Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 11.0 MPa | 1600 psi | TM R050-36 |
Resinlab® EP1112NC Clear Electronic Grade Epoxy Encapsulant Resinlab™ EP1112NC Clear is a two part unfilled fast curing electronic grade epoxy encapsulant designed for small to medium sized castings. EP1112NC Clear is a modified version of the standard EP11.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | TM R050-36 |
Resinlab® EP1290 Clear Mineral Filled Epoxy Adhesive Resinlab™ EP1290 Clear is a two part mineral filled epoxy adhesive designed for bonding metals and plastics. It cures at room temperature to a tough, semi-flexible material. It has good wetting to .. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ISO 527 |
Polimeri Europa Riblene® GP 20 Low Density Polyethylene - Coating Grade Riblene GP 20 is a high fluidity low density polyethylene resin (LDPE).Main Applications: Riblene GP 20 is suitable for coating applications where low neck-in and high draw-down are key factors. F.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne FireCon™ CPE 30-33 RoHS BLACK Polyethylene, Chlorinated (CPE) An excellent choice for low-voltage power-and-cable control cables, this RoHS compliant, flexible, black colored thermoplastic CPE jacketing compound offers wire and cable manufacturers the advantag.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | TM R050-36 |
Resinlab® EP1340 Medium Viscosity, Flame Retardant Epoxy Casting Resin System Resinlab™ EP1340 is a medium viscosity, flame retardant epoxy casting resin system. It is recognized under the Component Recognition Program of Underwriters Laboratories Inc., (File# E186034) for U.. |
|||
Tensile Strength at Break | 11.0 MPa @Temperature 23.0 °C |
1600 psi @Temperature 73.4 °F |
Die C2 hr; ASTM D412 |
PolyOne Dynaflex™ G7690-1 (Natural) Thermoplastic Elastomer (TPE) Dynaflex™ G7690-1 (Natural) is an easy processing, general purpose TPE designed for a wide variety of applications, including those where FDA compliance is required. - Overmold Adhesion to Polyprop.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D638 |
LyondellBasell Microthene® G MN71120 Low Density Polyethylene (Rotomolding) General DescriptionMicrothene G polyolefin powders are ground, irregularly-shaped particles designed for use in a broad range of specialty applications. Microthene G powders combine the unique prop.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D1414 |
Greene Tweed CHEMRAZ® 537 Perfluoroelastomer Chemraz®, a proprietary Greene, Tweed compound, has the broadest chemical resistance of any elastomeric material. Chemraz combines the resilience and sealing force of an elastomer with chemical r.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ISO 527-1, -2 |
LyondellBasell Hifaxâ„¢ CA244 Thermoplastic Polyolefin Elastomer Description: Hifaxâ„¢ CA244 high melt flow, 850 MPa flexural modulus, paintable thermoplastic elastomeric olefin (TEO) resin has an excellent combination of stiffness, processability and dynamic.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | 50 mm/min, 1A; ISO 527 |
SABIC Innovative Plastics SABIC PPCOMPOUND 8620 PP SABIC® PPcompound 8620 is a mineral filled, impact modified polypropylene TPO. This material combines scratch resistance and good flow with exterior automotive weathering stability. It was origin.. |
|||
Tensile Strength at Break | >= 11.0 MPa | >= 1600 psi | |
Shandong Dongyue Shenzhou New Material Co DS2602 Fluoroelastomer Copolymer Gum Conformable with: Q/DYS 005-2007Brief Introduction:FKM-DS2600 is copolymer of HFP and VDF. Normally it is white or light yellow translucent elastomer whose fluorine content is over 66%. After vulc.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D412 |
Teknor Apex Monprene® MP-1698 Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D412 |
Teknor Apex Telcar® TL-87-L832-B Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets P.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D412 |
Borealis LE0151 Easy Strippable Semiconductive Insulation Shield for Medium Voltage Power Cables LE0515 is an easy strippable crosslinkable semi conductive insulation shield compound designed for medium voltage (5kV-46kV) power cable applications. Application: LE0515 is especially suitable for.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D638 |
ELASTO UK Dryflex® 500800S SEBS Based Material, Unfilled Qualities, 80A Hardness, Translucent The 500-seriesis very favorable when transparency and good scratch resistance are required, as well as when there are high surface finish requirements. Unfilled grades have excellent flow and mecha.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D882 |
Diamond Polymers NPP10-2523 Low Density Polyethylene Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | Tensile stress at break. |
Dow AFFINITY™ EG 8150 Polyolefin Elastomer AFFINITY® EG 8150 polyolefin elastomer is a saturated ethylene-octene copolymer for general purpose elastomeric applications that is efficiently crosslinked by peroxide, silane or irradiation It ex.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | IEC 60811 |
Fainplast Compounds HAX HF 039/4H Halogen Free PVC Sheathing, insulation; high flexibility |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | IEC 60811 |
Fainplast Compounds HAX HF 4022 Halogen Free PVC General purpose |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ISO R 527 |
Fainplast Compounds PM 55 Flexible PVC, Lead Free Gaskets for frames |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ISO R 527 |
Fainplast Compounds PM 5510 Flexible PVC, Lead Free Gaskets for frames |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D638 |
Aclo Accutech Polypropylene Copolymer CP0437C40L Calcium Reinforced |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D638 |
Azdel SuperLite® SL550600-100 PP Resin Matrix / 55% Glass Fiber (3 mm Molded Thickness) AZDEL SuperLite® SL550600-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM-D638 |
Braskem IG58 HDPE Injection Molding Polyethylene Copolymer IG58 is a high-density polyethylene, narrow molecular weight butene-1 copolymer produced by the solution process for injection molding applications. It offers high stiffness, impact strength and out.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | Across Flow; ASTM D412 |
ExxonMobil Santoprene® 121-80M300 Thermoplastic Elastomer
(discontinued **) A soft, black, UV resistant thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material is designed for automotive interior applications requiring low fogging and good.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | 25mm/min; ISO 527 |
Borealis LE7710 Polyethylene Compound, Semiconductive, Thermoplastic LE7710 is a thermoplastic black polyethylene compound, specially designed for semiconductive screen applications. Applications: LE7710 is intended for semiconductive applications in medium voltage .. |