- Polymer Property : Tensile Strength at Break = 1740 psi
Polymer Property : Tensile Strength at Break = 1740 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ASTM D412 |
| Polimeri Europa Europrene® SOL T 190 Styrene - Isoprene Block Copolymer Europrene® SOL T 190 is a linear block copolymer obtained by anionic polymerization. The polymer is based on styrene and isoprene, where bound styrene content is 16% weight and diblock content is .. |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ISO 527 |
| Polimeri Europa Riblene® GM 20 R Low Density Polyethylene - Coating Grade Riblene GM 20 R is a medium fluidity low density polyethylene resin (LDPE).Main Applications: Riblene GM 20 R is suitable for coating applications where a low neck-in is required. Moreover, for it.. |
|||
| Tensile Strength at Break | <= 12.0 MPa | <= 1740 psi | ISO/R527 |
| Polykemi AB POLYelast TPE S902A Thermoplastic Elastomer, SBS-based Information provided by Polykemi AB |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ISO 527 |
| Polimeri Europa Flexirene® MS 40 A Linear Low Density Polyethylene Flexirene MS 40 A is a linear low density polyethylene (LLDPE), with antioxidants, suitable for injection molding application.Parts made with Flexirene MS 40 A are characterized by a good balance be.. |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ASTM D638 |
| SABIC M200056 High Density Polyethylene for Injection Molding Product Description: M200056 is a high density polyethylene grade with a narrow molecular weight distribution suitable for injection molding applications. It has been designed to provide good flow.. |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | 500mm/min; ASTM D638 Type IV Specimen |
| Westlake EMAC® SP2405 20% Ethylene-Methyl Acrylate Copolymer
(discontinued **) Westlake EMAC® SP2405 is a 20% EMA copolymer designed for blown or cast film, tie-layers, and extrusions where flexibility, compatibility, or low heat seal temperature are required. SP2405 provides.. |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | 500 mm/min; ASTM D638 |
| Eastman 1840A Polyethylene
(discontinued **) Polyethylene 1840A is a low-density formulation with no slip or antiblock. It is suggested for injection molding applications requiring good stiffness, gloss, good processability or layflat properti.. |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ASTM D638 |
| Petroquimica Triunfo Trithene® TS 7045 LDPE - Film - Plastification The Trithene TS 7045 resin is a low-density polyethylene (LDPE) with an excellent processability, which allows for a low energy consumption during extrusion and warrants the production of thin films.. |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL WCD801A PPE-TPE Flexible, migration-improved, halogen free extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Flame performance capable of meeting UL VW1 requirements.. |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL WCD883 PPE-TPE Flexible and non-halogenated flame retardant extrusion grade intended for evaluation in applications such as jacket of HD 21.14 flexible cables. Flame retardant performance capable of meeting EN 502.. |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ASTM D638 |
| Solvay Specialty Polymers Cogegum® GFR/340-HP Polyolefin Cogegum® XLPO-HFFR - Crosslinkable Halogen Free Fire Retardant compound. Silane grafted compound moisture curable by addition of a catalyst masterbatch (Sioplas® method). It consists of a poly.. |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ASTM D412 |
| Sumitomo Chemical ESPOLEX® WT318 Thermoplastic Elastomer ESPOLEX® TPE Series is a group of thermoplastic elastomers produced by Sumitomo Chemical Company. Among its material advantages, ESPOLEX® TPE Series is distinguished by offering many low-densi.. |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ASTM D638 |
| UBE J1019 Polyethylene Description: UBE Polyethylene is polymerized at high pressure using a tubular reactor. Production conditions are strictly controlled ensuring the product's superior physical and mechanical prope.. |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | 25mm/min; ISO 527 |
| Borealis LE0574 Polyethylene LE0574 is a thermoplastic black polyethylene compound, specially designed for strippable semi conductive screen applications. It can be used in thermoplastic form or crosslinked via a grafting proce.. |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ASTM D638 |
| ELASTO UK Mediprene™ 500600M TPE, Medical Applications, 60A Hardness All Mediprene™ compounds are designed and manufactured for use in medical and pharmaceutical applications. In both medical and food contact areas, high application demands are found, such as:Low e.. |
|||
| Tensile Strength at Break | >= 12.0 MPa | >= 1740 psi | ISO R 527 |
| Fainplast Compounds AP 80 Flexible PVC, Flame Retardant Insulation General purposes |
|||
| Tensile Strength at Break | >= 12.0 MPa | >= 1740 psi | ISO R 527 |
| Fainplast Compounds AP 86 Flexible PVC, Flame Retardant Insulation General purposes |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ISO R 527 |
| Fainplast Compounds GS 7004 Flexible PVC, Injection Molding for Footwear Sandals for armed force, antifungus |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ISO R 527 |
| Fainplast Compounds GSK 78/3 Flexible PVC, Injection Molding, Lead Free Plugs DOP free |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ISO R 527 |
| Fainplast Compounds GS 8202 Flexible PVC, Injection Molding for Footwear Soles |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ISO R 527 |
| Fainplast Compounds MPH 64 Medical Flexible PVC, Extrusion Tubolar apparatus |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ISO R 527 |
| Fainplast Compounds PG 60/FR Flexible PVC, Extrusion Modified with Rubber Profiels UL 94 Classe V1 |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ISO R 527 |
| Fainplast Compounds PK 71/FR Flexible PVC, Lead Free Spiral pipes |
|||
| Tensile Strength at Break | >= 12.0 MPa | >= 1740 psi | ASTM D4894 |
| Adamas Adalon® 252 PTFE, 28% Glass Fiber Information provided by Adamas, HPM |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ISO R 527 |
| Fainplast Compounds PM 67/FR Flexible PVC, Lead Free Spiral pipes, UL 94 Class V0 |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ASTM D638 |
| Azdel SuperLite® SL551400-100 PP Resin Matrix / 55% Glass Fiber (6 mm Molded Thickness) AZDEL SuperLite® SL551400-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP FP003 PE (Europe-Africa-Middle East) LNP *Lubricomp* FP003 is a compound based on Polyethylene resin, containing PTFE and Silicone. Added features include: Internally Lubricated. |
|||