Polymer Property : Tensile Strength, Yield = 35.9 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	35.9 MPa	5210 psi	Type I, 5.1 mm/min; ASTM D638
PolyOne LubriOne™ ATT-000/5T Black Acetal (POM) Copolymer LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L..
Tensile Strength, Yield	35.9 MPa	5200 psi	2 in per min; ASTM D638
Network Polymers NPP 30-007W Description: Homopolymer PolypropyleneInformation provided by Network Polymers Inc.
Tensile Strength, Yield	35.9 MPa	5200 psi	2 in per min; ASTM D638
Network Polymers NPP 30-1200 A Description: Homopolymer Polypropylene Nucleated with AntistaticInformation provided by Network Polymers Inc.
Tensile Strength, Yield	35.9 MPa	5200 psi	ASTM D638
Polymer Resources ABS-FR1 ABS, Flame Retardant Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Tensile Strength, Yield	35.9 MPa	5200 psi	ASTM D638
Polymer Resources ABS-GP1-[color]-3 ABS, General Purpose, UV-stabilized Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Tensile Strength, Yield	35.9 MPa	5200 psi	ASTM D638
Ravago Manufacturing Americas Hylac® HF224 ABS Entec's proprietary products include a full range of compounds in the Nylon 6/6, Nylon 6, ABS, PBT, Polycarbonate, PC/ABS, PC/ASA, PC/PBT, and PPO/PPE resin families.Information provided by Rava..
Tensile Strength, Yield	35.9 MPa @Thickness 3.20 mm	5200 psi @Thickness 0.126 in	At 51mm/min, injection molded ASTM Type 1 specimen; ASTM D638
Pinnacle Polymers 1703 Polypropylene Homopolymer, Stretched Tape Grade This Pinnacle Polymers Polypropylene is made via UNIPOL™ PP technology, which utilizes gas-phase fluidized bed reactors with a high activity catalyst system to ensure uniform physical properties an..
Tensile Strength, Yield	35.9 MPa	5200 psi
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 30 PHR N650 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	35.9 MPa	5200 psi
TSE Industries Millathane® CM Millable Polyether Urethane Rubber, Hardness 75A MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	35.9 MPa	5200 psi	2 in/min; ASTM D638
Phillips 66 COPYLENE® CH043L Polypropylene, Homopolymer, Lube, Straw COPYLENE™ CH043L is a high antistatic, medium flow polypropylene homopolymer resin, suitable for injection molding or extrusion applications. Applications: Housewares. Equivalent to Pro-fax® HL782..
Tensile Strength, Yield	35.9 MPa	5200 psi	ASTM D638
FiberfilÂ® PP-60/VO Polypropylene Homopolymer, Flame Retardant, UL94 V0 Information provided by FIBERFIL Engineered Plastics
Tensile Strength, Yield	35.9 MPa	5200 psi	ASTM D638
M. Holland Company PP210 Polypropylene Homopolymer AntistaticHomopolymerOdor-low to noneGood processing stabilityTaste-low to noneApplications: Drinking straws
Tensile Strength, Yield	35.9 MPa	5200 psi	51 mm/min; ASTM D638
I. Stern 1335 Prime Homopolymer Polypropylene Features:Excellent flow characteristicsFDAGood mold releaseLow odor and tasteApplicationsClosuresHousewaresSmall appliancesToysInformation provided by I. Stern & Co. Inc.
Tensile Strength, Yield	35.9 MPa	5200 psi	ASTM D638
Global MPP-140-C 40% Mica Reinforced Polypropylene Information provided by Global Polymers Corporation.
Tensile Strength, Yield	35.9 MPa	5200 psi	ASTM D638
Spartech Royalite R59 ABS/PVC Fire Rated Sheet Description: Fire Rated SheetInformation provided by Spartech.
