- Polymer Property : Tensile Strength at Break = 47.0 MPa
Polymer Property : Tensile Strength at Break = 47.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Cycoloy® C1204HF PC+ABS (Europe-Africa-Middle East) High heat PC/ABS blend offering good flow and excellent impact. Food compliant according to FDA and European directive 2002/72/EC. Available in limited colors. Effective January 15th, 2008 this gra.. |
|||
| Tensile Strength at Break | 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Cycoloy® CY5100 PC+ABS (Europe-Africa-Middle East) Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering excellent flow / impact balance for large size applicationsThis data was supplied by SABIC-IP .. |
|||
| Tensile Strength at Break | 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Cycoloy® RCY6113 PC+ABS (Asia Pacific) Cycoloy* RCY6113 resin is an injection moldable PC/ABS blend with non-brominated and non-chlorinated flame retardant. It contains 30% post consumer recycle content with a UL-94 5VB rating @ 2.0mm an.. |
|||
| Tensile Strength at Break | 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Geloy XTPMFR15 ASA+PC (Europe-Africa-Middle East) Geloy XTPMFR15 is a chlorine and bromine free flame retardant ASA/PC blend with improved impact performance/ductility and an UL94 rating of V0 at 1.5mm. This grade has a f1 rating according UL746C.T.. |
|||
| Tensile Strength at Break | 47.0 MPa | 6820 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® EXL4016 PC Copolymer 6% GF reinforced opaque polycarbonate-siloxane copolymer, for increased stiffness with good impact strength. Improved release properties. Available in limited colors only.This data was supplied by S.. |
|||
| Tensile Strength at Break | 47.0 MPa | 6820 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® EXL4016 PC Copolymer (Asia Pacific) 6% GF reinforced opaque polycarbonate-siloxane copolymer, for increased stiffness with good impact strength. Improved release properties. Available in limited colors only.This data was supplied by S.. |
|||
| Tensile Strength at Break | 47.0 MPa | 6820 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® FXE1414L PC Copolymer Opaque EXL, UV-Stabilized & light shielding capability (Wall thickness >0.8mm), for portable electronics device enclosure application. Only available in white, grey and limited pastel colors. Consul.. |
|||
| Tensile Strength at Break | 47.0 MPa | 6820 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® FXM1414T PC Copolymer (Europe-Africa-Middle East) PC-siloxane copolymer in special metallic colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may affect performance.This data was supplied by .. |
|||
| Tensile Strength at Break | 47.0 MPa | 6820 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Cycoloy® CP8930 PC+ABS (Asia Pacific) High heat, PC/ABS for automotive electro plating applications, excellent balance in flow/impact |
|||
| Tensile Strength at Break | 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Cycoloy® CP8930 PC+ABS (Asia Pacific) High heat, PC/ABS for automotive electro plating applications, excellent balance in flow/impact |
|||
| Tensile Strength at Break | 47.0 MPa | 6820 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics GELOY XTPMFR10 ASA+PC (Asia Pacific) Improved ASA/PC blend for high flow, 1.0mm V0 applications. Improved UV performance aesthetically and physically compared to alternatives. |
|||
| Tensile Strength at Break | 47.0 MPa | 6820 psi | ASTM D638 |
| Ineos Nova PS 2521 Crystal Polystyrene
(discontinued **) Information provided by Nova ChemicalsINEOS NOVA began October 1 2007 as an expansion of the 50:50 joint venture between NOVA Chemicals and INEOS to include North American assets. |
|||
| Tensile Strength at Break | 47.0 MPa @Temperature 23.0 °C |
6820 psi @Temperature 73.4 °F |
50 mm/min; ASTM D638 |
| Solvay Specialty Polymers Halar® 500LC Polyethylene, Chlorotrifluoroethylene (ECTFE)
(Unverified Data**)& Information provided by Solvay Specialty Polymers. |
|||
| Tensile Strength at Break | 47.0 MPa | 6820 psi | d.a.m.; ISO 527-1, -2; 5 mm/min |
| Lanxess Durethan® DP 2325 H3.0 DUS031 000000 Nylon 66 PA 66, non-reinforced, injection molding, improved flowability, impact modified, heat-aging stabilizedInformation provided by LANXESS. |
|||
| Tensile Strength at Break | 47.0 MPa | 6820 psi | ISO 37 |
| Huntsman AVALON® 95 AHT Thermoplastic Polyurethane AVALON® AHT TPUs are colorless, UV resistant and offer high transparency – even where parts need to be thick. With hardness levels ranging from 90 to 95 Shore A, AVALON® AHT is ideal for .. |
