Ascend Performance Materials Vydyne® 20NSP BLK Nylon 66, DAM

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Nucleated
Manufacturer Ascend Performance Materials (formerly Solutia)
Trade Name VYDYNE®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ascend Performance Materials Vydyne® 20NSP BLK Nylon 66, DAM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Vydyne® 20NSP BLK is a general-purpose, high nucleated, lubricated PA66 resin. Available in black, it is designed to crystallize rapidly in order to reduce cycle times and increase productivity through faster part set-up. The higher crystalline structure will increase tensile modulus and strength, reduce elongation and may slightly lower mold shrinkage when compared to standard general-purpose non nucleated PA66. The rapid crystallization of Vydyne 20NSP BLK resin may allow part ejection at a higher temperature compared to general-purpose PA66. Critical factors unique to each application such as mold design, part design, tolerances and other factors will dictate ultimate cycle time benefits. It is recommended to check critical part dimensions against specifications before adopting shorter molding cycles. Vydyne 20NSP BLK resin has an external lubricant for improved machine feed and an internal lubricant for improved mold release. Typical Applications/End Uses: End uses for Vydyne 20NSP BLK include terminal blocks, bears, control cams, electrical connectors, housings, cable ties, fasteners, switch components and industrial parts that require chemical resistance, stiffness, wear resistance and rigidity.Availability:Asia PacificEuropeNorth AmericaAdditive:LubricantNucleating Agent Features: Fast Molding CycleGeneral PurposeGood Mold ReleaseGood StiffnessHigh RigidityLubricatedNucleatedUses:BearingsCamsConnectorsFastenersGeneral PurposeHousingsIndustrial ApplicationsAppearance: BlackForms: PelletsProcessing Method: Injection MoldingInformation provided by Ascend Performance Materials.
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
ISO 1183
Water Absorption 1.2 %

@Time 86400 sec
1.2 %

@Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 2.4 %
2.4 %
50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.014 cm/cm

@Diameter 2.00 mm
0.014 in/in

@Diameter 0.0787 in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.016 cm/cm

@Diameter 2.00 mm
0.016 in/in

@Diameter 0.0787 in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 75.0 MPa
10900 psi
ISO 527-2
Tensile Strength, Yield 95.0 MPa
13800 psi
ISO 527-2
Elongation at Break 13 %
13 %
ISO 527-2
Elongation at Yield 5.0 %
5.0 %
ISO 527-2
Tensile Modulus 3.80 GPa
551 ksi
ISO 527-2
Flexural Strength 100 MPa
14500 psi
ISO 178
Flexural Modulus 3.20 GPa
464 ksi
ISO 178
Poissons Ratio 0.40
0.40
ISO 527-2
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
ISO 180
6.00 kJ/m²

@Temperature 23.0 °C
2.86 ft-lb/in²

@Temperature 73.4 °F
ISO 180
Charpy Impact Unnotched NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179/1eU
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.500 J/cm²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
0.600 J/cm²

@Temperature 23.0 °C
2.86 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 10.0 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
5.56 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
ISO 11359-2
CTE, linear, Transverse to Flow 10.0 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
5.56 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
ISO 11359-2
Melting Point 260 °C
500 °F
ISO 11357-3
Deflection Temperature at 0.46 MPa (66 psi) 230 °C
446 °F
Unannealed; ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi) 90.0 °C
194 °F
Unannealed; ISO 75-2/A
UL RTI, Electrical 130 °C

@Thickness 4.00 mm
266 °F

@Thickness 0.157 in
UL 746
130 °C

@Thickness 0.710 mm
266 °F

@Thickness 0.0280 in
UL 746
130 °C

@Thickness 1.50 mm
266 °F

@Thickness 0.0591 in
UL 746
130 °C

@Thickness 3.00 mm
266 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical with Impact 75.0 °C

