Polymer Property : Flexural Strength = 6380 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 44.0 MPa | 6380 psi | ASTM D790 |
| Proto3000 Duraform® AF Selective Laser Sintering (SLS®) Prototyping Polymer Description: Polyamide (nylon) material with metallic appearance for real-world physical testing and functional use.Features:Metallic appearance with nice surface finishGood powder recycle character.. |
|||
| Flexural Strength | <= 44.0 MPa | <= 6380 psi | ISO 178 |
| Polykemi AB POLYfill PPC K20040 Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Flexural Strength | 44.0 MPa | 6380 psi | ASTM D790 |
| SABIC Innovative Plastics LNP KONDUIT MT00E PP LNP KONDUIT* MT00E is a compound based on Polypropylene resin containing 70% Proprietary Thermal Filler. Added features of this material include: Thermally Conductive. |
|||
| Flexural Strength | 44.0 MPa | 6380 psi | ISO 178 |
| SABIC Innovative Plastics LNP KONDUIT MT00E PP LNP KONDUIT* MT00E is a compound based on Polypropylene resin containing 70% Proprietary Thermal Filler. Added features of this material include: Thermally Conductive. |
|||
| Flexural Strength | 44.0 MPa | 6380 psi | ASTM D790 |
| SABIC Innovative Plastics LNP KONDUIT MT00E PP (Asia Pacific) LNP KONDUIT* MT00E is a compound based on Polypropylene resin containing Proprietary Thermal Filler. Added features of this material include: Thermally Conductive. |
|||
| Flexural Strength | 44.0 MPa | 6380 psi | ASTM D790 |
| SABIC Innovative Plastics LNP KONDUIT MT00E PP (Europe-Africa-Middle East) LNP KONDUIT* MT00E is a compound based on Polypropylene resin containing Proprietary Thermal Filler. Added features of this material include: Thermally Conductive. |
|||
| Flexural Strength | 44.0 MPa | 6380 psi | |
| Plastcom SLOVALEN PC 93 T 15 1/M PP, 15% mineral filling, UV stability FeaturesModified PP for injection moulding with the content of 15 % mineral filling, uv stabilized. Increased rigidity, strength and thermal use up to 130°C depending on the talc content. Decreased.. |
|||
| Flexural Strength | 44.0 MPa | 6380 psi | ASTM D790 |
| SABIC PS 330 High Impact Polystyrene for Sheet Extrusion Product Description: High Impact Polystyrene PS 330 is manufactured by continuous mass polymerization of styrene monomer. An elastomer is incorporated during polymerization to achieve impact resis.. |
|||
| Flexural Strength | 44.0 MPa | 6380 psi | ASTM D790 |
| Ineos Nova Zyntar® F7080 Developmental Flame Retardant Polystyrene
(discontinued **) Features: General purpose non-Deca based resin (does not combine with Decabromodiphenyloxide)Good indoor UV light color stability(grey colors)UL94 V-0 @ 1.5 mm for all colors Good aesthetics for inj.. |
|||
| Flexural Strength | 44.0 MPa | 6380 psi | |
| Reliance Industries Polypropylene - Talc filled Information provided by Reliance Industries |
|||
| Flexural Strength | 44.0 MPa | 6380 psi | ASTM D790 |
| LG Chemical LUPOL HG-3250 High Gloss Polypropylene, 25% Mineral Fillers LUPOL resins, based on polyolefin with a wide range of characteristics, are a family of low cost engineering plastics.Applications: Automotive: Bumper cover, instrument panel, glove box, air cleaner.. |
|||
| Flexural Strength | 44.0 MPa | 6380 psi | ASTM D790 |
| Ineos Nova Styrosun® 3600 Weather Resistant High Impact Styrenic Polymer Features: Outdoor weatherablePhysical property retention after UV exposurePaintable and printableExcellent toughness Can be injection molded or co-extruded Easy to process, no drying required Appli.. |
|||
| Flexural Strength | 44.0 MPa | 6380 psi | ISO 178 |
| SABIC Innovative Plastics LNP Lubricomp ML002S PP LNP* Lubricomp* ML002S is a compound based on Polypropylene containing PTFE. Characteristics of this grade are: Heat Stabilized and Internally Lubricated.This data was supplied by SABIC-IP for the.. |
|||
| Flexural Strength | 44.0 MPa | 6380 psi | ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP ML004S PP LNP* LUBRICOMP* ML004S is a compound based on Polypropylene resin containing 20% PTFE. Added features of this material include: Wear Resistant, Heat Stabilized. |
