Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D412 |
Multibase TPSiV™ 3011-50A Thermoplastic Silicone Vulcanizate These materials are a novel family of TPV products based on cross-linked silicone rubber dispersed into various engineering thermoplastics. The dispersion of the silicone internal phase is produced.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ISO 527 |
Polimeri Europa Riblene® GP 26 Low Density Polyethylene - Coating Grade Riblene GP 26 is a high fluidity low density polyethylene resin (LDPE).Main Applications: Riblene GP 26 is suitable for coating applications where low neck-in and high draw-down are key factors. F.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D 638 |
NOVA Chemicals Novapol® LF-0718-A-INJECTION LDPE Injection Molding Resin LF-0718-A complies with the U.S. FDA specifications for olefin polymers and may be used in the U.S. as an article or component of an article intended for use in contact with food. LF-0718-A is subj.. |
|||
Tensile Strength at Break | 11.0 MPa @Temperature 23.0 °C |
1600 psi @Temperature 73.4 °F |
Die C2 hr; ASTM D412 |
PolyOne Dynaflex™ G7690-9 (Black) Thermoplastic Elastomer (TPE) Dynaflex™ G7690-9 (Black) is an easy processing, general purpose TPE designed for a wide variety of applications, including those where FDA compliance is required. - Overmold Adhesion to Polypropyl.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible D75M0 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | TM R050-36 |
Resinlab® EP1112NC Black Electronic Grade Epoxy Encapsulant Resinlab™ EP1112NC Black is a two part unfilled fast curing electronic grade epoxy encapsulant designed for small to medium sized castings. EP1112NC Black is a modified version of the standard EP11.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | TM R050-36 |
Resinlab® EP1340 Medium Viscosity, Flame Retardant Epoxy Casting Resin System Resinlab™ EP1340 is a medium viscosity, flame retardant epoxy casting resin system. It is recognized under the Component Recognition Program of Underwriters Laboratories Inc., (File# E186034) for U.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D638 |
Westlake EMAC® SP2242 Specialty Copolymer
(discontinued **) EMAC resins adhere to and are compatible with a wide range of materials including paper, polyolefins, oriented polyolefins, polyesters, ionomers, PVdC, unplasticized PVC and other polar polymers. Fo.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D638 |
LyondellBasell Microthene® G MN71020 Low Density Polyethylene General DescriptionMicrothene G polyolefin powders are ground, irregularly-shaped particles designed for use in a broad range of specialty applications. Microthene G powders combine the unique prop.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D638 |
LyondellBasell Microthene® G MN71120 Low Density Polyethylene (Rotomolding) General DescriptionMicrothene G polyolefin powders are ground, irregularly-shaped particles designed for use in a broad range of specialty applications. Microthene G powders combine the unique prop.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D1414 |
Greene Tweed CHEMRAZ® 517 Perfluoroelastomer Greene Tweed’s Chemraz® 517, a perfluoroelastomer, is a white specialty compound, perfect for applications where contamination from carbon black must be prevented. Chemraz 517 has a Shore A.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | 50 mm/min, 1A; ISO 527 |
SABIC Innovative Plastics SABIC PPCOMPOUND 8620 PP SABIC® PPcompound 8620 is a mineral filled, impact modified polypropylene TPO. This material combines scratch resistance and good flow with exterior automotive weathering stability. It was origin.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | |
Shin-Etsu Silicones FE-401U Fluorosilicone Elastomer ShinEtsu FE401 U is a fluorosilicone/silicone blend. It is designed to process well in molding applications.Product Features: Good fuel and oil resistance.Information Provided by Shin-Etsu Silicones.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | |
Master Bond UV15X-6MED-2 UV Curable Compound for Medical Applications Description: Master Bond Polymer System UV15X-6MED-2 is a newly developed one component clear, non-yellowing, UV curable urethane elastomer system possessing high flexibility and outstanding abrasio.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D638 |
ELASTO UK Dryflex® 502800S SEBS Based Material, Unfilled Qualities, 80A Hardness, Black The 500-seriesis very favorable when transparency and good scratch resistance are required, as well as when there are high surface finish requirements. Unfilled grades have excellent flow and mecha.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | Tensile stress at break. |
Dow AFFINITY™ EG 8150 Polyolefin Elastomer AFFINITY® EG 8150 polyolefin elastomer is a saturated ethylene-octene copolymer for general purpose elastomeric applications that is efficiently crosslinked by peroxide, silane or irradiation It ex.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ISO R 527 |
Fainplast Compounds GS 64/BT Flexible PVC, Injection Molding for Footwear Soles for cold climates |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | IEC 60811 |
Fainplast Compounds HAX HF 019/G Halogen Free PVC Sheathing; high flexibility |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | IEC 60811 |
Fainplast Compounds HAX HF 3622 Halogen Free PVC General purpose |
|||
Tensile Strength at Break | >= 11.0 MPa | >= 1600 psi | ISO R 527 |
Fainplast Compounds HG 83 Flexible PVC, Sheathing for High Temperatures Operating temperature 90°C |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ISO R 527 |
Fainplast Compounds GSK 78 Flexible PVC, Injection Molding, Lead Free Plugs |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ISO R 527 |
Fainplast Compounds PH 55 Flexible PVC, Transparent Extrusion Transparent profiles |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ISO R 527 |
Fainplast Compounds PM 55 Flexible PVC, Lead Free Gaskets for frames |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D638 |
Azdel SuperLite® SL551600-100 PP Resin Matrix / 55% Glass Fiber (7 mm Molded Thickness) AZDEL SuperLite® SL551600-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | 500mm/min; ASTM D638 Type IV Specimen |
Westlake EMAC® Plus SP1330 22% Ethylene-Methyl Acrylate Copolymer Westlake EMAC® Plus SP1330 is a 22% EMA copolymer designed for blown or cast film, tie-layers, and extrusions where flexibility, compatibility, or low heat seal temperatures are required. SP1330 is.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ISO 527 |
Polyplastic Armlen® PE MF 70-2FR Magnesium Hydroxide Filled Polyethylene 70% Magnesium HydroxideFor extrusion of fire resistant aluminum composite panels.Information provided by PolyPlastic Group. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | 25mm/min; ISO 527 |
Borealis LE7704 Polyethylene Compound, Semiconductive, Thermoplastic LE7704 is a thermoplastic black polyethylene compound, specially designed for semiconductive screen applications. Applications: LE7704 is intended for semiconductive applications in medium voltage.. |