Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 33.0 MPa | 4790 psi | ASTM D638 |
Petromont 8001 High Density Polyethylene Resin Pétromont HDPE 8001 is a high density, homopolymer polyethylene resin produced using the UNIPOL® Process. This high strength resin is intended for extrusion on cast line, where excellent processab.. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | 50 mm/min |
Polimeri Europa KOBLEND HI 10 PBT+PC, Impact Grade
(discontinued **) Symbol according to ISO 1043/1: PBT+PC-HI Elastomer modified PBT+PC blend with very good impact behaviour, ductility even at low temperatures, resistant to solvents. Main application fields: autom.. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | |
TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 0.5 PHR Zinc Stearate Millathane® 76 is a very suitable choice for use in products such as bushings, small copier rolls; automotive applications — bumpers, o-rings, hydraulic seals, belts, gaskets, solid tires — and m.. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | ASTM D638 |
BP Amoco Acctuf® 3119HS Ultra High Impact Copolymer Polypropylene
(discontinued **) Suggested fabrication methods: Extrusion; ThermoformingFeatures: High stiffness, Low Temperature impactComplies with FDA specification, Title 21, CFR 177.1520.Typical property data below from inject.. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP MG004 PP (Europe-Africa-Middle East) LNP* Lubricomp* MG004 is a compound based on Polypropylene resin containing Graphite Powder. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP ML003S PP LNP* LUBRICOMP* ML003S is a compound based on Polypropylene resin containing 15% PTFE. Added features include: Heat Stabilized, Wear Resistant. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP ML004LS PP LNP* LUBRICOMP* ML004LS is a compound based on Polypropylene resin containing 20% PTFE. Added features of this matLNP* Lubricomp* ML004LS is a compound based on Polypropylene resin containing PTFE... |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® 309 PBT PBT, For compounding only. Not intended for Injection Molding. Melt viscosity: 250C at 21.6 kgf is 3500-4500. Available in Natural (1001) only. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | 50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 20808 Polyvinylidene Fluoride (PVDF) Copolymer; Low ViscosityAdditional Properties: Abrasion Resistance - ASTM D4060 29.0 mg; Coefficient of Friction - ASTM D1894 0.280; Coefficient of Linear Thermal Expansion - ASTM D696 1.4E-4 to 1.6.. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL PPX PPX7200 PPE+PP+PS (Asia Pacific) PP+PPE+PS. Improved chemical resistance and surface aesthetics in injection molded applications. NSF61-capable. UL-94 HB listed. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | 50mm/min; ISO 527-2 |
Borealis HG430MO Polypropylene HG430MO is a polypropylene homopolymer intended for injection molding. This polymer product is characterized by a superior impact resistance. This grade has ductile failure in falling weight impact .. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | 50 cm/min; ASTM D638 |
Washington Penn PPUP4G402 Polypropylene, 40% Talc Filled, High Flow Exceptional retention of mechanical properties and appearance upon long term heat aging.Applications: Appliance parts.Data provided by Washington Penn Plastic Co., Inc. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | ISO 527-2 |
Tisan TISOPLEN® 10% Talc Filled Heat Stabilized Homopolymer Polypropylene TISOPLEN has a wide area of application in furniture, durable goods, household appliances, electrics/electronics, and telecommunication industries. General specifications include Low densityLow mois.. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | ISO 527-2 |
Total PPH 3051 Polypropylene, Homopolymer ATOFINA Polypropylene PPH 3051 is homopolymer.ApplicationATOFINA Polypropylene PPH 3051 is intended for the extrusion of flat bioriented films for food packaging or high strength adhesive tapes. Inf.. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | ASTM D638 |
Total PPH 3727W Polypropylene, High Performance Injection Molding Grade Balanced Properties TOTAL Polypropylene 3727W strikes an optimum balance between excellent mechanical properties (tensile, flex and impact) and processability making it a superior molding grade for.. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | ISO 527-2 |
Total PPH 4054 Polypropylene Homopolymer Polypropylene PPH 4054 is a homopolymer polypropylene with a Melt Flow index of 3 g/10 min.Polypropylene PPH 4054 has been designed for the production of BOPP film with the tenter frame process. Th.. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | ASTM D638 |
Total PSI 3441 High Heat Resistance Impact Polystyrene Total Petrochemicals Polystyrene 3441 is a high heat resistance, high impact polystyrene for injection molding. It is recommended for the manufacturing of articles which require good dimensional st.. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | ISO 527-2/50 |
ExxonMobil PP1013H1 Polypropylene Homopolymer Product Description: A homopolymer resin that meets certified requirements for use in Medical and Pharmaceutical applications.Availability: Europe and North America Features:Autoclave SterilizableE.. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | 50%RH; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® RS LC1610 BK387 Nylon 1010
(Unverified Data**) Plasticized Toughened Renewably Sourced Polyamide 1010 Developed for Extrusion Information provided by DuPont Performance Polymers |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | parallel; ISO 527-3 |
Covestro Desmopan® W DP89085A Polyurethane PreprocessingMax. Water content |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | ASTM-D638 |
Braskem H 125 HOMO Polypropylene Homopolymer H 125 is a high melt flow rate homopolymer designed for nonwoven by spunbonded processing. It is used in fiber extrusion processing. This resin features excellent processing, allowing increased line.. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | 50 mm/min |
Arkema Group Rilsan® MB 3501 Nylon 11, Flexible Tubing Grade (Dry) Designation ISO 1874-PA11-HI,MHL,22-004Flexible grade for tubes extrusion. Available color: black. Light and heat stabilized.Flexibility. High burst pressure and impact strength. Fit for use in a wi.. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | 50 mm/min; ASTM D638 |
Carmel Olefins CAPILENE® E 65 F Polypropylene Homopolymer Description: CAPILENE® E 65 F is a polypropylene homopolymer designed for the production of biaxially oriented polypropylene films (BOPP). It exhibits good processability, easy film stretchabilit.. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | ASTM D638 |
Carmel Olefins CAPILENE® Y 50 V Polypropylene Homopolymer CAPILENE® Y 50 V is an ultra high melt flow rate polypropylene homopolymer suitable for thin walled injection molding and as a base resin for compounds applications. The product combines high stiff.. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | ASTM D638 |
Braskem H 603 Blow Molding Polypropylene Description: H 603 is a low melt flow rate homopolymer used for general purposes. This resin is designed for blow moulding and extrusion applications. H 603 exhibits excellent processability, excell.. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | ISO value at 50 mm/min. |
BASF Capron® 8351 Impact Modified Nylon 6 (Conditioned)
(discontinued **) Capron 8351 is a type 6 polyamide graft copolymer developed for injection molding applications requiring a high level of toughness combined with moderate flexibility and faster cycles. It is also .. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | ISO R 527 |
Addiplast Addilene H 442 M30 Polypropylene Homopolymer High heat resistance, detergent stabilizedInformation provided by Addiplast. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | ASTM D638 |
Braskem H 401 Cast Film Extrusion Polypropylene Description: H 401 is a medium melt flow rate homopolymer polypropylene, additived with slip and antiblocking agents. Designed specially for cast film. This product features good impact strength, ex.. |