@Thickness 4.00 mm
167 °F

@Thickness 0.157 in
UL 746
75.0 °C

@Thickness 0.710 mm
167 °F

@Thickness 0.0280 in
UL 746
75.0 °C

@Thickness 1.50 mm
167 °F

@Thickness 0.0591 in
UL 746
75.0 °C

@Thickness 3.00 mm
167 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical without Impact 75.0 °C

@Thickness 4.00 mm
167 °F

@Thickness 0.157 in
UL 746
85.0 °C

@Thickness 0.710 mm
185 °F

@Thickness 0.0280 in
UL 746
85.0 °C

@Thickness 1.50 mm
185 °F

@Thickness 0.0591 in
UL 746
85.0 °C

@Thickness 3.00 mm
185 °F

@Thickness 0.118 in
UL 746
Flammability, UL94 V-2

@Thickness 0.400 mm
V-2

@Thickness 0.0157 in
V-2

@Thickness 0.710 mm
V-2

@Thickness 0.0280 in
V-2

@Thickness 4.50 mm
V-2

@Thickness 0.177 in
V-2

@Thickness 3.00 mm
V-2

@Thickness 0.118 in
Oxygen Index 26 %
26 %
ISO 4589-2
Glow Wire Test 700 °C

@Thickness 0.710 mm
1290 °F

@Thickness 0.0280 in
Ignition Temperature; IEC 60695-2-13
700 °C

@Thickness 1.50 mm
1290 °F

@Thickness 0.0591 in
Ignition Temperature; IEC 60695-2-13
700 °C

@Thickness 3.00 mm
1290 °F

@Thickness 0.118 in
Ignition Temperature; IEC 60695-2-13
800 °C

@Thickness 0.710 mm
1470 °F

@Thickness 0.0280 in
Flammability Index; IEC 60695-2-12
800 °C

@Thickness 1.50 mm
1470 °F

@Thickness 0.0591 in
Flammability Index; IEC 60695-2-12
930 °C

@Thickness 3.00 mm
1710 °F

@Thickness 0.118 in
Flammability Index; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+10 ohm-cm

@Thickness 0.750 mm
1.00e+10 ohm-cm

@Thickness 0.0295 in
IEC 60093
Dielectric Strength 26.0 kV/mm

@Thickness 1.00 mm
660 kV/in

@Thickness 0.0394 in
IEC 60243
Arc Resistance 120 - 179 sec

@Thickness 3.00 mm
120 - 179 sec

@Thickness 0.118 in
ASTM D495
Comparative Tracking Index 600 V

@Thickness 3.00 mm
600 V

@Thickness 0.118 in
IEC 60112
Hot Wire Ignition, HWI 7.0 - 14 sec

@Thickness 0.710 mm
7.0 - 14 sec

@Thickness 0.0280 in
UL 746
15 - 29 sec

@Thickness 1.50 mm
15 - 29 sec

@Thickness 0.0591 in
UL 746
15 - 29 sec

@Thickness 3.00 mm
15 - 29 sec

@Thickness 0.118 in
UL 746
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 0.710 mm
>= 120 arcs

@Thickness 0.0280 in
UL 746
>= 120 arcs

@Thickness 1.50 mm
>= 120 arcs

@Thickness 0.0591 in
UL 746
>= 120 arcs

@Thickness 3.00 mm
>= 120 arcs

@Thickness 0.118 in
UL 746
High Voltage Arc-Tracking Rate, HVTR 0.000 - 10.0 mm/min
0.000 - 0.394 in/min
UL 746
Processing Properties Metric English Comments
Rear Barrel Temperature 260 - 280 °C
500 - 536 °F
Middle Barrel Temperature 270 - 280 °C
518 - 536 °F
Front Barrel Temperature 280 - 290 °C
536 - 554 °F
Nozzle Temperature 280 - 300 °C
536 - 572 °F
Melt Temperature 285 - 300 °C
545 - 572 °F
Mold Temperature 65.0 - 95.0 °C
149 - 203 °F
Drying Temperature <= 70.0 °C
<= 158 °F