BASF Ultramid® B3GK24 BK 00564 10/20% Glass/Glass Bead Filled PA6 (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 10% Glass Fiber Filled , Nylon 6, Glass Bead Filled
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® B3GK24 BK 00564 10/20% Glass/Glass Bead Filled PA6 (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: combined 10% glass-fiber and 20% glass-bead reinforced injection-molding grade for technical articles of very good dimensional stability, for instance, vehicle ash tray housings and electronic housings.Information provided by BASF
Physical Properties Metric English Comments
Bulk Density 0.500 - 0.800 g/cc
0.0181 - 0.0289 lb/in³
Density 1.34 g/cc
0.0484 lb/in³
ISO 1183
Water Absorption 6.3 - 6.9 %
6.3 - 6.9 %
Saturation; ISO 62
Moisture Absorption at Equilibrium 1.9 - 2.3 %
1.9 - 2.3 %
23°C; 50% RH; ISO 62
Viscosity Measurement 140
140
ISO 307
Linear Mold Shrinkage 0.0050 cm/cm
0.0050 in/in
restricted
Melt Flow 93.8 g/10 min

@Load 5.00 kg,
Temperature 275 °C
93.8 g/10 min

@Load 11.0 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 60.0 MPa
8700 psi
50 mm/min; ISO 527-1/-2
Elongation at Yield 15 %
15 %
50 mm/min; ISO 527-1/-2
Modulus of Elasticity 3.00 GPa
435 ksi
ISO 527-1/-2
Flexural Strength 70.0 MPa
10200 psi
at max force; ISO 178
100 MPa
14500 psi
ISO 178
Flexural Modulus 3.00 GPa
435 ksi
ISO 178
Izod Impact, Notched (ISO) 8.50 kJ/m²

@Temperature 23.0 °C
4.04 ft-lb/in²

@Temperature 73.4 °F
ISO 180/A
Charpy Impact Unnotched 9.00 J/cm²

@Temperature 23.0 °C
42.8 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 1.10 J/cm²

@Temperature 23.0 °C
5.23 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Tensile Creep Modulus, 1000 hours 2000 MPa

@Strain <=0.500 %
290000 psi

@Strain <=0.500 %
ISO 899-1
Thermal Properties Metric English Comments
Specific Heat Capacity 1.40 J/g-°C
0.335 BTU/lb-°F
Thermal Conductivity 0.340 W/m-K
2.36 BTU-in/hr-ft²-°F
DIN 52612
Melting Point 220 °C
428 °F
DIN 53765
Maximum Service Temperature, Air 100 °C
212 °F
for 50% loss of tensile strength after 20000hr
200 °C
392 °F
Decomposition Temperature >= 300 °C
>= 572 °F
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+10 ohm-cm
1.00e+10 ohm-cm
IEC 60093
Surface Resistance 1.00e+10 ohm
1.00e+10 ohm
IEC 60093
Dielectric Constant 4.6

@Frequency 1.00 Hz
4.6

@Frequency 1.00 Hz
IEC 60250
Dissipation Factor 0.070

@Frequency 1.00e+6 Hz
0.070

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 425 V
425 V
Test solution A; IEC 60112
Processing Properties Metric English Comments
Processing Temperature 80.0 °C
176 °F
Hopper Throat
Zone 1 260 °C
500 °F
Feed Zone
Zone 2 270 °C
518 °F
Compression
Zone 3 280 °C
536 °F
Metering-zone
Zone 4 280 °C
536 °F
Nozzle
Melt Temperature 270 - 290 °C
518 - 554 °F
Injection-molding/Extrusion
280 °C
536 °F
Optimal
Mold Temperature 80.0 °C
176 °F
Optimal
80.0 - 90.0 °C
176 - 194 °F
Injection-molding
Drying Temperature 80.0 °C
176 °F
Dry Time 4 hour
4 hour
Moisture Content 0.030 - 0.060 %
0.030 - 0.060 %
Optimal
<= 0.15 %
<= 0.15 %
Descriptive Properties Value Comments
Color BK 00564
Commercial Status Europe
Ignition Temperature >400°C
ASTM D129
Peripheral screw speed < 0.3 m/s