- Polymer Property : Tensile Strength, Ultimate = 130000 psi
Polymer Property : Tensile Strength, Ultimate = 130000 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 896 MPa | 130000 psi | Typical |
| PSM Industries PolyAlloys MIM-17-4PH sintered Stainless Steel PolyAlloys Injected Metals, a division of PSM Industries, Inc., offers precision, High-Performance components for structural, magnetic and electronic applications that require a high degree of compl.. |
|||
| Tensile Strength, Ultimate | 896 MPa | 130000 psi | |
| High Temp Metals Alloy 49 Iron-Nickel High Permeability Alloy, Strip, Cold-Rolled High Permeability "49" alloy is a 48% nickel-iron alloy which has a saturation flux density of approximately 15,000 Gauss after hydrogen annealing. Hysteresis loss is very low in either DC or AC cir.. |
|||
| Tensile Strength, Ultimate | 896 MPa | 130000 psi | |
| High Temp Metals Alloy 49 Iron-Nickel High Permeability Alloy, Strip, Cold-Rolled High Permeability "49" alloy is a 48% nickel-iron alloy which has a saturation flux density of approximately 15,000 Gauss after hydrogen annealing. Hysteresis loss is very low in either DC or AC cir.. |
|||
| Tensile Strength, Ultimate | >= 895 MPa | >= 130000 psi | |
| Kobe Steel KS EL-F Alpha-Beta Titanium Alloy, Annealed Nominal Composition: Ti-4.5 Al-4 Cr-0.5 Fe-0.2 C Applications: Aircraft parts, connecting rods, valve spring retainers, structural parts, golf club heads.Features:High strength, excellent balance b.. |
|||
| Tensile Strength, Ultimate | >= 895 MPa | >= 130000 psi | |
| Kobe Steel KS6-4 Alpha-Beta Titanium Alloy, ASTM Gr. 5, Annealed Nominal Composition: Ti-6 Al-4 V Applications: Aircraft parts, connecting rods, valve spring retainers, structural parts, golf club heads.Features:High strength, excellent balance between strength .. |
|||
| Tensile Strength, Ultimate | >= 895 MPa | >= 130000 psi | |
| Kobe Steel KSTI-9 Alpha-Beta Titanium Alloy, ASTM Gr. 35, Annealed (coil, sheets) Nominal Composition: Ti-4.5 Al-2 Mo-1.6 V-0.5 Fe-0.3 Si-0.03 C Applications: Aircraft parts, connecting rods, valve spring retainers, structural parts, golf club heads.Features:High strength, excel.. |
|||
| Tensile Strength, Ultimate | 896 MPa | 130000 psi | |
| Meehanite K-295 Austempered Ductile Iron Type K-295 is used for applications such as gears requiring high contact rolling and tooth bending fatigue properties. Type K-295 also possess high fracture toughness impact strength. Excellent fo.. |
|||
| Tensile Strength, Ultimate | 895 MPa | 130000 psi | |
| Haynes 230® alloy plate, 1000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Tensile Strength, Ultimate | 895 MPa | 130000 psi | |
| Haynes 230® alloy plate, 4000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Tensile Strength, Ultimate | 896 MPa | 130000 psi | Annealed |
| Latrobe MP35N® Alloy MP35N is a nickel-cobalt base alloy of the Multiphase alloy system that has a unique combination of properties - ultra high strength, toughness, ductility, and outstanding corrosion resistance. The .. |
|||
| Tensile Strength, Ultimate | 896 MPa @Temperature 316 °C |
130000 psi @Temperature 601 °F |
|
| Haynes Ultimet® alloy, 1.6 mm sheet Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Tensile Strength, Ultimate | 896 MPa | 130000 psi | |
| Haynes Ultimet® alloy, 19.1 mm thick plate, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Tensile Strength, Ultimate | >= 896 MPa | >= 130000 psi | |
| Materion Alloy M65 (C17465) Beryllium Copper Rod Alloy M65 (C17465) is a machinable, high-performance, copper beryllium rod alloy from Brush Wellman. M65 has excellent strength, conductivity, and resistance to elevated temperature stress relaxatio.. |
|||
| Tensile Strength, Ultimate | 895 MPa | 130000 psi | |
| Haynes 625 alloy, hot rolled and 1050°C mill-annealed plate Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Tensile Strength, Ultimate | 895 MPa | 130000 psi | |
| Haynes 625 alloy, plate after 4000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Tensile Strength, Ultimate | 896 MPa | 130000 psi | |
| Haynes Hastelloy® C-22® alloy, 10% cold worked sheet HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Tensile Strength, Ultimate | 894 MPa | 130000 psi | |
