Polymer Property : Tensile Strength at Break = 20.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	20.0 MPa	2900 psi
Plastcom SLOVALEN EQ 71 N PP, imp. strength FeaturesPE modified with EVA. The addition of EVA causes increased toughness. General application in all industry branches. Delivered in natural mode and in the full RAL colour scale.Packaging, tran..
Tensile Strength at Break	20.0 MPa	2900 psi	2 in/min; ASTM D638
Polimeros Mexicanos Rotolene® Natural Linear Medium Density Polyethylene Hexene Copolymer Linear Medium Density Polyethylene for rotational molding. This resin is fully UV8 stabilized. Available as natural and several colors powder compounds.High quality Polyethylene re..
Tensile Strength at Break	<= 20.0 MPa	<= 2900 psi	ISO/R527
Polykemi AB POLYfill PP CQX10030 R3 Polypropylene, Mineral Reinforced, Scratch Resistant Information provided by Polykemi AB
Tensile Strength at Break	>= 20.0 MPa	>= 2900 psi	ASTM D638
NIZHNEKAMSKNEFTEKHIM 825EF High Impact Polystyrene Grade 825EF is a high impact polystyrene designed for extrusion and hot molding application. It is suited for hot molded deep drawn industrial packages and multilayer shaped sheet production via ex..
Tensile Strength at Break	20.0 MPa	2900 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP CL001I PS (Asia Pacific) LNP* Lubricomp* CL001I is a compound based on Polystyrene resin containing PTFE. Added features of this material include: Internally Lubricated, High Impact.
Tensile Strength at Break	20.0 - 40.0 MPa	2900 - 5800 psi	ASTM 1457-69 T
Fluorseals PTFE Unfilled Information provided by TEKU GmbH Fluorkunststoffe, a distributor of Fluorseals materials.
Tensile Strength at Break	20.0 MPa	2900 psi	GB/T1040.1
Lushan DE-1 Polyethylene Sintered Powder PE sintered powder Lushan DE-1 is combined with more than 10 years practice and experience on the area of oil & gas pipeline anti-corrosion. PE sintered powder Lushan DE-1 is used on anti-corrosion ..
Tensile Strength at Break	>= 20.0 MPa	>= 2900 psi	50mm/min; ASTM D638
Lushan EJ-1 Polyethylene compounds for steel pipe top coats Black high density polyethylene compounds Lushan EJ-1 for steel pipe top coats is used as anti-corrosion material for 2PE/3PE buried against-corrosion steel pipe coating system or coated steel plast..
Tensile Strength at Break	20.0 MPa	2900 psi
LATI Latiblend 5262 PP Homopolymer/PA6 Blend based on Polypropylene homopolymer (PPh) / Polyamide 6 (PA6). Unfilled. High impact resistance. Very good elongation.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; No..
Tensile Strength at Break	20.0 MPa	2900 psi	after 7days @113Â°C; UL 1581
SABIC Innovative Plastics NORYL WCD841U PPE-TPE (Europe-Africa-Middle East) Flexible, UV stabilized, halogen free extrusion grade for applications such as wire insulation and cable jacket. Good color stability after UV weathering per ASTM D4459. Light color capable. Flame r..
Tensile Strength at Break	20.0 MPa	2900 psi	ASTM D638
SABIC Innovative Plastics LNP STAT-KON CD000I PS (Asia Pacific) LNP* Stat-kon* CD000I is a compound based on Polystyrene resin containing Carbon Powder. Added features of this material include: Electrically Conductive, High Impact.
Tensile Strength at Break	20.0 MPa	2900 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON MX12407C PP LNP* STAT-KON* MX12407C is a compound based on Polypropylene resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Clean Compounding System.
Tensile Strength at Break	20.0 MPa	2900 psi	ISO 527-2
Total PSI 8350 High Impact Polystyrene 8350 is a very high impact polystyrene for extrusion. This grade has an improved environmental stress crack resistance in comparison with standard high impact grades. It is proposed for the produc..
Tensile Strength at Break	20.0 MPa	2900 psi	ASTM D638
Eastman Eastman AP005 Copolyester Applications:Automotive componentsBreathable filmsElectrical/electronic componentsFilm ModificationFlexible hingesHose mandrelIndustrial componentsIndustrial hoses/beltsOffice furniturePackagingPoly..
Tensile Strength at Break	20.0 MPa	2900 psi	ASTM D 638
Cossa Polimeri ESTAPROP 1540 TG V0 H Flame Retardant Polypropylene, 20% Mineral Filled PP with 20% mineral fillerFlame retardant class UL V0 and class M2 according to NL P92-507Information provided by Cossa Polimeri S.r.l.