|||
| Flexural Strength | 44.0 MPa | 6380 psi | ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP SP003 PA 12 (Asia Pacific) LNP* Lubricomp* SP003 is a compound based on Nylon 12 resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated. |
|||
| Flexural Strength | 44.0 MPa | 6380 psi | ISO 178 |
| SABIC Innovative Plastics LNP Stat-loy 9X05426C PMMA LNP* Stat-loy* 9X05426C is a compound based on PMMA resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for the Americas region. |
|||
| Flexural Strength | 44.0 MPa | 6380 psi | ISO 178 |
| SABIC Innovative Plastics LNP Stat-loy 9X05426C PMMA (Asia Pacific) LNP* Stat-loy* 9X05426C is a compound based on PMMA resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Flexural Strength | 44.0 MPa | 6380 psi | ISO 178 |
| SABIC Innovative Plastics LNP STAT-LOY AX11421 ABS LNP* STAT-LOY* AX11421 is a compound based on ABS resin. Added feature of this material is: Antistatic. |
|||
| Flexural Strength | 44.0 MPa | 6380 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP MB006S PP LNP THERMOCOMP* MB006S is a compound based on Polypropylene resin containing 30% Glass Bead. Added features of this material include: Heat Stabilized. |
|||
| Flexural Strength | 44.0 MPa | 6380 psi | ISO 178 |
| Styrolution PS 576H HIPS Styrolution PS 576H is a high gloss, high impact polystyrene with a good flow and good heat resistance.High gloss HIPSGood flow and heat resistanceHIPS with good balance of mechanical properties and.. |
|||
| Flexural Strength | 44.0 MPa | 6380 psi | ASTM D790 |
| Teknor Apex Sinpolene CPP1030 Polypropylene Availability: Africa & Middle East; Latin America; Asia Pacific; South America Calcium Carbonate Filler, 30% Filler by Weight Features: Homopolymer Uses: Appliance Components; Furniture; Housings F.. |
|||
| Flexural Strength | 44.0 MPa | 6380 psi | ASTM D790 |
| Videolar 825 High Impact Polystyrene (HIPS) Injection molding gradeMedium melt flow and high glossGood balance between rigidity and impactFeatures: Excellent mechanical strengthExcellent temperature resistancehigh impactApplications: Toys, ap.. |
|||
| Flexural Strength | 44.0 MPa | 6380 psi | ASTM D790 |
| Goodfellow TPX® RT31XB Injection Molding Grade Polymethylpentene This grade is highly recommended for injection molding; also for film and fiber extrusion.TPX® is semi-crystalline, transparent, very light and - for a polyolefin - expensive. It has good release c.. |
|||
| Flexural Strength | 44.0 MPa | 6380 psi | ASTM D790M |
| DSM Somos® 9110 Epoxy Photopolymer DescriptionDSM Somos® 9110 is a liquid photopolymer that produces robust, functional and accurate parts using stereolithography machines. The material offers superior chemical resistance, a wide p.. |
|||
| Flexural Strength | 44.0 - 46.0 MPa | 6380 - 6670 psi | UV Postcure; ASTM D790M |
| DSM Somos® 9120 The need for movable parts is a constant when it comes to prototyping. Being able to ensure the proper fit for parts within a component can save both time and money. Somos® 9120 creates semi-transp.. |
|||
| Flexural Strength | 44.0 MPa | 6380 psi | 50%RH; ISO 178 |
| DuPont Performance Polymers Zytel® 157HSL BK010 Nylon 612
(Unverified Data**) Unreinforced Heat Stabilized Polyamide 612 Information provided by DuPont Performance Polymers |
|||
| Flexural Strength | 44.0 MPa | 6380 psi | ASTM D790 |
| 3D Systems DuraForm® AF Nylon for SLS® Systems Polyamide (nylon) material with metallic appearance for real-world physical testing and functional use. For use with all selective laser sintering SLS® systems.ApplicationsHousings and enclosuresCo.. |
|||
| Flexural Strength | 44.0 MPa | 6380 psi | ASTM D790 |
| Aclo Accutech Polypropylene Homopolymer HP0336M30L Mica Reinforced |
|||
| Flexural Strength | 44.0 MPa | 6380 psi | ASTM D790 |
| Aclo Accutech Polypropylene Homopolymer HP0336M40L Mica Reinforced |
|||
| Flexural Strength | <= 44.0 MPa | <= 6380 psi | ISO 178 |
| Polykemi AB POLYfill PPHC TS15020 Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||