SABIC Innovative Plastics Cycoloy® CP8930 PC+ABS (Asia Pacific)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® CP8930 PC+ABS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High heat, PC/ABS for automotive electro plating applications, excellent balance in flow/impact
Physical Properties Metric English Comments
Specific Gravity 1.13 g/cc
1.13 g/cc
ASTM D792
Density 1.10 g/cc
0.0397 lb/in³
ISO 1183
Moisture Absorption 0.200 %
0.200 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.40 %
0.40 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 16 g/10 min

@Load 5.00 kg,
Temperature 260 °C
16 g/10 min

@Load 11.0 lb,
Temperature 500 °F
ASTM D1238
Melt Index of Compound 20 g/10 min

@Load 5.00 kg,
Temperature 265 °C
20 g/10 min

@Load 11.0 lb,
Temperature 509 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 47.0 MPa
6820 psi
50 mm/min; ISO 527
47.0 MPa
6820 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 51.0 MPa
7400 psi
50 mm/min; ISO 527
52.0 MPa
7540 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 100 %
100 %
50 mm/min; ISO 527
110 %
110 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 4.0 %
4.0 %
50 mm/min; ISO 527
4.2 %
4.2 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.37 GPa
344 ksi
5 mm/min; ASTM D638
2.40 GPa
348 ksi
1 mm/min; ISO 527
Flexural Yield Strength 65.0 MPa
9430 psi
2 mm/min; ISO 178
82.0 MPa
11900 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.20 GPa
319 ksi
2 mm/min; ISO 178
2.37 GPa
344 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 5.60 J/cm
10.5 ft-lb/in
ASTM D256
3.80 J/cm

@Temperature -30.0 °C
7.12 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 50.0 kJ/m²
23.8 ft-lb/in²
80*10*3; ISO 180/1A
35.0 kJ/m²

@Temperature -30.0 °C
16.7 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
Charpy Impact, Notched 5.00 J/cm²
23.8 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
3.50 J/cm²

@Temperature -30.0 °C
16.7 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 55.0 J

@Temperature 23.0 °C
40.6 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
40.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
40.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 78.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
43.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
78.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
43.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 103 °C
217 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
103 °C

@Thickness 3.20 mm
217 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 126 °C
259 °F
Rate B/50; ISO 306
126 °C
259 °F
Rate B/50; ASTM D1525
129 °C
264 °F
Rate B/120; ISO 306
Descriptive Properties Value Comments
Ball Pressure Test, 75°C +/- 2°C PASSES
IEC 60695-10-2