol ESTALOC® 60204 Polyester-Type, Reinforced Engineering Thermoplastic Polyurethane Features: Fast Cycling, Dimensional Stability, Durability, Aesthetics, Low Temperature ImpactUses: Injection MoldingAvailability: Americas, Europe, Middle East, Africa, India and AsiaInformation pro..
Flexural Strength	41.0 - 55.0 MPa	5950 - 7980 psi	Polypropylene; ASTM D790M
DSM Somos® 9120 The need for movable parts is a constant when it comes to prototyping. Being able to ensure the proper fit for parts within a component can save both time and money. Somos® 9120 creates semi-transp..
Flexural Strength	41.0 MPa	5950 psi	ASTM D790
Entec Hypro™ PPH-CC30 Natural Homopolymer Polypropylene, 30% Calcium Carbonate Filled Information provided by Entec
Flexural Strength	41.0 MPa	5950 psi	ISO 178
Eurostar Starpylen HU 30E4 ECR PP, Mineral Filled, Injection Molding Starpylen HU 30E4 ECR is a reinforced Polypropylene with a low carbon footprint renewable mineral filler, Injection Molding Resin (also known as HUS30E4ECR)Information provided by Eurostar.
Flexural Strength	41.0 MPa	5950 psi	After conditioning at 23°C and 50% RH; ISO 178
Arkema Group Orgalloy® LE 60 SF Polyamide Alloy Polyamide Alloy, Film and PackagingInformation provided by Arkema Group
Flexural Strength	41.0 MPa	5950 psi	ASTM D790
Aclo Accutech Polypropylene Homopolymer HP0334M10CL Mica Reinforced Coupled
Flexural Strength	41.0 MPa	5950 psi	ASTM D790
Aclo Accutech Polypropylene Homopolymer HP0334M20L Mica Reinforced
Flexural Strength	41.0 MPa	5950 psi	ASTM D 790
SABIC Innovative Plastics LNP Lubricomp CI001 PS (Asia Pacific) LNP* Lubricomp* CI001 is a compound based on Polystyrene resin containing Silicone. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Asia Pa..