| HP Alloys Alloy C-276, 10% Cold Worked 10% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Internati.. |
|||
| Tensile Strength, Ultimate | 896 MPa | 130000 psi | |
| Universal Wire Works 6Al-4V (AMS 4954) Titanium Alloy Filler Metal Universal 6Al-4V titanium alloy is often repaired with the gas tungsten arc or gas metal arc welding process, provided adequate inert gas shielding of the filler wire and deposited weld metal is pro.. |
|||
| Tensile Strength, Ultimate | 896 MPa | 130000 psi | |
| Universal Wire Works 6Al-4V (ELI) (AMS 4956) Titanium Alloy Filler Metal Universal titanium alloy 6Al-4V (ELI) is similar to type 6Al-4V in chemical analysis with the exception of Extra Low Interstitial gases (ELI). By controlling these contaminating gases the fracture t.. |
|||
| Tensile Strength, Ultimate | >= 896 MPa | >= 130000 psi | |
| TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5) Rod or Thickness, 4.00-6.00 in, Annealed, Per Mil-T-9047G Medium To High Strength General-Purpose Alloy. Minimum tensile property data below are specific to Rod or Thickness, 4.00-6.00 in, Annealed, Per Mil-T-9047G; other specific form/thickness entries .. |
|||
| Tensile Strength, Ultimate | >= 895 MPa | >= 130000 psi | L and LT Directions |
| TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5) Sheet and Plate, 0.025-1.000 in, Annealed, Per ASTM B265 Medium To High Strength General-Purpose Alloy. Minimum tensile property data below are specific to Sheet and Plate, 0.025-1.000 in, Annealed, Per ASTM B265; other specific form/thickness entries a.. |
|||
| Tensile Strength, Ultimate | 897 MPa | 130000 psi | Typical |
| TIMET 6-4 Titanium Alloy (Ti-6Al-4V-0.1Ru; ASTM Grade 29) Medium To High Strength General-Purpose Alloy. Property data below are typical of Timet® 6-4 ELI (without Ru). The 0.1 Ru ELI variant is used for enhanced corrosion resistance.Data provided by TI.. |
|||
| Tensile Strength, Ultimate | 896 MPa | 130000 psi | cold worked |
| CMW® ELKONIUM 34 platinum based alloy Platinum has complete freedom from atmospheric corrosion and is preferred for devices that have low closed forces and where surety of making a circuit may be a problem. It has a high melting point (.. |
|||
| Tensile Strength, Ultimate | 896 MPa | 130000 psi | |
| AK Steel 17-7 PH® Precipitation Hardening Stainless Steel, Condition A AK Steel 17-7 PH® provides high strength and hardness, excellent fatigue properties, good corrosion resistance, good formability, and minimum distortion upon heat treatment. This alloy provides va.. |
|||
| Tensile Strength, Ultimate | 896 MPa | 130000 psi | 20.7% Cold Work |
| AK Steel NITRONIC® 19-D Duplex Stainless Steel AK Steel NITRONIC® 19D is a stainless steel with a mixed ferrite and austenite structure. This alloy provides high yield strength (65 ksi minimum {448 MPa}),
good drawing and welding characteristi.. |
|||
| Tensile Strength, Ultimate | 895 MPa | 130000 psi | |
| ATI Allegheny Ludlum AL 418™ Special (Greek Ascoloy) Martensitic Stainless Steel Uses include engine braces, turbine exhaust components, exhaust struts, stiffeners, and ducts.Information provided by Allegheny Ludlum |
|||
| Tensile Strength, Ultimate | 895 MPa | 130000 psi | |
| ATI Allegheny Ludlum Grade 5 Titanium 6Al-4V (UNS R56400) Uses: blades, discs, rings, airframe, fasteners, components, vessels, cases, hubs, forgings.Mechanical property data below is typical of annealed samples at room temperature.Information provided by .. |
|||
| Tensile Strength, Ultimate | 896 MPa | 130000 psi | |
| AK Steel PH 15-7 Mo® Precipitation Hardening Stainless Steel, Condition A AK Steel 15-7 Mo® provides high strength and hardness, good corrosion resistance and minimum distortion on heat treatment. It is easily formed in the annealed condition and develops effective bala.. |
|||
| Tensile Strength, Ultimate | <= 896 MPa | <= 130000 psi | AMS 5542 annealed, strip and sheet |
| ATI Allegheny Ludlum Altemp® X-750 Nickel-Based superalloy Characteristics: precipitation hardenable, high strength up to 1300°F, oxidation resistant up to 1800°F. Applications: aerospace, heat treatment fixtures, forming tools, extrusion dies.Information.. |
|||
| Tensile Strength, Ultimate | 895 MPa | 130000 psi | |
| Haynes 230® alloy plate, 8000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||