- Polymer Property : Tensile Strength, Yield = 25.0 MPa
Polymer Property : Tensile Strength, Yield = 25.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ISO 527 |
| Polimeri Europa Eraclene® ML 70 U High Density Polyethylene - Injection Molding Eraclene ML 70 U is a gas phase high density polyethylene resin (HDPE) with antioxidants, suitable for injection molding application.This grade has a narrow molecular weight distribution. It combin.. |
|||
| Tensile Strength, Yield | 25.0 - 30.0 MPa | 3630 - 4350 psi | ISO.527 DN.53455 |
| Polimersan Plastics POLITEF® (PTFE) POLITEF (PTFE) was invented in 1938. It is the most preferable and known fluoropolymer among fluorine polymers. It has superior properties that none of the other industrial plastics have because of .. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | 500 mm/min (20 in./min.); ASTM D638, Type IV Specimen |
| Eastman M3016-P Polyethylene
(discontinued **) M3016-P is suggested for applications such as spiral-wound can linings, release paper, and photographic paper. M3016-P Has been found to exhibit good barrier properties, temperature resistance, and.. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ISO 527 |
| Total Finathene® WR 201 B N HDPE blow molding
(discontinued **) FINATHENE® WR 201 B N is a high density polyethylene produced by the slurry loop low pressure polymerization process. FINATHENE® WR 201 B N has been developed for the blow molding of Plastic Fuel .. |
|||
| Tensile Strength, Yield | 25.0 MPa @Temperature 120 °C |
3630 psi @Temperature 248 °F |
ASTM D638 |
| BASF Capron® 8202 NL Nylon 6 (DAM)
(discontinued **) Information provided by BASF Corporation.Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | |
| LyondellBasell Lupolen® 5236 HX HDPE, Impact Grade Medium flow, impact resistant, high stress-crack resistant grade for closures for bottles that contain carbonated liquids. This product contains a slip agent.Data was collected by ISO methods and o.. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM D638 |
| Ineos Nova 6200 Super High Impact Polystyrene Good toughness, Deep draw, Easy processing using all conventional methodsApplications: Thermoformed and molded packaging, Drink cups and lids, Structural foam, Custom sheetProperties were determined.. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | 50 mm/min; ISO 527-1,-2 |
| Inno-Comp INNOPOL® CS 3-9230 KAR BU UV-Stabilized, 26% Mineral-Filled Compound Blend Of Polypropylene Homopolymer And Block-Copolymer INNOPOL® CS 3-9230 KAR BU is a black colored, UV-stabilized, 26% mineral-filled compound based on a blend of polypropylene homopolymer and block-copolymer.INNOPOL® CS 3-9230 KAR BU is develope.. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM D638 |
| IRPC Polimaxx Polene 2500H Polypropylene Block Copolymer CHARACTERISTICS: EXCELLENT HIGH IMPACT, HIGH TOUGHNESS GOOD EXTRUDABILITYAPPLICATIONS: SHEET / BLOW MOLD EXTRUSION AND INJECTION MOLDING FOR CORRUGATE SHEETS, SHEETS FOR FILE, HOUSEWARES, CONTAINERS.. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM D638 |
| IRPC Polimaxx Polene 2564PCX TA6 Polypropylene Compound CHARACTERISTICS: POLYPROPYLENE BLOCK COPOLYMER WITH 30% TALCUM REINFORCED HIGH IMPACT STRENGTH CONTAIN UV STABILIZER AND LONG TERM HEAT AGING ADDITIVESAPPLICATIONS: INJECTION MOLDING FOR AUTOPARTS, .. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ISO 527-1, -2 |
| LyondellBasell Hostacomâ„¢ CB271FC Thermoplastic Polyolefin Elastomer Description: Hostacomâ„¢ CB271FC high melt flow, 2,400 MPa flexural modulus, precolored, UV-stabilized, mineral-filled thermoplastic elastomeric olefin (TEO) resin has an excellent combination of.. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ISO 527 |
| SABIC Innovative Plastics NORYL WCV063 PPE+SEBS+Polyolefin (Asia Pacific) Flexible, non-halogenated FR, mPPE extrusion grade material for evaluation in automotive wire coating applications requiring ISO6722. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP Thermocomp MB006SU PP (Europe-Africa-Middle East) LNP* THERMOCOMP* MB006SU is a compound based on Polypropylene resin containing Glass Bead. Added features include: Heat Stabilized, UV-Stabilized.This data was supplied by SABIC-IP for the Europe-Af.. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM D638 |
| Teknor Apex Sinelec CCB1834 Polypropylene Availability: Africa & Middle East; Latin America; Asia Pacific; South America Features: Electrically Conductive Forms: Pellets Processing Method: Injection MethodInformation Provided by Teknor Apex.. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM D638 |