Tensile Strength at Break	20.0 MPa	2900 psi	ISO 37
ELASTO UK Dryflex® 8004-101 Flame Retardant TPE for Injection Molding, Black, Halogen Free Dryflex® thermoplastic elastomers combine the performance of most vulcanized rubber with the process properties of thermoplastics. Dryflex® compounds permit sophisticated component design and thu..
Tensile Strength at Break	20.0 - 45.0 MPa	2900 - 6530 psi	ASTM D638
Daikin POLYFLON F-104 PTFE Fine Powder Processing Methods: Paste extrusion, calendering.Applications: Unsintered tape, sealing tape, low specific gravity tape, tape for wrapping flat cables, tubes.Information provided by Daikin Industrie..
Tensile Strength at Break	20.0 - 45.0 MPa	2900 - 6530 psi	ASTM D638
Daikin POLYFLON M-392 PTFE Molding Powder, Free Flow Free flow powder.Processing Methods: Compression molding, automatic or semi-automatic compression molding, isostatic molding, and ram extrusion.Features: Good fill characteristics particularly into ..
Tensile Strength at Break	20.0 - 45.0 MPa	2900 - 6530 psi	ASTM D638
Daikin POLYFLON MG-1431F PTFE 20% Glass Fiber and 5% MoS2 Filled Molding Powder, High Apparent Density, Free Flow 15% glass fiber and 5% MoS2 filled. High apparent density and free-flowing properties. High wear resistance, good electrical properties, low friction, high creep resistance.Applications: Mechanica..
Tensile Strength at Break	20.0 - 45.0 MPa	2900 - 6530 psi	ASTM D638
Daikin POLYFLON MG-2030 PTFE 15% Graphite Filled Molding Powder 15% graphite filled. Low friction, excellent chemical resistance, high creep resistance.Applications: Mechanical and chemical service (e.g. bearings, gaskets, packings)Information provided by Daiki..
Tensile Strength at Break	>= 20.0 MPa	>= 2900 psi	ISO R 527
Fainplast Compounds HL 94 Flexible PVC, Insulation for High Temperatures Operating temperature 90°C
Tensile Strength at Break	20.0 - 45.0 MPa	2900 - 6530 psi	ASTM D638
Daikin POLYFLON MG-1030F PTFE 15% Glass Fiber Filled Molding Powder, High Apparent Density, Free Flow 15% glass fiber filled. High apparent density and free-flowing properties. High wear resistance, low friction, good electrical properties.Applications: Mechanical and electrical service. Availabl..
Tensile Strength at Break	>= 20.0 MPa	>= 2900 psi	ISO R 527
Fainplast Compounds KLT 92/1 Flexible PVC, Insulation Transparent Cables Lead Free Transparent cables (90°C)
Tensile Strength at Break	20.0 MPa	2900 psi	ISO R 527
Addiplast Addilene PMD 50213 Polypropylene Copolymer Mineral reinforced, improved scratch resistanceInformation provided by Addiplast.
Tensile Strength at Break	20.0 MPa @Temperature 120 °C	2900 psi @Temperature 248 °F	ISO Data
BASF Ultramid® 8202C PA6 (Conditioned) Ultramid 8202C is a modified crystalline and low viscosity, nylon 6 injection molding homopolymer. It is also available in heat stabilized (Ultamid 8202C HS) and/or pigmented versions. Its unique ..
Tensile Strength at Break	20.0 MPa	2900 psi	film; ASTM D638
3M Dyneon™ THV 221GZ Fluoroplastic Granules 3M™ Dyneon™ Fluoroplastic Granules THV 221GZ is a flexible, transparent fluoroplastic composed of tetrafluoroethylene, hexafluoropropylene, and vinylidene fluoride in the form of pellets. It provi..
Tensile Strength at Break	<= 20.0 MPa	<= 2900 psi	ISO/R527
Polykemi AB POLYfill PPHC K8040G E10 Polypropylene, Mineral Reinforced Information provided by Polykemi AB
Tensile Strength at Break	20.0 MPa	2900 psi	ISO 527-2/50
ExxonMobil Exxtral™ CMW 402 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin designed for automotive under-the-hood applications. Availability: Africa & Middle East, Asia Pacific, Europe, South America and North..
Tensile Strength at Break	>= 20.0 MPa	>= 2900 psi
Shandong Dongyue Shenzhou New Material Co DS608 Fluorinated Ethylene-Propylene Copolymer For High-Speed Extrusion Conformable with: Q/DYS 003-2007Fluorinated Ethylene Propylene is the copolymer of TFE and HFP, with good thermal stability, outstanding chemical inertness, good electrical insulation, and low coeff..