Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | <= 21.0 MPa | <= 3050 psi | ISO/R527 |
Polykemi AB POLYfill PP CIP6020F Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | <= 21.0 MPa | <= 3050 psi | ISO/R527 |
Polykemi AB POLYfill PP EQX10030R UV Polypropylene, Mineral Reinforced, Modified Information provided by Polykemi AB |
|||
Tensile Strength at Break | <= 21.0 MPa | <= 3050 psi | ISO/R527 |
Polykemi AB POLYfill PPC T4020 E20 Polypropylene Copolymer, Mineral Reinforced, Modified Information provided by Polykemi AB |
|||
Tensile Strength at Break | >= 21.0 MPa | >= 3050 psi | ASTM D638 |
NIZHNEKAMSKNEFTEKHIM 825ES High Impact Polystyrene Grade 825ES is a high impact polystyrene designed for extrusion and hot molding application. It is suited for hot molded deep drawn industrial packages and multilayer shaped sheet production via ex.. |
|||
Tensile Strength at Break | <= 21.0 MPa | <= 3050 psi | ISO/R527 |
Polykemi AB POLYfill PPC 20000 Polypropylene Copolymer Information provided by Polykemi AB |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | 50mm/min; ASTM D638 |
Kingfa FRHIPS-960PC Flame Retardant Polystyrene Features:UL 94 V-0 @ 3.2mmNon-DPO, UV stabilityExcellent heat stabilityExcellent electrical propertiesApplications:Injection moldingGas moldingTV and audio housingElectrical appliance housingInforma.. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | after 7days @113°C; UL 1581 |
SABIC Innovative Plastics NORYL WCD771 PPE-TPE (Asia Pacific) Flexible, high tensile elongation, halogen-free extrusion grade intended for evaluation in applications such as cable jacket. Flame retardant performance capable of meeting UL VW-1 requirement. 80C .. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | after 7days @113°C; UL 1581 |
SABIC Innovative Plastics NORYL WCD891B PPE-TPE (Asia Pacific) Non-halogenated flame retardant, flexible Noryl resin intended for evaluation in wire and cable applications. Strong flame retardant performance capable of meeting VW-1 and 80°C end use tempera.. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP MX91206 PP LNP* Lubricomp* MX91206 is a compound based on Polypropylene containing proprietary fillers. Added feature of this grade is: Wear Resistant. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-LOY AX11421 ABS LNP* STAT-LOY* AX11421 is a compound based on ABS resin. Added feature of this material is: Antistatic. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-LOY AX11421 ABS LNP* STAT-LOY* AX11421 is a compound based on ABS resin. Added feature of this material is: Antistatic. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D638 |
Sterigenics Raprex® R-200 Branched High Density Polyethylene Applications: Injection Molding and ExtrusionRAPREX® R-200 is a high density polyethylene based resin that exhibits an excellent balance of melt processability and physical properties due to its .. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D638 |
Sterigenics Raprex® R200D Branched High Density Polyethylene Applications: Injection Molding and ExtrusionRAPREX® R200D is a high density polyethylene based resin that exhibits an excellent balance of melt processability and physical properties due to its .. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D638 |
Teknor Apex APEX® 84859 Polyvinyl Chloride, Flexible Notes: 75°C Jacket; RoHS Compliant Features: Flame Retardant; Sunlight Resistant (720 hours) Uses: Cable Jacketing Forms: Pellets Agency Ratings: UL QMTT2 .E73402; UL 62 Wire Types: SJTW; STWInfo.. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp TH0450D LNP* Thermocomp* TH0450D is a compound based on Polyurethane resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity.This data was supplied by .. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp TH0450D PUR (Asia Pacific) LNP* Thermocomp* TH0450D is a compound based on Polyurethane resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity.This data was supplied by .. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Noryl HIPS3191 PS This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | after 7days @113°C; UL 1581 |
SABIC Innovative Plastics NORYL WCD851 PPE-TPE (Asia Pacific) Flexible, strong flame-retardant, halogen-free extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Flame retardant performance capable of meeting UL VW-.. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp 2Z004 FP-E (EFTE) LNP* 2Z004 is a compound based on Ethylenetetrafluoroethylene (ETFE) containing Milled Glass.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D638 |
UBE R300 Polyethylene Description: UBE Polyethylene is polymerized at high pressure using a tubular reactor. Production conditions are strictly controlled ensuring the product's superior physical and mechanical prope.. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ISO 527-2 |
Total PSI 7240 High Impact Polystyrene 7240 is a very high impact polystyrene for the extrusion industry. This grade has been designed to be diluted with crystal polystyrene (such as LACQRENE® 140, 1340 or 1540) at higher levels than c.. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D638 |
Chesterton ARC CS4 low-viscosity, 100% solids, barrier coating Description: An advanced composite formulated to protect concrete surfaces from harsh chemical attack. It is normally applied at a thickness of 250-375 microns (10-15 mils) per coat in a 2 coat syst.. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D 638 |
Cossa Polimeri ESTAPROP H 10100 BS Polypropylene, 50% Mineral Filled PP homopolymer 50% mineral fillerExcellent surface appearance, high densityInformation provided by Cossa Polimeri S.r.l. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D 638 |
Cossa Polimeri ESTAPROP HK 1280 T8 Polypropylene, 40% Mineral Filled PP homopolymer 40% mineral fillerExcellent physical and mechanical characteristics, good surface appearanceInformation provided by Cossa Polimeri S.r.l. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D638 |
Equate EMDA-8920 HDPE Injection Molding Resin EMDA-8920 is a high density copolymer polyethylene resin designed for injection molding applications which require excellent toughness and gloss.Applications: EMDA-8920 is a high density copolymer p.. |
|||
Tensile Strength at Break | >= 21.0 MPa | >= 3050 psi | ISO R 527 |
Fainplast Compounds HLA 075 Flexible PVC, Insulation for High Temperatures Operating temperature 105°C |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ISO R 527 |
Fainplast Compounds PK 96 Flexible PVC, Lead Free Semi-rigid extrusion |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | Conditioned; ISO R 527 |
Addiplast Addilene J 490 M20F Flame Retardant Polypropylene, 20% Mineral Filled Flame retardant, mineral filled, with halogensInformation provided by Addiplast. |
|||
Tensile Strength at Break | >= 21.0 MPa @Temperature 23.0 °C |
>= 3050 psi @Temperature 73.4 °F |
ASTM D1708 |
Solvay Specialty Polymers Hyflon® PFA P450 Perfluoroalkoxy (PFA)
(Unverified Data**) Hyflon PFA is a unique family of semi-crystalline, melt processable perfluoropolymers which combine excellent mechanical characteristics to unique properties such as chemical inertness, heat resista.. |