| A. Schulman POLYFORT™ FXP 2779U UV Stabilized Copolymer Polypropylene DescriptionPolyfort® FXP 2779U is a 20% talc-filled, UV stabilized copolymer polypropylene.Information provided by A. Schulman. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | 50 mm/min; ASTM D638 |
| A. Schulman PP 1407L-01 Polypropylene High-Impact Copolymer Polypropylene DescriptionPolypropylene PP 1407L-01 is a super high-impact copolymer polypropylene.Information provided by A. Schulman. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ISO 527-2 |
| Total PPC 11712 Polypropylene, Heterophasic Copolymer ATOFINA Propylene 11712 is a nucleated controlled-rheology heterophasic copolymer. PPC 11712 is characterized by good stiffness and impact resistance as well as low shrinkage and low warpage. It h.. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ISO 527-2 |
| Total PSI 4440(EU) High Impact Polystyrene 4440 is a high impact polystyrene for the injection molding of parts demanding good dimensional stability at high temperatures, particularly front and back covers for television sets. In addition, .. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | GB/1040 |
| Zhejiang Juner PP430R Weatherability PP Series Applications: Air Conditioning SystemInformation provided by Zhejiang Juner New Materials Co, Ltd. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM D638 |
| A. Schulman POLYFORT™ FPP 2661 Injection Molding Grade Mineral Fortified Polypropylene DescriptionPolyfort® FPP 2661 is a injection molding grade mineral fortified impact enhanced polypropylene.Information provided by A. Schulman. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM D638 |
| A. Schulman POLYFORT™ FXP 2779U UV Stabilized Copolymer Polypropylene DescriptionPolyfort® FXP 2779U is a 20% talc-filled, UV stabilized copolymer polypropylene.Information provided by A. Schulman. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | dry; ISO 527-1/-2 |
| EMS-Grivory Grivory® L 25 W 40 ESD PA12 Product Description: Grilamid L 25 W 40 ESD is a high viscosity, anti-static highly flexible extrusion grade of Polyamide 12 (PA12). Grilamid L 25 W 40 ESD is plasticized and heat stabilized The inh.. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ISO R 527-2 |
| Arkema Group OREVAC® 18510P Grafted Maleic Anhydride Polyethylene OREVAC 18510P is a maleic anhydride grafted polyethylene used in the manufacturing of three layer MDPE or HDPE coating for steel pipeline. It is a powder product. OREVAC 18510P is mainly used in pip.. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM D638 |
| Aclo Accutech Polypropylene Homopolymer HP0334C40L Calcium Reinforced |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | |
| BASF Novolen® 3200 H Polypropylene Blow moldings and thermoformed parts.Data was collected by ISO methods and provided by BASF. |
|||
| Tensile Strength, Yield | 25.0 MPa @Temperature 120 °C |
3630 psi @Temperature 248 °F |
ISO Data |
| BASF Ultramid® 8202C HS PA6 (Conditioned) Ultramid 8202C HS is a heat stabilized, low viscosity, PA6 injection molding homopolymer possessing a modified crystalline structure for increased property performance and faster cycles. It is also.. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | 50 mm/min |
| Arkema Group Rilsan® 8020 Nylon 11, Flexible Tubing Grade (Conditioned) Designation ISO 1874-PA11/xx,E,16-003Transparent and flexible copolymer for tubes extrusion. Additive free.Good flexibility. Very good transparency. High chemical resistance.USP XXIII class VI appro.. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | 50 mm/min; ASTM D638 |
| Carmel Olefins CAPILENE® HU 75 AV Polypropylene Impact Copolymer Description: CAPILENE® HU 75 AV is a nucleated and antistatic controlled rheology impact copolymer for injection molding. It is characterized by improved stiffness and medium impact resistance. .. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM D638 |
| A. Schulman POLYFORT™ PP 1329 UV Stabilized, Medium Impact Copolymer Polypropylene DescriptionPolyfort® PP 1329HU is a high flow UV stabilized, medium impact copolymer polypropylene. Information provided by A. Schulman. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | |
| TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 60 PHR Non-Black, Aerosil 200 Millathane® 76 is a very suitable choice for use in products such as bushings, small copier rolls; automotive applications — bumpers, o-rings, hydraulic seals, belts, gaskets, solid tires — and m.. |
|||