Solvay TECHNYL® C 536XT PA6, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Extruded |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® C 536XT PA6, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: TECHNYL® C 536XT is an unreinforced polyamide 6, high viscosity, for extrusion blow molding. This product is available in natural color.Benefits: The product offers a good processing behavior, high impact resistance even at low temperature and high barrier properties especially to fluids such as fuels and oils, as well as a high toughness.Available in: Europe and North AmericaRegulations compliance: Grades produced or imported in Europe comply with directive 453/2010/EC, which amends REACH directive 1907/2006/EC. This grade complies with RoHS directive 2002/95/EC. Unless specified, this grade is not suitable for food contact, medical devices or toy applications.Applications: This grade is particularly recommended for use in applications such as tanks or pipes.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | ISO 1183/A |
| Water Absorption | 1.27 % @Temperature 23.0 °C, Time 86400 sec |
1.27 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Viscosity | 220 cP @Shear Rate 1000 1/s, Temperature 270 °C |
220 cP @Shear Rate 1000 1/s, Temperature 518 °F |
|
| 1050 cP @Shear Rate 100 1/s, Temperature 270 °C |
1050 cP @Shear Rate 100 1/s, Temperature 518 °F |
||
| 2200 cP @Shear Rate 10.0 1/s, Temperature 270 °C |
2200 cP @Shear Rate 10.0 1/s, Temperature 518 °F |
||
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.0206 cm/cm | 0.0206 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0207 cm/cm | 0.0207 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 47.0 MPa | 6820 psi | ISO 527 Type 1A |
| Tensile Strength, Yield | 54.0 MPa | 7830 psi | ISO 527 type 1 A |
| Elongation at Break | 55 % | 55 % | ISO 527 Type 1A |
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527 type 1 A |
| Tensile Modulus | 2.20 GPa | 319 ksi | ISO 527 Type 1A |
| Flexural Modulus | 1.95 GPa | 283 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 66.0 kJ/m² | 31.4 ft-lb/in² | ISO 180/1eA |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| Charpy Impact, Notched | 1.60 J/cm² @Temperature -30.0 °C |
7.61 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 7.60 J/cm² @Temperature 23.0 °C |
36.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 200 - 220 °C | 392 - 428 °F | |
| Adapter Temperature | 210 - 230 °C | 410 - 446 °F | |
| Die Temperature | 215 - 230 °C | 419 - 446 °F | |
| Head Temperature | 220 - 230 °C | 428 - 446 °F | |
| Screw Cooling Temperature | 210 - 230 °C | 410 - 446 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Drying Temperature | 80.0 °C @Time 28800 sec |
176 °F @Time 8.00 hour |
dew point -35°C |
| Moisture Content | <= 0.080 % | <= 0.080 % |