Polymer Property : Tensile Modulus = 638 ksi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Modulus | 4.40 GPa | 638 ksi | 50 mm/min; ASTM D638 |
| Ovation Polymers RIGITRON 10030 GF Polycarbonate, 30% Glass Reinforced PC - Glass reinforced (30 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared accor.. |
|||
| Tensile Modulus | 4.40 GPa | 638 ksi | 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Cycoloy® RCM6123 PC+ABS (Asia Pacific) Cycoloy* RCM6123 resin is an injection moldable filled PC/ABS blend with non-brominated and non-chlorinated flame retardant. It contains 30% post consumer recycle content with a UL-94 V0 rating @ 1.. |
|||
| Tensile Modulus | 4.40 GPa | 638 ksi | ISO 527-2 |
| Pasargad Polymer Peyvand Pasalen 3P-H3130B Polypropylene, 30% Glass Fiber Reinforced Form: PelletsProcessing Method: Injection MoldingUses: Automotive Application Furniture Appliance Components Automotive Exterior PartsAutomotive Interior PartsInformation provided by Pasargad Poly.. |
|||
| Tensile Modulus | 4.40 GPa | 638 ksi | ASTM D638 |
| North Wood Plastics HDPE with 60% Wood Fiber Data provided by North Wood Plastics, Inc. |
|||
| Tensile Modulus | 4.40 GPa | 638 ksi | ISO 527-1/-2 |
| Lanxess Durethan® BKV 215 W1 902176 Copolyamide, 15% Glass Fiber CoPA, injection molding grade, 15% glass fibers, elastomer-modified, weather-stabilized |
|||
| Tensile Modulus | 4.40 GPa | 638 ksi | Conditioned; ISO 527-1/-2 |
| Lanxess Durethan® BKV 230 H2.0 901510 Copolyamide, 30% Glass Fiber CoPA, injection molding grade, 30% glass fibers, elastomer-modified, higher impact and notched impact strength and also higher energy absorption under biaxial impact load than BKV 130, conditioning .. |
|||
| Tensile Modulus | 4.40 GPa | 638 ksi | 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL V03505 PPE+HIPS (Asia Pacific) Noryl* V03505 is a 35% milled fiber reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives t.. |
|||
| Tensile Modulus | 4.40 GPa @Temperature 80.0 °C |
638 ksi @Temperature 176 °F |
1 mm/min; ISO 527 |
| SABIC Innovative Plastics SABIC STAMAX 30YK270 PP SABIC® STAMAX 30YK270 is a 30% long glass fiber reinforced polypropylene with improved impact and flow properties. The glass fibers are chemically coupled to the PP matrix, resulting in high stif.. |
|||
| Tensile Modulus | 4.40 GPa | 638 ksi | 1 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP Lubricomp WBG16 PBT (Europe-Africa-Middle East) LNP* Lubricomp* WBG16 is a compound based on Polybutylene Terephalate resin containing Glass Bead, Graphite.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Tensile Modulus | 4.40 GPa | 638 ksi | 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® 4012G PBT (Europe-Africa-Middle East) VALOX 4012G is a 10% glass fibre reinforced PBT injection moulding resin with excellent mechanical properties. Applications: connectors. This grade is a 4012 with improved cycle time and ductility. |
|||
| Tensile Modulus | 4.40 GPa | 638 ksi | 1 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL GTX GTX985 PPE+PA66 NORYL GTX985 is a 18% mineral filled material. This material combines high stiffness and excellent temperature resistance with conductivity for electrostatic painting. |
|||
| Tensile Modulus | 4.40 GPa | 638 ksi | 1 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL GTX GTX985 PPE+PA66 (Asia Pacific) NORYL GTX985 is a 18% mineral filled material. This material combines high stiffness and excellent temperature resistance with conductivity for electrostatic painting. |
|||
