BASF Ultramid® B3GK24 10/20% Glass Bead/Fiber Filled PA6 (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Bead Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® B3GK24 10/20% Glass Bead/Fiber Filled PA6 (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid B3GK24 is 30% combined glass-fiber and glass bead injection molding PA6 grade for industrial articles having very high dimensional stability.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Water Absorption | 6.3 - 6.9 % | 6.3 - 6.9 % | ISO 62 |
| Moisture Absorption at Equilibrium | 1.9 - 2.3 % | 1.9 - 2.3 % | (23°C/50% R.H.); ISO 62 |
| Viscosity Test | 140 cm³/g | 140 cm³/g | Viscosity number |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | |
| Melt Flow | 93.8 g/10 min @Load 5.00 kg, Temperature 275 °C |
93.8 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50mm/min; ISO 527 |
| Elongation at Yield | 15 % | 15 % | 50mm/min; ISO 527 |
| Modulus of Elasticity | 3.00 GPa | 435 ksi | ISO 527 |
| Flexural Strength | 70.0 MPa | 10200 psi | ISO 178 |
| Flexural Modulus | 3.00 GPa | 435 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 8.50 kJ/m² | 4.04 ft-lb/in² | ISO 180/A |
| Charpy Impact Unnotched | 9.00 J/cm² | 42.8 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 1.10 J/cm² | 5.24 ft-lb/in² | ISO 179/1eA |
| Tensile Creep Modulus, 1000 hours | 2000 MPa @Strain 0.500 % |
290000 psi @Strain 0.500 % |
ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 1.40 J/g-°C | 0.335 BTU/lb-°F | |
| Thermal Conductivity | 0.340 W/m-K | 2.36 BTU-in/hr-ft²-°F | DIN 53765 |
| Melting Point | 220 °C | 428 °F | |
| Maximum Service Temperature, Air | 200 °C | 392 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 |
| Dielectric Constant | 4.6 @Frequency 1.00e+6 Hz |
4.6 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dissipation Factor | 0.070 @Frequency 1.00e+6 Hz |
0.070 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 425 V | 425 V | Test Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | Injection-molding/Extrusion |
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection-molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | North America and Europe | |
| Form | Pellets | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding | |
| Processing | Injection Molding | |
| Special characteristic | Heat stabilized or stable to heat |
Users viewing this material also viewed the following:
- Chevron Phillips Valtra® EA8100 Advanced Styrenic Polymer (discontinued **)
- Lotte Chemical Titan TITANPRO® EPC40R Polypropylene impact copolymer
- Solvay Specialty Polymers Catalyst PS/2 Black Polyolefin
- Teknor Apex Telcar® TL-2572A Thermoplastic Elastomer
- Weartech International WT-31 Cobalt Hardfacing & Wear Resistant Alloy
- Hexcel® Redux® 322 Modified epoxy film adhesive (0.078 psf)
- Master Bond Supreme 11HT High Temperature Resistant Two Component Epoxy System
- ExxonMobil Exceed™ 1327CA Metallocene Polyethylene Resin (European Grade)
- BASF Elastollan R 1000 20% Glass Filled TPUR
- 3M Scotch® 893 Filament Tape
Copyright © lookpolymers.com All Rights Reserved