Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Strength | 8.96 - 11.0 MPa | 1300 - 1600 psi | |
ITW Plexus Plexusâ„¢ MA420FS Methacrylate Adhesive Two-part adhesive designed for structural bonding of thermoplastic, metal, and composite assemblies.All purpose adhesive, very fast curing.Information provided by Illinois Tool Works. |
|||
Shear Strength | 8.96 - 12.4 MPa | 1300 - 1800 psi | |
ITW Plexus Plexusâ„¢ MA550 Methacrylate Adhesive Two-part adhesive designed for structural bonding of thermoplastic, metal, and composite assemblies.Excellent marine adhesive, UV stable.Information provided by Illinois Tool Works. |
|||
Shear Strength | 8.96 MPa | 1300 psi | Overlap, Isopropyl Alcohol/Abrade/Isopropyl Alcohol surface prep, Phenolic |
3M Scotch-Weld™ DP420 Off-White Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion, and very high levels of durability.Information provided by 3M |
|||
Shear Strength | 8.96 MPa | 1300 psi | Overlap, Galvanized Steel |
3M Scotch-Weld™ DP805 Acrylic Adhesives 3M™ Scotch-Weld™ Acrylic Adhesive DP805 is a two-part, 1:1 mix ratio, toughened acrylic structural adhesives. They exhibit excellent shear and peel strengths along with good impact and durability .. |
|||
Shear Strength | 8.96 MPa | 1300 psi | Overlap, PVC, Substrate Failure |
3M Scotch-Weld™ DP807 Acrylic Adhesives 3M™ Scotch-Weld™ Acrylic Adhesive DP807 is a two-part, 1:1 mix ratio, toughened acrylic structural adhesives. They exhibit excellent shear and peel strengths along with good impact, durability and.. |
|||
Shear Strength | 8.96 MPa | 1300 psi | Overlap, ABS, Substrate Failure |
3M Scotch-Weld™ DP8805NS Low Odor Acrylic Adhesives 3M™ Scotch-Weld™ Low Odor Acrylic Adhesives are high performance, two-part acrylic adhesives with lower odor than most acrylic adhesives. These toughened products offer excellent shear, peel, and .. |
|||
Shear Strength | 8.96 MPa | 1300 psi | Overlap, ABS, Substrate Failure |
3M Scotch-Weld™ DP8810NS Low Odor Acrylic Adhesives 3M™ Scotch-Weld™ Low Odor Acrylic Adhesives are high performance, two-part acrylic adhesives with lower odor than most acrylic adhesives. These toughened products offer excellent shear, peel, and .. |
|||
Shear Strength | 8.96 MPa | 1300 psi | Overlap, FRP (red) (IPA/abrade/IPA) - Substrate Failure; ASTM D1002 |
3M Scotch-Weld™ LSB90 Flexible Epoxy 3M™ Scotch-Weld™ Epoxy Adhesive LSB90 is a high performance, two-part, flexible epoxy adhesive offering high shear and peel adhesion and very high levels of durability. It has a 90 minute worklife.. |
|||
Shear Strength | 8.96 MPa @Temperature 32.0 °C |
1300 psi @Temperature 89.6 °F |
Overlap, Plywood, 90% RH, Substrate Failure |
3M Scotch-Weld™ Thin Instant Wood Adhesives and Surface Activator 3M™ Scotch-Weld™ Instant Wood Adhesives an Surface Activator are single component, room temperature-curing adhesives that provides cure and speed and shear strength for demanding applications in t.. |
|||
Shear Strength | 8.96 MPa | 1300 psi | Overlap, Cold Rolled Steel |
3M Scotch-Weld™ DP-105 Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP105 Clear is a fast setting, very flexible 1:1 mix ratio epoxy adhesive/sealant. Its flexibility when cured makes it ideal for applications involving dissimilar s.. |
|||
Shear Strength | 8.96 MPa @Temperature 82.0 °C, Time 900 sec |
1300 psi @Temperature 180 °F, Time 0.250 hour |
Aluminum, etched, Overlap, Adhesive Failure |
3M Scotch-Weld™ LSB60NS Toughened Epoxy Adhesives 3M™ Scotch-Weld™ Toughened Epoxy Adhesive LBS60NS is a high performance, two-part, toughened epoxy adhesives offering outstanding shear adhesion and very high levels of durability with a choice of.. |
|||
Shear Strength | 8.96 MPa | 1300 psi | Overlap, Isopropyl Alcohol/Abrade/Isopropyl Alcohol surface prep, SBR/Steel |
3M Scotch-Weld™ DP420 Black Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion, and very high levels of durability.Information provided by 3M |
|||
Shear Strength | 8.96 MPa | 1300 psi | cured, grit-blasted steel; ASTM D1002 |
3M Scotch-Weld™ RT3500B Rubber-Toughened Instant Adhesive 3M™ Scotch-Weld™ Rubber Toughened Instant Adhesives are formulated with a unique elastomer that maximizes impact, vibration, peel, and thermal cycling resistance while providing tough flexible bon.. |