Polymer Property : Tensile Creep Modulus, 1000 hours = 2000 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Creep Modulus, 1000 hours	2000 - 5000 MPa	290000 - 725000 psi	Average value: 3580 MPa Grade Count:6
Overview of materials for Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled".Specific grades with glass content between 5% ..
Tensile Creep Modulus, 1000 hours	2000 MPa	290000 psi	Average value: 2000 MPa Grade Count:3
Overview of materials for Nylon 6, Glass Bead Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Glass Bead Filled". Each property range of values reported is minimum and maximum values of app..
Tensile Creep Modulus, 1000 hours	2000 MPa	290000 psi	ISO 899-1
Lanxess DurethanÂ® BG 30 X 000000 Nylon 6, 30% Glass Fiber PA 6, injection molding grade, 30% glass fibers/glass spheres, good surface, low warpage
Tensile Creep Modulus, 1000 hours	2000 MPa	290000 psi	Conditioned; ISO 889-1
Lanxess DurethanÂ® BG 30 X H3.0 000000 Nylon 6, 30% Glass Fibers/Glass Spheres PA 6, 30% glass fibers/glass spheres, injection molding, heat-ageing stabilized, low tendency to warp
Tensile Creep Modulus, 1000 hours	2000 MPa	290000 psi	ISO 899-1
Lanxess DurethanÂ® BKV 115 H2.0 901510 Copolyamide, 15% Glass Fiber CoPA, injection molding grade, 15% glass fibers, elastomer-modified, electroplateable, higher notched impact strength and also higher energy absorption under biaxial impact load than BKV 15, even in..
Tensile Creep Modulus, 1000 hours	2000 MPa	290000 psi	ISO 899-1
Lanxess DurethanÂ® BKV 115 000000 Copolyamide, 15% Glass Fiber CoPA, injection molding grade, 15% glass fibers, elastomer-modified, electroplateable, higher notched impact strength and also higher energy absorption under biaxial impact load than BKV 15, even in..
Tensile Creep Modulus, 1000 hours	2000 MPa	290000 psi	At 1% Deformation; DIN 53444
Wolf Kunststoff ZEDEX® ZX-100K A1K Polymer Alloy Main Characteristics: Hard; Stiff; Tough; High fatigue strength; Good weather resistance; Good machinability; FDA compliant LABS; PTFE and silicone-free; KTW approved; Stress resistantApplications: ..
Tensile Creep Modulus, 1000 hours	2000 MPa @Strain <=0.500 %	290000 psi @Strain <=0.500 %	ISO 899-1
BASF Ultradur® B 4300 M5 25% Mineral Filled PBT Description: Is a PBT-HI, injection-molding grade reinforced with 25% of minerals, for the production of parts with good surface quality and low warpage, e.g. housings and visible parts of domestic ..
Tensile Creep Modulus, 1000 hours	2000 MPa @Strain <=0.500 %	290000 psi @Strain <=0.500 %	ISO 899-1
BASF Ultramid® A3XZG5 BK 23187 25% Glass Filled PA66 FR (Conditioned) Description: Impact-modified, 25% glass-fiber reinforced injection-molding grade with improved flame retardance and enhanced long-term stability. Flame retardant based on red phosphorus; for compone..
Tensile Creep Modulus, 1000 hours	2000 MPa @Strain 0.500 %	290000 psi @Strain 0.500 %	ISO 899-1
BASF Ultramid® B3GK24 10/20% Glass Bead/Fiber Filled PA6 (Conditioned) Ultramid B3GK24 is 30% combined glass-fiber and glass bead injection molding PA6 grade for industrial articles having very high dimensional stability.
Tensile Creep Modulus, 1000 hours	2000 MPa @Strain <=0.500 %	290000 psi @Strain <=0.500 %	ISO 899-1
BASF Ultramid® B3GK24 BK 00564 10/20% Glass/Glass Bead Filled PA6 (Conditioned) Description: combined 10% glass-fiber and 20% glass-bead reinforced injection-molding grade for technical articles of very good dimensional stability, for instance, vehicle ash tray housings and ele..