Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics EXTEM VH1003F PEI Copolymer Transparent, Thermoplastic Polyimide (TPI) resin with a glass transition temperature (Tg) of 247C. This product has thinwall FR capability and has a UL94 V0 listing. This material is RoHS compliant.. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | ISO 527-1/2 |
Radici Radilon® SRCP3010LK (dry) Nylon 6 Heat stabilized glass-fiber reinforced and mineral reinforcedInformation provided by Radici group. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | ISO 527-1/-2 |
DSM Akulon® S223-E Nylon 66 (European and Asian Grade) (Dry)
(discontinued **) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | ISO 527-1/-2 |
Lanxess Durethan® A 30 S 000000 Nylon 66 PA 66 standard injection molding-grade, non-reinforced, good demolding, very rapid solidificationApplication Examples: plug connectors, terminal blocks, cable clips, bobbins |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | d.a.m.; ISO 527-1, -2; 50 mm/min |
Lanxess Durethan® A 30 S H3.0 000000 Nylon 66, Injection Molding PA 66, non-reinforced, injection moldingInformation provided by LANXESS. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | ISO 527 type 1 A |
Solvay TECHNYL® B 218 Black 21 N PA66/6, DRY Description: Unreinforced copolyamide PA 66/6 , heat stabilized , medium viscosity, for injection molding.Available in: EuropeProduct Applications: TECHNYL® B 218 offers all of the primary proper.. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RFL22E PA6.6 (Europe-Africa-Middle East) LNP* LUBRICOMP* RFL22E Is a compound based on PA66 resin, containing Glass Fiber and PTFE. Added features include: Internally Lubricated, Easy Moulding |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | ISO-DIS 527 |
Schwartz Technical Plastics LAMIGAMID® 319 Cast Polyamide 6, Oil Filled, Dry Application: sheaves and wheels without additional bearings, sliding linersInformation provided by Schwartz Technical Plastics GmbH |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RX03643H PA 66 (Asia Pacific) LNP* Lubricomp* RX03643H is a compound based on Nylon 66 resin containing Proprietary Filler(s). Added features of this material include: Internally Lubricated. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM DH1004 PEI (Asia Pacific) High Temperature, Transparent, Polyetherimide Blend with Improved Ductility and Enhanced Hydrostability. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM DH1004 PEI (Europe-Africa-Middle East) High Temperature, Transparent, Polyetherimide Blend with Improved Ductility and Enhanced Hydrostability. RoHS compliant and UL94 V0 listed. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Ultem HATX200 PEI+PCE High flow Polyetherimide blend. ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compli.. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Ultem HFATX200 PEI+PCE High flow Polyetherimide blend with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Ultem XH6050F PEI Copolymer (Europe-Africa-Middle East) Transparent, enhanced flow Polyetherimidesulfone copolymer (Tg 247C). ECO Conforming. US FDA Compliant. Resin is subject to U.S. Commerce Control Laws (15CFR Chapter VII, Part 774).This data was .. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® VX5011 PBT (Europe-Africa-Middle East) VALOX VX5011 is a 10% glass fibre reinforced PBT+PC blend with low warpage characteristics. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Thermocomp PX05046 PA 6 (Europe-Africa-Middle East) LNP* THERMOCOMP* PX05046 is a compound based on PA 6 resin containing Glass Bead, Glass Fiber.
Added features include: Heat Stabilized, UV-Stabilized.This data was supplied by SABIC-IP for the Europ.. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM AUT230 PEI Transparent polyetherimide (Tg 247 degC). Very low outgassing and plateout, for automotive lighting applications where highly metallized, reflective surfaces are required. Haze onset temperature of.. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® 815F PBT+PET (Asia Pacific) PBT+PET, 15% Glass, Mold Release, Heat Stabilized, For food contact applications |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | ISO 527-2 |
Tisan TISLAMID® 6 20% Glass Fiber Reinforced, Flame Retardant (V0). Halogen Free Heat Stabilized Nylon 6 TISLAMID has a wide area of application in electric/electronic, automotive, durable goods and telecommunications industries. It demonstrates characteristics such as Excellent chemical resistanceElec.. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | ISO 527-1/-2 |
DSM Akulon® K222-D Nylon 6 (European and Asian Grade) (Dry) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | dry; ISO 527-1/-2 |
EMS-Grivory Grivory® BK-50 PA6-GB50 Information provided by EMS Grivory |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | ISO 527-2 |
Ascend Performance Materials Vydyne® 20NSP1 Nylon 66, DAM Availability:Asia PacificEuropeNorth AmericaFiller/Reinforcement:Glass Fiber, 43% Filler by Weight Additive:Nucleating AgentLubricant Features:Fast Molding CycleGeneral PurposeGood Mold Release Good.. |
|||
Tensile Strength, Yield | 95.0 MPa @Temperature -40.0 °C |
13800 psi @Temperature -40.0 °F |
ISO Data |
BASF Ultramid® 8350 HS PA6 (Conditioned) Ultramid 8350 HS is a heat stabilized, impact modified type 6 graft copolymer developed for extrusion, tubing, and jacketing applications requiring a high level of toughness combined with a moderate.. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | 50 mm/min; ISO 527-2 |
BASF Ultradur® B 4406 G2 10% Glass Filled PBT Description: Is a PBT, flame-retardant injection-molding grades, with 10% glass fibers, for parts requiring enhanced fire resistance, e.g. plug-and-socket connectors, housings, coil formers and ligh.. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | ASTM D638 |
Beijing Ranger Chem PBT-201-G10 Flame Retarding FR PBT Modified PBT Characteristics: Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning (94HB) and self-extinguishin.. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | 50 mm/min; Same value from ASTM and ISO test. |
BASF Capron® 5202CQ Blend HS Blend Nylon 66 (Dry)
(discontinued **) Capron 5202CQ HS Blend is a heat stabilized, blended polyamide 6,6 injection molding homopolymer developed for fast molding cycles. It is also available in pigmented versions.Capron 5202CQ HS Blend.. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | |
Radici Radilon® A 38 (dry) Nylon 66 Radilon® A is a range of polyamide 66 (PA66) products obtained through the polymerization of hexamethylendiamine and adipic acid, and used for injection, extrusion and blow-molding.Information prov.. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | |
Radici Radilon® A 42 (dry) Nylon 66 Radilon® A is a range of polyamide 66 (PA66) products obtained through the polymerization of hexamethylendiamine and adipic acid, and used for injection, extrusion and blow-molding.Information prov.. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® 3412ECR PC (Asia Pacific) Lexan* 3412ECR Polycarbonate (PC) resin is a 20% glass fiber filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant GF-PC has an UL-94 V0 rating and is available in v.. |