Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 2.81 GPa | 408 ksi | Type I, 51 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Rigid Molding 87546 Polyvinyl Chloride, Rigid (PVC, Rigid) Provisional Data SheetInformation provided by PolyOne |
|||
Tensile Modulus | 2.81 GPa @Thickness 6.40 mm |
408 ksi @Thickness 0.252 in |
ASTM D 638 |
SABIC Innovative Plastics Lexan® FL3000 PC Structural foam: 10% weight reduction at 0.250" wall with non-brominated and non-chlorinated FR systems. Impact modified PC with excellent low-temperature impact and UV-stability.This data was supp.. |
|||
Tensile Modulus | 2.81 GPa | 408 ksi | Type I, 51 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Fittings 210A White 271(HS) Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
Tensile Modulus | 2.81 GPa @Thickness 6.40 mm |
408 ksi @Thickness 0.252 in |
ASTM D 638 |
SABIC Innovative Plastics Lexan® FL3000 PC (Asia Pacific) Structural foam: 10% weight reduction at 0.250" wall. ECO-conforming. Impact modified PC with excellent low-temperature impact and UV-stability.This data was supplied by SABIC-IP for the Asia Paci.. |
|||
Tensile Modulus | 2.81 GPa @Temperature -18.0 °C |
408 ksi @Temperature -0.400 °F |
1-mm/min; ISO 527 |
Ineos ABS Lustran® Guardian™ 682 ABS, Injection Molding Grade Lustran® ABS 682 is a high performance, HCFC-141b resistant grade of ABS for injection molded refrigerator and freezer components. |
|||
Tensile Modulus | 2.81 GPa | 408 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON DD0009 PC LNP* STAT-KON* DD0009 is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Electrically Conductive, Flame Retardant. |
|||
Tensile Modulus | 2.81 GPa | 408 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON DD0009 PC (Asia Pacific) LNP* Stat-kon* DD0009 is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Powder. Added features of this material include: Electrically Conductive, Flame Retardant. |
|||
Tensile Modulus | 2.81 GPa | 408 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON DD0009 PC (Europe-Africa-Middle East) LNP* Stat-kon* DD0009 is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Powder. Added features of this material include: Electrically Conductive, Flame Retardant. |
|||
Tensile Modulus | 2.81 GPa | 408 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON DD0009XP PC (Asia Pacific) LNP* Stat-kon* DD0009XP is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include:Electrically Conductive, Flame Retardant. Also known as Stat-Kon*.. |
|||
Tensile Modulus | 2.81 GPa | 408 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL EXNL1117 PPE+HIPS high gloss Noryl |
|||
Tensile Modulus | 2.81 GPa | 408 ksi | 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL GTX GTX674PC PPE+PA6 A conductive PPE/PA blend designed to have improved surface appearance and elevated heat resistance for powder coating. The material is suitable for injection molding. The material is only availab.. |
|||
Tensile Modulus | 2.81 GPa | 408 ksi | 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL GTX GTX674PC PPE+PA6 (Europe-Africa-Middle East) A conductive PPE/PA blend designed to have improved surface appearance and elevated heat resistance for powder coating. The material is suitable for injection molding. The material is only availab.. |
|||
Tensile Modulus | 2.81 GPa | 408 ksi | ASTM D-638 |
Axiall 7456 Rigid PVC, Extrusion Georgia Gulf 7456 is a special purpose rigid PVC extrusion compound designed for applications requiring the following properties: ToughnessWeatherabilityWeldabilityChemical ResistanceEase of Proces.. |