|||
| Tensile Strength at Break | 47.0 MPa | 6820 psi | ISO 527 Type 1A |
| Solvay TECHNYL® C 236SI PA6, DRY Description: Unreinforced polyamide 6 with high impact strength for injection molding.Available in: Europe and North AmericaProduct Applications: TECHNYL® C 236SI has high impact strength and fle.. |
|||
| Tensile Strength at Break | 47.0 MPa | 6820 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP ZX07421 PPO LN:* LUBRICOMP* ZX07421 is a compound based on PPO resin containing proprietary fillers. Added feature of this grade is: Wear Resistant. |
|||
| Tensile Strength at Break | 47.0 MPa | 6820 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Xenoy® IQ1103 PBT+PC (Asia Pacific) Xenoy iQ*1103 resin - Environmentally responsible and sustainable low carbon footprint resin. Xenoy iQ1103 is an unreinforced, impact modified alloy of PC (polycarbonate) + Valox iQ* PBT (polybuty.. |
|||
| Tensile Strength at Break | 47.0 MPa | 6820 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Xenoy® IQ1103 PBT+PC (Europe-Africa-Middle East) Xenoy iQ*1103 resin - Environmentally responsible and sustainable low carbon footprint resin. Xenoy iQ1103 is an unreinforced, impact modified alloy of PC (polycarbonate) + Valox iQ* PBT (polybuty.. |
|||
| Tensile Strength at Break | 47.0 MPa | 6820 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP Stat-kon RX08408_NA1D004 PA 66 LNP* Stat-Kon* RX08404_NA1D004 is a compound based on Nylon 66 containing Carbon Powder. Characteristics of this grade include: Electrically Conductive, High Impact.This data was supplied by SABI.. |
|||
| Tensile Strength at Break | 47.0 MPa | 6820 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP Lexan_BFL2200 PC (Asia Pacific) design for black light frame application as high flow PC, V-2, high reflection grade. |
|||
| Tensile Strength at Break | 47.0 MPa | 6820 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL NH4030B PPE+HIPS NH4030B is a modified PPE-HIPS blend that presents an excellent balance of non halogenated flame retardance, lower smoke production upon burning and low specific gravity for light weight parts. Nory.. |
|||
| Tensile Strength at Break | 47.0 MPa | 6820 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL PKN4775 PPE+PS PPE+PS blend. Opaque. FDA compliant in limited colors. High heat. Modulus at elevated temperature. Good ESCR performance. Thin wall extrusion and injection molding. Typical applications include pack.. |
|||
| Tensile Strength at Break | 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL PKN4775 PPE+PS (Europe-Africa-Middle East) PPE+PS blend. Opaque. FDA compliant in limited colors. High heat. Modulus at elevated temperature. Good ESCR performance. Thin wall extrusion and injection molding. Typical applications include pack.. |
|||
| Tensile Strength at Break | 47.0 MPa | 6820 psi | ISO 527 Type 1A |
| Solvay TECHNYL® C 536XT PA6, DRY Description: TECHNYL® C 536XT is an unreinforced polyamide 6, high viscosity, for extrusion blow molding. This product is available in natural color.Benefits: The product offers a good processing.. |
|||
| Tensile Strength at Break | 47.0 MPa | 6820 psi | ISO 527 |
| SABIC Innovative Plastics LNP STAT-KON KD000 Acetal Copolymer LNP* STAT-KON* KD000 is a compound based on Acetal resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive. |
|||
| Tensile Strength at Break | 47.0 MPa @Thickness 4.00 mm |
6820 psi @Thickness 0.157 in |
Injection Molded; ISO 527-2/50 |
| Styron PULSEâ„¢ 2000 EZ PC/ABS Engineering Resin Overview: PULSE 2000 Engineering Resin is designed to provide top performance in tough applications, from single piece items to intricate components. Ideal for energy management solutions, it can wi.. |
|||
| Tensile Strength at Break | 47.0 MPa | 6820 psi | ISO 527 |
| Eastman Eastar MN004 Copolyester Eastar Copolyesters are brilliantly clear polymers that have excellent impact strength, chemical resistance, dimensional stability, and low shrinkage rates. Eastar MN004 contains a mold release.Appl.. |
|||
| Tensile Strength at Break | 47.0 MPa | 6820 psi | ASTM D 638 |
| Cossa Polimeri ESTABLEND 6500 F Polycarbonate ABS Blend Polycarbonate and Acrylonitrile Butadiene Styrene blendHigh melt flow rate, good thermal resistance, good impact resistance, excellent processability, good surface appearanceInformation provided by .. |
|||
| Tensile Strength at Break | <= 47.0 MPa | <= 6820 psi | ISO/R527 |
| Polykemi AB POLYabs H00 ABS, Heat Resistant Information provided by Polykemi AB |
|||