Tensile Strength, Yield	35.9 MPa	5200 psi	ASTM D638
Westlake Plastics Kynar® PVDF CN-P Polyvinylidene Fluoride (conductive) Carbon-powder-filled, thermally stable, conductive material with consistent resistivities
Tensile Strength, Yield	35.9 MPa	5200 psi
Tra-Con Tra-Bond 5126 Medium Viscosity Aerospace-Grade Epoxy Adhesive TRA-BOND 5126 AEROSPACE-GRADE EPOXY ADHESIVE is a two-part, clear (amber), medium viscosity, aerospace-grade epoxy adhesive system recommended for bonding a wide variety of materials for structural ..
Tensile Strength, Yield	35.9 MPa	5200 psi
TSE Industries Millathane® CM Millable Polyether Urethane Rubber, Hardness 75A MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	35.9 MPa	5200 psi
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 30 PHR N339 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	35.9 MPa	5200 psi
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 30 PHR N650 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	35.9 MPa	5200 psi	ASTM D638
Engineered Polymer Solutions ABS 450 Low Gloss, Medium Impact. Natural and colors available. Injection molding grade. Uses: General PurposeInformation provided by Engineered Polymer Solutions.
Tensile Strength, Yield	35.9 MPa	5200 psi	chs 2 in/min; ASTM D638
Diamond Polymers ASA S950 Description: ASA Weatherable Polymer, Injection Molding Grade, Very High ImpactInformation provided by Diamond Polymers, Inc.
Tensile Strength, Yield	35.9 MPa	5210 psi	2 in/min (50 mm/min); ASTM D638
Bapolene® 4012 Polypropylene, Extrusion Grade Bapolene PP4012 is a general purpose extrusion resin with excellent stiffness and processability, chemical resistance, and ESCR properties. This product meets FDA standards for food contact applic..
Tensile Strength, Yield	35.9 MPa	5210 psi	2 in/min (50 mm/min); ASTM D638
Bapolene® 4082 Polypropylene, Injection Grade Bapolene PP4082 is a high flow, fast cycle injection molding resin. Injection molded parts exhibit good stiffness and chemical resistance. This product meets FDA standards for food contact applica..
Tensile Strength, Yield	35.9 MPa	5200 psi	ASTM D638
Plastics Group Polifil® RP-ABS Acrylonitrile-Butadiene Styrene, High Flow Version Polifil® RP- Acrylonitrile-Butadiene Styrene is a styrenic resin with improved toughness and heat resistance versus HIPS grades. ABS exhibits high gloss, low shrinkage, and good dimensional stabili..
Tensile Strength, Yield	35.9 MPa @Temperature 23.0 °C	5200 psi @Temperature 73.4 °F	ASTM D638
Ineos H20G-00 Polypropylene Homopolymer This is a general purpose homopolymer for injection molding applications. This material meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520.ApplicationsC..
Tensile Strength, Yield	35.9 MPa	5200 psi	2.0 in/min; ASTM D638
LTL Color Compounds ColorFast® GPA300X ABS Extrusion grade, high impact, high gloss ABSAll information provided by LTL Color Compounders, Inc.
Tensile Strength, Yield	35.9 MPa	5210 psi	ASTM D638
Eastman Tenite Butyrate 465E2R30008 Natural, Trsp Cellulose Acetate Butyrate (discontinued **) Plasticizer 8%. Weight loss on heating = 0.7% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of pr..
Tensile Strength, Yield	35.9 MPa	5210 psi	ASTM D638
Eastman Tenite Butyrate 465E3720008 Clear, Trsp Cellulose Acetate Butyrate (discontinued **) Plasticizer 8%. Weight loss on heating = 0.7% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of pr..
Tensile Strength, Yield	35.9 MPa	5210 psi	ASTM D638
Eastman Tenite Butyrate 513E3720012 Clear, Trsp Cellulose Acetate Butyrate (discontinued **) Plasticizer 8%. Weight loss on heating = 0.7% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of pr..