SABIC Innovative Plastics NORYL WCD841U PPE-TPE (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL WCD841U PPE-TPE (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flexible, UV stabilized, halogen free extrusion grade for applications such as wire insulation and cable jacket. Good color stability after UV weathering per ASTM D4459. Light color capable. Flame retardant performance capable of meeting UL VW-1 requirement. 80C application temperature rating as defined by UL 1581. 84 Shore A hardness. Processing typically conducted on standard extrusion equipment. UL 1581 tests conducted on 2.0 mm wire with 0.12 mm x 20 stranded copper conductor.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Melt Flow | 23 g/10 min @Load 5.00 kg, Temperature 250 °C |
23 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 84 | 84 | 30S reading; ASTM D2240 |
| Tensile Strength at Break | 17.0 MPa | 2470 psi | 50 mm/min; ISO 527 |
| 18.0 MPa | 2610 psi | UL 1581 | |
| 18.0 MPa | 2610 psi | Type I, 50 mm/min; ASTM D638 | |
| 20.0 MPa | 2900 psi | after 7days @113°C; UL 1581 | |
| Elongation at Break | 220 % | 220 % | 50 mm/min; ISO 527 |
| 238 % | 238 % | after 7days @113°C; UL 1581 | |
| 250 % | 250 % | Type I, 50 mm/min; ASTM D638 | |
| 295 % | 295 % | UL 1581 | |
| Flexural Modulus | 0.0900 GPa | 13.1 ksi | 12.5 mm/min, 100 mm span; ASTM D790 |
| 0.0900 GPa | 13.1 ksi | 12.5 mm/min; ISO 178 | |
| Heat Distortion | 19 % @Load 0.250 kg, Temperature 100 °C |
19 % @Load 0.551 lb, Temperature 212 °F |
UL 1581 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | UL temperature rating; UL 1581 |
| Brittleness Temperature | <= -40.0 °C | <= -40.0 °F | ASTM D746 |
| Oxygen Index | 25 % | 25 % | ISO 4589 |
| Glow Wire Test | 750 °C | 1380 °F | IEC 60695-2-13 |
| 960 °C @Thickness 3.00 mm |
1760 °F @Thickness 0.118 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.20e+15 ohm-cm | 4.20e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.6 @Frequency 1.00e+6 Hz |
2.6 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 21.5 kV/mm @Thickness 2.00 mm |
546 kV/in @Thickness 0.0787 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.0060 @Frequency 1.00e+6 Hz |
0.0060 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Smoke Density on 0.5mm plaque, Flame, Ds, max | 133 | ASTM E 662 |
| Smoke Density on 0.5mm plaque, Non-flame, Ds, max | 170 | ASTM E 662 |
| VW-1 | Pass | UL 1581 |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 20-7796 Polyphthalamide, with aramid reinforcement and PTFE
- Kennametal Stellite Deloro® 208 PM after P/M Processing
- SABIC Innovative Plastics NORYL PX9406 PPE+PS
- SolVin 257RF Polyvinyl Chloride General Purpose - Rigid
- DuPont 20 Series 2010 Specialty Polyethylene Resin
- A. Schulman PP 828-31 Polypropylene Black Molding Grade Impact Polypropylene
- ChevronTexaco Regal® 100 R&O
- 3M 4125 Polyethylene Protective Tapes
- Arkema Group KYNAR® 1000 HD Polyvinylidene Fluoride Homopolymer - Injection Molding and Extrusion
Copyright © lookpolymers.com All Rights Reserved