| Tensile Modulus | 4.40 GPa | 638 ksi | 1 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL GTX GTX985 PPE+PA66 (Europe-Africa-Middle East) NORYL GTX985 is a 18% mineral filled material. This material combines high stiffness and excellent temperature resistance with conductivity for electrostatic painting. |
|||
| Tensile Modulus | 4.40 GPa | 638 ksi | 1 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL NH7112 PPE+HIPS (Asia Pacific) Noryl* NH7112 resin is a 10% glass reinforced, modified PPE-PS blend. The material offers an exceptional balance of strength and dimensional stability while using non-halogenated flame retardants to.. |
|||
| Tensile Modulus | 4.40 GPa | 638 ksi | 1 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL NH7112 PPE+HIPS (Europe-Africa-Middle East) Noryl* NH7112 resin is a 10% glass reinforced, modified PPE-PS blend. The material offers an exceptional balance of strength and dimensional stability while using non-halogenated flame retardants to.. |
|||
| Tensile Modulus | 4.40 GPa | 638 ksi | 1 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP 2F004 FP-E (EFTE) LNP* FP-EF-1004 is a fluoropolymer compound based on ETFE resin containing 20% Glass Fiber. |
|||
| Tensile Modulus | 4.40 GPa | 638 ksi | 5 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Xenoy® X5630 PC+PET Mineral filled PC/PET blend with high heat dimensional stability, low shrinkage and low CTE, especially for painted applicationsThis data was supplied by SABIC-IP for the Americas region. |
|||
| Tensile Modulus | 4.40 GPa | 638 ksi | 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Xenoy® X5630 PC+PET (Asia Pacific) Mineral filled PC/PET blend with high heat dimensional stability, low shrinkage and low CTE, especially for painted applications |
|||
| Tensile Modulus | 4.40 GPa | 638 ksi | 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL GFN1 PPE+HIPS (Asia Pacific) PPE+PS blend. 10% Glass reinforced. FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Suitable for fluid engineering applications including wate.. |
|||
| Tensile Modulus | 4.40 GPa | 638 ksi | ISO 527-1/-2 |
| DSM Akulon® K224-G4U (Cond.) 23% Glass Reinforced Nylon 6 (North America) Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis.. |
|||
| Tensile Modulus | 4.40 GPa | 638 ksi | 1mm/min; D638 |
| Ensinger Tecapeek® ST PolyEtherKetoneEtherKetoneKetone, Unreinforced TECAPEEK® ST is a multipurpose semi-crystaline material from the polyaryletherketone family based on PEKEKK that features improved mechanical properties at higher temperatures. The benefits of TECA.. |
|||
| Tensile Modulus | 4.40 GPa | 638 ksi | 50mm/min; ISO 527-1 |
| Denka TH-23 Transparent Resin Polymer (MBS resin) Polymethacrylate Butadiene Styrene "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a.. |
|||
| Tensile Modulus | 4.40 GPa | 638 ksi | Storage |
| Epoxy Technology EPO-TEK® E2036 Epoxy Product Description: A two component, slightly flexible, silver-filled, electrically conductive adhesive for semiconductor and electronic assemblies. It is a low Tg epoxy, intended for many kinds o.. |
|||
| Tensile Modulus | 4.40 GPa | 638 ksi | |
| BASF Procom® D 1012 Polypropylene Data was collected by ISO methods and provided by BASF. |
|||
| Tensile Modulus | 4.40 GPa | 638 ksi | 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Xenoy® X5630 PC+PET (Europe-Africa-Middle East) Mineral filled PC/PET blend with high heat dimensional stability, low shrinkage and low CTE, especially for painted applications |
|||
| Tensile Modulus | 4.40 GPa | 638 ksi | 1 mm/min; ISO 527-1 |
| Sax Polymers SAXALEN PPH303G20 Polypropylene Homopolymer, 20% Glass Filled SAXALEN PPH303G20 is a 20% glass filled Polypropylene - Homopolymer injection molding grade with good stiffness.Information provided by SAX Polymers |
|||