Polymer Property : Tensile Strength, Yield = 34.5 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	34.5 MPa	5000 psi	ASTM D638
Polymer Resources PPX-GP4-IM Modified-PPO, Impact Modified Modified-Polyphenylene Oxide, Impact Modified, 210F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informati..
Tensile Strength, Yield	34.5 MPa @Thickness 3.20 mm	5000 psi @Thickness 0.126 in	At 51mm/min, injection molded ASTM Type 1 specimen; ASTM D638
Pinnacle Polymers 1220 Polypropylene Homopolymer, Injection Molding Grade This Pinnacle Polymers Polypropylene is made via UNIPOL™ PP technology, which utilizes gas-phase fluidized bed reactors with a high activity catalyst system to ensure uniform physical properties an..
Tensile Strength, Yield	34.5 MPa	5000 psi
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 30 PHR Hi-Sil 233 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	34.5 MPa	5000 psi
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 45 PHR Hi-Sil 233 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	34.5 MPa	5000 psi	ASTM D638
Albis Plastics Cellulose Acetate Butyrate B900 (Base Grade), 7% Plasticizer (discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T..
Tensile Strength, Yield	34.5 MPa	5000 psi	ASTM D638
Albis Plastics Cellulose Acetate Butyrate B9004 (Odor Mask Added), 7% Plasticizer (discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T..
Tensile Strength, Yield	34.5 MPa	5000 psi	ASTM D638
M. Holland Company AB308LG ABS Acrylonitrile Butadiene Styrene High flowGood impact resistanceHigh stiffnessApplications: Household goodsPackagingInformation provided by M. Holland
Tensile Strength, Yield	34.5 MPa	5000 psi	ASTM D1457
Greene Tweed AvalonÂ® 56 PTFE PTFE is used in many pharmaceutical-sealing applications. Its chemical inertness and ultra-low level extractables provide pharmaceutical process and validation engineers with a safe material to use..
Tensile Strength, Yield	34.5 MPa	5000 psi	ASTM D638
Spartech Royalite R24 ABS General Purpose Sheet Description: General Purpose SheetInformation provided by Spartech.
Tensile Strength, Yield	34.5 MPa	5000 psi	ASTM D638
Techmer ES HiFill FRÂ® PP GF10 FR BK 10% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 10% Filler by WeightFeatures: Flame Retardant Appearance: BlackInformation provided by TP Composites, Inc.
Tensile Strength, Yield	34.5 MPa	5000 psi	Longitudinal
Saint-Gobain NortonÂ® FluorglasÂ® ChemfilmÂ® R191 Skived Sintered PTFE Tape (0.001" thick) Description: Skived Sintered PTFE Films are used as barrier and insulation tapes for wire and cable, as well as the primary wall material for convoluted hose, Description: Skived sintered films meet..
Tensile Strength, Yield	34.5 MPa	5000 psi	ASTM D412-92
Saint-Gobain TygothaneÂ® C-544-AI.B. Precision Polyurethane Pressure Tubing Formulation Description: TygothaneÂ® C-544-A I.B.: More flexible than many other reinforced urethane tubings, TygothaneÂ® Pressure Tubing can be used in some of the most physically demanding applications,..
Tensile Strength, Yield	34.5 MPa	5000 psi	ASTM D638
A. Schulman PP 1255-01 Polypropylene General Purpose Homopolymer Polypropylene DescriptionPolypropylene PP 1255-01 Natural is a general purpose molding grade, with UL 94 HB approval, homopolymer polypropylene. ApplicationPolypropylene PP 1255-01 meets FDA Regulation 21 CFR 177..
Tensile Strength, Yield	34.5 MPa	5000 psi	50mm/min; ISO 527-2
Borealis HE125MO Polypropylene HE125MO is a polypropylene homopolymer intended for injection molding. This grade is characterized by good flow properties and high stiffness in and is specially suitable for high-speed injection mo..
Tensile Strength, Yield	34.5 MPa	5000 psi	ASTM D638
Washington Penn Homopolymer Polypropylene 40% Talc Filled Talc-filled polypropylene compounds have been tailored specifically to meet the requirements of each of the major automobile producers. Grades are available to meet FDA food and drug packaging requi..
Tensile Strength, Yield	34.5 MPa	5000 psi	2" (50mm) per min.; ASTM D638
Formosa Plastics Formolene® 4101O BCF Fiber Spinning Polypropylene HomopolymerApplications: Multifilament and bulk continuous filament fiber.Formolene 4101O is a low viscosity, highly isotactic polypropylene homopolymer designed primarily for multifilament and bulk..
Tensile Strength, Yield	34.5 MPa	5000 psi	2" (50mm) per min.; ASTM D638
Formosa Plastics Formolene® 5100H Extrusion processing Polypropylene HomopolymerApplications: Various extrusion profile, sheet and film applications.Formolene 5100H DEVELOPMENTAL is a high molecular weight, highly isotactic polypropylene homopolymer designed for vari..
Tensile Strength, Yield	34.5 MPa	5000 psi	ASTM D638
A. Schulman PP 3468-01 Polypropylene Homopolymer For High Speed Extrusion DescriptionPolypropylene PP 3468-01 is a specially designed homopolymer for high speed extrusion applications. ApplicationTypical applications of PP 3468-01 include profile extrusions, strapping, r..
Tensile Strength, Yield	34.5 MPa	5000 psi	50 mm/min; ASTM D638
A. Schulman PP 829-01 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 829-01 is a homopolymer polypropylene approved to Ford specification ESB-M4D63A. Primarily used for interior automotive components, this material is also well suited for..
Tensile Strength, Yield	34.5 MPa	5000 psi	ASTM D638
A. Schulman PP 3490-01G Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 3490-01G Natural is a homopolymer for extrusion and compounding applications. This material can also be used as a carrier resin for color concentrates. ApplicationPP 349..
Tensile Strength, Yield	34.5 MPa	5000 psi	chs 2.0 in/min; ASTM D638
Diamond Polymers GPPS BEADS Injection Molding Grade, General Purpose Polystyrene Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Tensile Strength, Yield	34.5 MPa	5000 psi	2 in/min; D-638
Bapolene® 4042 Polypropylene, Fiber/Filament Grade Bapolene PP4042 is a fiber extrusion resin with excellent thermal and mechanical properties. This product meets FDA standards for food contact applications.Applications: Rope and twine, fibrillated..
Tensile Strength, Yield	34.5 MPa	5000 psi	ASTM D638
Aaron Industries AAROLENE® AVPS HIPS 100-3 MELT 14 Virgin HIPS Resin A virgin, high impact polystyrene, natural in color, specifically designed for injection molding applications.
Tensile Strength, Yield	34.5 MPa	5000 psi
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 45 PHR Hi-Sil 233 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	34.5 MPa @Temperature 23.0 °C	5000 psi @Temperature 73.4 °F	2 in/min; ASTM D638
Ineos H20E-00 Polypropylene Homopolymer This is a homopolymer containing antistatic designed for injection molding. This material meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520.Application..
Tensile Strength, Yield	34.5 MPa @Temperature 23.0 °C	5000 psi @Temperature 73.4 °F	ASTM D638
Ineos H35G-00 Polypropylene Homopolymer This is a general purpose homopolymer for injection molding applications. This material meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520.ApplicationsC..